Professur Bauchemie und Polymere Werkstoffe
Refine
Document Type
- Article (11)
- Doctoral Thesis (11)
- Conference Proceeding (1)
- Diploma Thesis (1)
- Habilitation (1)
Institute
Keywords
- Bindemittel (4)
- Wasserglas (4)
- Geopolymere (3)
- Mikrostruktur (3)
- Mörtel (3)
- Alkalisilikat (2)
- Alumosilikat (2)
- Bauchemie (2)
- Epoxidharz (2)
- Geopolymer (2)
- Kationenaustausch (2)
- Kunststoffadditiv (2)
- Magnesiumsulfat (2)
- Mehrphasensystem (2)
- Metakaolin (2)
- OA-Publikationsfonds2023 (2)
- Polymere (2)
- Reifungsprozess (2)
- Sauerstoff (2)
- Silikat (2)
- Strukturbildungsprozess (2)
- Verflüssigung (2)
- ATZ (1)
- Affecting factors; Measurement uncertainty; Materials testing; Quantitative comparison; Strain comparison; Tensile test (1)
- Air tightness (1)
- Alterung (1)
- Ammonium-Ton (1)
- Anisotropie (1)
- Anorganische Salze (1)
- Anorganisches Bindemittel (1)
- BSCF (1)
- Baustahl (1)
- Baustein (1)
- Bentonit (1)
- Betonverflüssiger (1)
- Beugungsgitter (1)
- Brechzahländerung (1)
- Building monitoring (1)
- CSMF (1)
- Creep (1)
- Dauerhaftigkeit (1)
- Deammonisierung (1)
- Denkmalpflege (1)
- Dispersionskeramik (1)
- Dynamische Messungen (1)
- Elastizitätsmodul (1)
- Epoxide (1)
- Festbett (1)
- Feuchtigkeit (1)
- Fließmittel (1)
- GIXRD (1)
- Himalaja (1)
- Himalaya (1)
- Hydratation (1)
- Hüftgelenkprothese (1)
- Indoor climate (1)
- Inertgas (1)
- Interpartikuläre Wechselwirkungen (1)
- KTP-Einkristall (1)
- Kaliumtitanylphosphat (1)
- Keramik (1)
- Knoop Mikrohärte (1)
- Konservierung (1)
- Kriechen (1)
- Kunststoffmörtel (1)
- Kupferfixierung (1)
- Kupfersilicate (1)
- LSCF (1)
- Lehm (1)
- Lehmbau (1)
- Lehmhaus (1)
- Lettenkeupersandstein (1)
- Lower Keuper Sandstone (1)
- Luftdichtheit (1)
- Luftzerlegung (1)
- Lösungsanalytik (1)
- Metaphosphat (1)
- Microstructure (1)
- Middle Keuper Sandstone (1)
- Mikroskopie (1)
- Modellierung (1)
- Modifizierung (1)
- Monitoring (1)
- Montmorillonite (1)
- Multiscale modeling (1)
- Multiskalenmodellierung (1)
- NRA (1)
- Natriumsulfat (1)
- Naturstein (1)
- Nitrate (1)
- OA-Publikationsfonds2020 (1)
- OA-Publikationsfonds2021 (1)
- Oxidkeramik (1)
- Perowskit (1)
- Polymer modification (1)
- Polymeradsorption (1)
- Polymermodifizierung (1)
- Raumklima (1)
- Rb/K-Diffusionskoeffizient (1)
- Restaurierung (1)
- Salzmischungen (1)
- Salzschmelze (1)
- Sauerstoffseparation (1)
- Schilfsandstein (1)
- Schüttung (1)
- Simulation (1)
- Sorption (1)
- Sorptionswärme (1)
- SrMnO3 (1)
- Steinfestigung (1)
- Steinkonservierung (1)
- Stickstoff (1)
- Stärkefließmittel (1)
- Superplasticizer (1)
- Suspensionsanalytik (1)
- Synthese (1)
- Thermische Energiespeicherung (1)
- Thermochemische Wärmespeicherung (1)
- Ton <Geologie> (1)
- Tribologie (1)
- U-value (1)
- Werkstoffprüfung (1)
- Wärmebehandlung (1)
- Wärmedurchgangszahl (1)
- Wärmespeicherung (1)
- Young's modulus (1)
- Zement (1)
- Zementhydratation (1)
- Zementstein (1)
- Zugversuch (1)
- Zusatzmittel (1)
- acid resistant coating material (1)
- alumosilicate (1)
- alumosilicatic (1)
- alumosilikatisch (1)
- amine hardener (1)
- berlinite (1)
- bio-based (1)
- carboxymethylcellulose (1)
- cement (1)
- china clay (1)
- curing agent (1)
- depletion method (1)
- epoxy (1)
- geopolymer (1)
- hermochemical heat storage, hydration mechanism, magnesium sulfate; sodium sulfate (1)
- mass spectrometry (1)
- metakaoline (1)
- metaphosphate (1)
- mortar (1)
- motars (1)
- natural building stone (1)
- optisches Gitter (1)
- polycarboxylate ether (1)
- polymer adsorption (1)
- poröse Trägermaterialien (1)
- sodium silicate solution (1)
- stone consolidation (1)
- stone decay (1)
- superplasticizer (1)
- superplasticizers (1)
- säurefeste Beschichtungen (1)
- vanillin (1)
- visible spectrophotometry (1)
- wasserbeständig (1)
- water-glass (1)
Calcined clays are interesting starting materials to be used as SCMs (supplementary cementitious materials) in cements or to be converted to geopolymers by activation with a high alkaline activator. The adjustment of the properties in the fresh state, especially regarding the consistency of these binders, is almost exclusively achieved by the addition of water, since commercially available superplasticizers seem to be ineffective in low-calcium geopolymer systems. The aim of this study was a systematic investigation of various PCE (polycarboxylate ester/ether) superplasticizers (methacrylate ester PCE: MPEG, isoprenol ether PCE: IPEG, methallyl ether PCE: HPEG) with respect to their stability in different alkaline activators (NaOH, KOH, sodium and potassium silicate solutions). The effectiveness of superplasticizers (SPs) in low-calcium geopolymer binders was verified by rheological tests. Size exclusion chromatography was used to investigate if structural degradation of the superplasticizers occurs. The investigated PCE superplasticizers showed a thickening effect in the low-calcium geopolymer system. Depending on the alkalinity of the activator solution, a degradation process was detected for all the PCEs investigated. The side chains of the PCEs are cleaved off the backbone by basic ester and ether hydrolysis. The highest degree of degradation was found in sodium and potassium silicate solutions. In alkaline hydroxide solutions, the degradation process increases with increasing alkalinity.
This paper reports the formation and structure of fast setting geopolymers activated by using three sodium silicate solutions with different modules (1.6, 2.0 and 2.4) and a berlinite-type aluminum orthophosphate. By varying the concentration of the aluminum orthophosphate, different Si/Al-ratios were established (6, 3 and 2). Reaction kinetics of binders were determined by isothermal calorimetric measurements at 20 °C. X-ray diffraction analysis as well as nuclear magnetic resonance (NMR) measurements were performed on binders to determine differences in structure by varying the alkalinity of the sodium silicate solutions and the Si/Al-ratio. The calorimetric results indicated that the higher the alkalinity of the sodium silicate solution, the higher the solubility and degree of conversion of the aluminum orthophosphate. The results of X-ray diffraction and Rietveldt analysis, as well as the NMR measurements, confirmed the assumption of the calorimetric experiments that first the aluminum orthophosphate was dissolved and then a polycondensation to an amorphous aluminosilicate network occurred. The different amounts of amorphous phases formed as a function of the alkalinity of the sodium silicate solution, indicate that tetrahydroxoaluminate species were formed during the dissolution of the aluminum orthophosphate, which reduce the pH value. This led to no further dissolution of the aluminum orthophosphate, which remained unreacted.
Die thermochemische Wärmespeicherung über reversible Salzhydratation stellt einen aussichtsreichen Weg zur Speicherung von Niedertemperaturwärme, wie z.B. solarer Energie, dar.
Untersuchungen an Magnesiumsulfat-Hydraten zeigen, dass das bei 130°C entwässerte Magnesiumsulfat-Heptahydrat seinen thermodynamisch stabilen Endzustand während der Reaktion mit gasförmigem Wasser nicht wieder erreicht. Um diese kinetische Hemmung zu überwinden und den Einfluss von unterschiedlichen Porenräumen auf die Hydratation bzw. Sorption des Magnesiumsulfates zu charakterisieren, wurde das Magnesiumsulfat in Trägermaterialien auf Basis offenporiger Gläser mit durchschnittlichen Porendurchmessern von 4 nm bis 1,4 µm eingebracht und diese Kompositmaterialien untersucht. Dabei ist festgestellt worden, dass jede salzbezogene Sorptionswärme im Porenraum höher ist, als die des ungeträgerten Salzes und mit kleiner werdendem Porenradius weiter zunimmt.
Weiterhin wurden Teile des Magnesiumsulfates mit niedrig deliqueszierenden Salzen substituiert, um die Wasseraufnahme und somit die Wärmespeicherkapazität zu erhöhen. Dies stellt einen neuen Weg zur Herstellung von Kompositmaterialien dar, über den man Eigenschaften wie Deliqueszenzfeuchte und Desorptionstemperatur einstellen und an die Sorptionsbedingungen eines Speichers anpassen kann. Als niedrig deliqueszierende Salze wurden Magnesiumchlorid und Lithiumchlorid
als Zusätze untersucht, wobei ein Ansteigen der Sorptionswärme und Wasseraufnahme mit steigendem Chloridanteil festgestellt wurde. Aufgrund der geringeren Deliqueszenzfeuchte des Lithiumchlorides gegenüber dem Magnesiumchlorid wurden bei gleichen Massenverhältnissen höhere Sorptionswärmen erzielt. Untersuchungen zu Zinksulfat in Verbindung mit Chloriden bescheinigen diesem Salz -speziell bei tieferen Entwässerungstemperaturen- eine gute Eignung als Aktivstoff zur Wärmespeicherung.
Zusammenfassend konnte festgestellt werden, dass sich die Wärmespeicherkapazitäten über die Porengröße, in die das Salz eingebracht wird, und die gewählte Mischungszusammensetzung steuern lassen. Die gemessenen Sorptionswärmen ermöglichen insbesondere bei niedrigen Sorptionstemperaturen und hohen Luftfeuchtigkeiten den Schluss, dass die Verwendung von Salzmischungen als Aktivkomponente in Kompositmaterialien einen geeigneten Weg zur thermochemischen Speicherung solarer Wärme (≤130 °C) darstellt.
Der Einsatz von Lehmbaustoffen stößt an Grenzen, wenn das Material Feuchtigkeit ausgesetzt ist. Die vorliegende Arbeit enthält Untersuchungen zur Verbesserung der Wasserbständigkeit von Lehmbaustoffen. Es konnte gezeigt werden, dass mittels alumosilikatischer Polymerbinder der Widerstand von Lehmbaustoffen gegen Feuchteeinwirkung erheblich verbessert werden kann. Die positiven bauklimatischen Eigenschaften werden dabei nicht negativ beeinflusst.
Ziel der Arbeit war das Adsorptionsverhalten ausgewählter schutzkolloidstabilisierter Polymerpartikel mit variierender chemischer Basis im zementären System zu beschreiben und basierend auf den gewonnenen Erkenntnissen das Konkurrenzverhalten beim Angebot unterschiedlicher mineralischer Oberflächen zu klären.
Sowohl die Destabilisierung der Polymerpartikel im alkalischen Milieu, welche eine Voraussetzung für derartige Adsorptionsprozesse ist, als auch die Veränderung von Oberflächeneigenschaften verschiedener mineralischer Partikel durch Hydratations- und Ionenadsorptionsprozesse, wurden u. a. mit Hilfe elektrokinetischer Experimente erfasst. Die spektralphotometrische Erstellung von Adsorptionsisothermen ermöglichte zudem die Ermittlung der jeweiligen adsorbierten Polymermenge zu verschiedenen Zeitpunkten der frühen Hydratation. Weiterhin wurde die Polymeradsorption an Partikeln ausgewählter Zusatzstoffe in Abhängigkeit von der Ionenstärke der Flüssigphase beschrieben.
Rasterelektronenmikroskopische Untersuchungen cryo-präparierter polymermodifizierter Zementleimproben ermöglichten es außerdem deren Mikrostruktur im suspensiven Zustand zu visualisieren. Diese Aufnahmen, ebenso wie die Ergebnisse grundlegender hydratationskinetischer Untersuchungen wurden in Wechselbeziehung zu den Ergebnissen der Adsorptionsuntersuchungen gebracht.
Maßgelbliche intermolekulare und interpartikuläre Wechselwirkungen, infolge derer sich die Stabilitätsverhältnisse im Zementleim ändern und die Polymerpartikel adsorbieren sind im Wesentlichen die Desorption des Schutzkolloids von der Polymerpartikeloberfläche, die Ionisation funktioneller Gruppen der Polymerpartikel und der Schutzkolloidmakromoleküle im alkalischen Milieu und infolgedessen die Komplexbildung mit Ionen der Zementleimporenlösung. Die Auswirkungen dieser Vorgänge auf die Lösungs- und Fällungskinetik des Zementleimes wurden erfasst und mit der chemischen Zusammensetzung der polymeren Systeme korreliert.
The amount of adsorbed styrene acrylate copolymer (SA) particles on cementitious surfaces at the early stage of hydration was quantitatively determined using three different methodological approaches: the depletion method, the visible spectrophotometry (VIS) and the thermo-gravimetry coupled with mass spectrometry (TG–MS). Considering the advantages and disadvantages of each method, including the respectively required sample preparation, the results for four polymer-modified cement pastes, varying in polymer content and cement fineness, were evaluated.
To some extent, significant discrepancies in the adsorption degrees were observed. There is a tendency that significantly lower amounts of adsorbed polymers were identified using TG-MS compared to values determined with the depletion method. Spectrophotometrically generated values were lying in between these extremes. This tendency was found for three of the four cement pastes examined and is originated in sample preparation and methodical limitations.
The main influencing factor is the falsification of the polymer concentration in the liquid phase during centrifugation. Interactions in the interface between sediment and supernatant are the cause. The newly developed method, using TG–MS for the quantification of SA particles, proved to be suitable for dealing with these revealed issues. Here, instead of the fluid phase, the sediment is examined with regard to the polymer content, on which the influence of centrifugation is considerably lower.
6 Zusammenfassung und Ausblick
Die hydrothermal induzierte Phasentransformation konnte für ATZ-Keramik mit tiefenge-mittelten und tiefenaufgelösten Methoden charkterisiert und quantifiziert werden.
Die zeit- und temperaturabhängige Alterungskinetik von ATZ wurde durch neun Tempera-turstufen in einem Temperaturbereich von 50 °C bis 134 °C untersucht und die kinetischen Parameter nummerisch bestimmt. Für 3Y-TZP wurde diese Prozedur bei drei Temperaturen im Temperaturbereich von 70 °C bis 134 °C angewendet. Aufgrund des ARRHENIUS-Verhaltens der Umwandlungskinetik konnte der zeitliche Verlauf der isotherm stattfinden-den hydrothermal induzierten Phasentransformation bei Körpertemperatur simuliert wer-den. Die Simulation dient zur Bewertung der Langzeitstabilität von medizinischen Implanta-ten aus ATZ bzw. 3Y-TZP. Die Untersuchungen wurden in Wasser und in Wasserdampf bzw. wasserdampfgesättigter Luft durchgeführt. Die Langzeitsimulation für 3Y-TZP wurde an-hand von Explantat-Untersuchungen verifiziert.
ATZ zeigt gegenüber 3Y-TZP eine höhere Alterungsstabilität bezogen auf die zeitliche Ent-wicklung der monoklinen Phase. Im Hinblick auf die Oberflächenhärte, die durch die Pha-senumwandlung stark beeinflusst wird, erweist sich ATZ über einen langen Alterungszeit-raum stabiler als 3Y-TZP. Bis zu einem monoklinen Gehalt von 40 % beweist ATZ einen deutlichen Härtevorteil gegenüber 3Y TZP, dieser entspricht in der Langzeitsimulation für die Wasserlagerung ca. 35 Jahre. Das wirkt sich insbesondere bei Verschleißpaarungen wie beim künstlichen Hüftgelenk positiv aus.
Verschleißuntersuchungen an einer neu entwickelten Kugel-auf-Scheibe-Geometrie mit li-nearer Kinematik, die dem Hüftgelenk nachempfunden wurde, belegen die vorteilhaften Verschleißeigenschaften von ATZ in Form von sehr geringen Abtragsraten und einer intak-ten Oberfläche nach 720 000 absolvierten Zyklen. Dabei wurde sogar eine Aufhärtung der Oberfläche durch die Verschleißbeanspruchung um bis zu 8 % nachgewiesen.
Bei der tiefengemittelten Charakterisierung der hydrothermalen Alterung wurde in beiden Materialtypen festgestellt, dass die Geschwindigkeit der Phasentransformation neben der Temperatur merklich von der Änderung der H2O-Stoffmengenkonzentrantion an der Ober-fläche der Keramik abhängig ist, was sich mit den unterschiedlichen Aktivierungsenergien für Wasser- bzw. Wasserdampflagerung belegen lässt. Die Aktivierungsenergie Ea der hyd-rothermalen Phasentransformation wurde mit Hilfe der ARRHENIUS-Beziehung ermittelt und beträgt für ATZ bei Wasserdampflagerung 102 kJ/mol und bei Wasserlagerung 92 kJ/mol. Für Y-TZP beträgt die Aktivierungsenergie 114 kJ/mol bei Wasserdampflagerung und 102 kJ/mol bei Wasserlagerung. Der resultierende präexponentielle Faktor k0 unterscheidet sich für Wasserlagerung und Wasserdampflagerung um eine Größenordnung, was auf einen leicht andersartigen thermisch aktivierten Gesamtprozess hinweist.
Der Avrami-Exponent n, der einen Hinweis auf den Mechanismus der Keimbildung sowie deren geometrische Ordnung geben kann, zeigte keine signifikante Abhängigkeit von der Temperatur und vom Umgebungsmedium. Er ist dagegen zeitabhängig und fällt mit zuneh-mender Alterungszeit, d.h. mit zunehmendem monoklinem Gehalt von ca. 4 auf 0,5 ab, was auf eine abnehmende Keimbildungsrate hindeutet. In Verbindung mit weiteren Untersu-chungen durch unabhängige und zum Teil tiefenauflösende Methoden wie GIXRD, NRA und Knoop-Mikrohärte-Messungen lässt sich der Alterungsmechanismus, bzw. sein zeitlicher und örtlicher Ablauf, durch die drei Stadien A, B und C beschreiben:
A 0-5 ma. % m-ZrO2 Quasi-homogene Keimbildung an bevorzugten Orten wie Kornkan-ten und Kornecken (n≈4), Wassertransport wahrscheinlich via Korngrenzendiffusion, Aufhärtung der Oberfläche
B 5-40 ma. % m-ZrO2 Keimbildung an den Korngrenzflächen bis zur Keimsättigung (n≈2), monokline Randschicht wächst zeitlich linear, Wassertransport konvektiv über Mikrorisse, deutlicher Härteverlust der Oberfläche
C ≥ 40 ma. % m-ZrO2 Wachstum der monoklinen Kristallite von den Korngrenzflächen in die tetragonalen Kristallite unter starker Verzwillingung (n≈0,5), Abnahme der tetragonalen Kristallitgröße, starke Mikrorissbildung, dramatischer Rückgang der Oberflächenhärte
Die Kristallitgröße der monoklinen Phase verbleibt im ATZ über alle drei Abschnitte bei 30 ±5 nm. Ein Anwachsen der Kristallite ist mechanische behindert. Kleinere monokline Kristallite sind im ATZ thermodynamisch instabil. Die Kristallitgröße der tetragonalen Phase fällt in den Abschnitten A und B sehr langsam und in C sehr schnell bis auf 25 nm ab. Bei dieser Kristallitgröße ist die tetragonale Phase gegenüber der monoklinen Phase thermody-namisch stabil. Diese residualen tetragonalen Kristallite weisen nach vollständigem Reakti-onsablauf einem Anteil von 7 ma. % auf. Der Sättigungsgehalt der monoklinen Phase betrug in beiden Materialen unabhängig von der Temperatur bzw. dem Umgebungsmedium 75 % der ZrO2-Phase.
In Abschnitt C besitzt die residuale tetragonale Phase eine starke Orientierung. Dadurch wird die geometrische Bedingtheit der hydrothermal induzierten Phasenumwandlung ver-deutlicht. Die monokline Phase ist über den gesamten Alterungsprozess stark nach m(1 1 1) orientiert, was mit einer bevorzugten Umklapprichtung der c-Achse zur freien Oberfläche hin verbunden ist.
Mit Hilfe der tiefenaufgelösten Phasenanalyse konnte die Wachstumsgeschwindigkeit der monoklinen Randschicht von der Oberfläche in das Volumen untersucht werden. Die Ge-schwindigkeit des Schichtwachstums ist in Abschnitt B nicht zeit- und tiefenabhängig, son-dern konstant mit ausgeprägtem ARRHENIUS-Verhalten (Temperaturabhängigkeit). Die Akti-vierungsenergie der Schichtwachstumsgeschwindigkeit km liegt in der gleichen Größenord-nung wie die der Transformationskonstante k.
Die Umwandlungszone schreitet also mit konstanter Geschwindigkeit in das Volumen fort und hinterlässt ein verzweigtes Mikro- und Nanoriss-System. FESEM-Aufnahmen bestätigen das Vorhandensein einer porösen Randschicht, durch die das Wasser nahezu ungehindert eindringen kann.
NRA Untersuchungen deuten in Stadium A auf Korngrenzendiffusion hin und bestätigen in Stadium B einen konvektiven Transport des Wassers an die Transformationszone. Eine Dif-fusion über Sauerstoffleerstellen im Gitter konnte anhand von Proben aus 8YSZ nicht nach-gewiesen werden. Dagegen kommt es in dem verzweigten Riss- und Porensystem in der gealterten Randschicht zum Rücktransport des Wassers an die Oberfläche, sobald die Pro-ben aus der hydrothermalen Atmosphäre genommen, an Luft gelagert oder in die Hochva-kuumkammer der NRA-Messapparatur eingeschleust werden.
Mikrostrukturelle Untersuchungen an eigens entwickelten Verschleißpaarungen zeigten nach 720000 Zyklen ähnliche Oberflächeneigenschaften wie im Alterungsstadium A. Man kann daher davon ausgehen, dass die Stadien B und C aus Stabilitätsgründen in der tribolo-gischen Kontaktzone nicht existieren können und es dass sich im Falle einer gleichzeitigen, hydrothermalen und tribologischen Beanspruchung um einen stationären Alterungs- und Verschleißprozess handelt. Durch quasiplastische Deformation der monoklinen und tetra-gonalen Kristallite wird die Verschleißrate und die Abriebpartikel bei einer hart /hart Paa-rung aus ATZ deutlich minimiert, so dass ATZ für die Hüftendoprothetik ein durchaus geeig-neten Werkstoff darstellt, der sich auf der Grundlage der in dieser Arbeit gewonnenen Daten über eine Imlantationsdauer von .mehr als 15 Jahre stabil verhalten kann.
Durch Reifungs- und Strukturbildungsprozesse kann es bei silikatischen und alumosilikatischen Bindern zu Rissbildung bei behinderter Verformung, Festigkeitsverlust und somit Verlust der Dauerhaftigkeit kommen. Die Bewertung dieser Prozesse erfolgt an silikatischen Materialien mit einem Ausblick auf die alumosilikatischen Binder.
Durch Reifungs- und Strukturbildungsprozesse kann es bei silikatischen und alumosilikatischen Bindern zu Rissbildung bei behinderter Verformung, Festigkeitsverlust und somit Verlust der Dauerhaftigkeit kommen. Die Bewertung dieser Prozesse erfolgt an silikatischen Materialien mit einem Ausblick auf die alumosilikatischen Binder
Bentonite sind quellfähige Tone, die häufig in der Umwelttechnik (in Abdichtungsbauwerken oder in der Bodensanierung) eingesetzt werden. Ziel der Arbeit war die Klärung, wie eine unterschiedliche Kationenbelegung mit Cu2+ und NH4+ die Eigenschaften der Bentonite bei Raumtemperatur und nach moderater Wärmebehandlung (300 – 450°C) beeinflusst. Im Blickpunkt stand insbesondere die gleichzeitige Präsenz von Kupfer- und Ammoniumionen, die als Vertreter für häufig auftretende Inhaltsstoffe von Wässern in der Umgebung von technischen Bentoniten ausgewählt wurden.
Die Untersuchungen zur Cu2+-Sorption bei Raumtemperatur und nach moderater Wärmebehandlung (300 – 450°C) erfolgten an Pulverproben von zwei technischen Bentoniten, die sich in der ursprünglichen Kationenbelegung, Art und Anteil an Nebengemengteilen, sowie der Schichtladungsverteilung in den Montmorilloniten unterscheiden. Vor der Wärmebehandlung wurden die Bentonite durch Kontakt mit verschieden konzentrierten Kupfer- und Ammoniumlösungen mit unterschiedlichen Gehalten der Kationen Cu2+, NH4+, Na+, Ca2+, Mg2+ belegt.
Der Eintrag von Kupferionen in die Bentonite durch Kationenaustausch bei Raumtemperatur wurde erwartungsgemäß durch präsente Nebengemengteile (wie Carbonat) beeinflusst, so dass die Kupferionen zusätzlich spezifisch adsorbiert und in festen Phasen angereichert wurden.
Die Cu2+-Fixierung infolge der Wärmebehandlung wurde vom Cu2+-Totalgehalt in den Bentoniten, der Präsenz von Nebengemengteilen und die Schichtladungsverteilung in den Montmorilloniten beeinflusst. Es waren generell Behandlungstemperaturen von > 400°C erforderlich, um Cu2+-Fixierungsraten von > 95% zu erzielen.
Waren während der Wärmebehandlung neben Cu2+-Ionen gleichzeitig NH4+-Ionen in den Bentoniten präsent, konnte die Cu2+-Fixierungstemperatur herabgesetzt werden. Die Deammonisierung (NH4+ --> NH3 + H+) der NH4+-belegten Bentonite fand größtenteils unterhalb der Dehydroxylierungstemperatur der Bentonite statt.
Durch Untersuchungen (XRD, FTIR, NMR, ESR) zum Mechanismus der Cu2+-Einbindung in die Bentonite an speziell aufbereiteten Proben (carbonatfrei, < 2 µm) konnte nachgewiesen werden, dass in den Cu2+-belegten Montmorilloniten die Cu2+-Ionen infolge der Wärmebehandlung nicht bis in die Oktaederschicht der Tonminerale vordringen, sondern nur bis in die Tetraederschicht wandern. In den NH4+-belegten Montmorilloniten treten im Zusammenhang mit der Deammonisierung keine zusätzlichen Strukturänderungen (wie Auflösung der Oktaederschicht) infolge der Wärmebehandlung auf.