- Affecting factors; Measurement uncertainty; Materials testing; Quantitative comparison; Strain comparison; Tensile test (1)
This paper reports the formation and structure of fast setting geopolymers activated by using three sodium silicate solutions with different modules (1.6, 2.0 and 2.4) and a berlinite-type aluminum orthophosphate. By varying the concentration of the aluminum orthophosphate, different Si/Al-ratios were established (6, 3 and 2). Reaction kinetics of binders were determined by isothermal calorimetric measurements at 20 °C. X-ray diffraction analysis as well as nuclear magnetic resonance (NMR) measurements were performed on binders to determine differences in structure by varying the alkalinity of the sodium silicate solutions and the Si/Al-ratio. The calorimetric results indicated that the higher the alkalinity of the sodium silicate solution, the higher the solubility and degree of conversion of the aluminum orthophosphate. The results of X-ray diffraction and Rietveldt analysis, as well as the NMR measurements, confirmed the assumption of the calorimetric experiments that first the aluminum orthophosphate was dissolved and then a polycondensation to an amorphous aluminosilicate network occurred. The different amounts of amorphous phases formed as a function of the alkalinity of the sodium silicate solution, indicate that tetrahydroxoaluminate species were formed during the dissolution of the aluminum orthophosphate, which reduce the pH value. This led to no further dissolution of the aluminum orthophosphate, which remained unreacted.
Objektive Oberflächenbewertung von (P)SCC-Sichtbeton mittels automatisierter Analyse von Bilddaten
(2019)
Sichtbeton ist aufgrund seiner Vielfältigkeit in der Formgebung eines der am meisten verbreiteten Gestaltungsmittel der modernen Architektur und optimal für neue Bauweisen sowie steigende Anforderungen an das Erscheinungsbild öffentlicher Bauwerke geeignet. Die Herstellung qualitativ hochwertiger Sichtbetonoberflächen hängt im hohen Maße von den Wechselwirkungen zwischen Beton und Trennmittel, zwischen Trennmittel und Schalmaterial, sowie von der Applikationsart und -menge des Trennmittels ab. In Laborversuchen wurden diese Einflüsse auf die Sichtbetonoberflächen eines polymermodifizierten selbstverdichtenden Betons (PSCC) im Vergleich zu einem herkömmlichen selbstverdichtenden Beton (SCC) untersucht. Im Rahmen dieser Arbeiten wurde eine Methode zur Beurteilung der Sichtbetonqualität entwickelt, mit welcher Ausschlusskriterien, wie maximale Porosität und Gleichmäßigkeit, objektiv und automatisiert bestimmt werden können. Veränderungen dieser Werte durch Witterungseinflüsse ließen zudem erste Rückschlüsse auf die Dauerhaftigkeit der Sichtbetonoberflächen zu.
The amount of adsorbed styrene acrylate copolymer (SA) particles on cementitious surfaces at the early stage of hydration was quantitatively determined using three different methodological approaches: the depletion method, the visible spectrophotometry (VIS) and the thermo-gravimetry coupled with mass spectrometry (TG–MS). Considering the advantages and disadvantages of each method, including the respectively required sample preparation, the results for four polymer-modified cement pastes, varying in polymer content and cement fineness, were evaluated.
To some extent, significant discrepancies in the adsorption degrees were observed. There is a tendency that significantly lower amounts of adsorbed polymers were identified using TG-MS compared to values determined with the depletion method. Spectrophotometrically generated values were lying in between these extremes. This tendency was found for three of the four cement pastes examined and is originated in sample preparation and methodical limitations.
The main influencing factor is the falsification of the polymer concentration in the liquid phase during centrifugation. Interactions in the interface between sediment and supernatant are the cause. The newly developed method, using TG–MS for the quantification of SA particles, proved to be suitable for dealing with these revealed issues. Here, instead of the fluid phase, the sediment is examined with regard to the polymer content, on which the influence of centrifugation is considerably lower.
As part of an international research project – funded by the European Union – capillary glasses for facades are being developed exploiting storage energy by means of fluids flowing through the capillaries. To meet highest visual demands, acrylate adhesives and EVA films are tested as possible bonding materials for the glass setup. Especially non-destructive methods (visual analysis, analysis of birefringent properties and computed tomographic data) are applied to evaluate failure patterns as well as the long-term behavior considering climatic influences. The experimental investigations are presented after different loading periods, providing information of failure developments. In addition, detailed information and scientific findings on the application of computed tomographic analyses are presented.
Conventional superplasticizers based on polycarboxylate ether (PCE) show an intolerance to clay minerals due to intercalation of their polyethylene glycol (PEG) side chains into the interlayers of the clay mineral. An intolerance to very basic media is also known. This makes PCE an unsuitable choice as a superplasticizer for geopolymers. Bio-based superplasticizers derived from starch showed comparable effects to PCE in a cementitious system. The aim of the present study was to determine if starch superplasticizers (SSPs) could be a suitable additive for geopolymers by carrying out basic investigations with respect to slump, hardening, compressive and flexural strength, shrinkage, and porosity. Four SSPs were synthesized, differing in charge polarity and specific charge density. Two conventional PCE superplasticizers, differing in terms of molecular structure, were also included in this study. The results revealed that SSPs improved the slump of a metakaolin-based geopolymer (MK-geopolymer) mortar while the PCE investigated showed no improvement. The impact of superplasticizers on early hardening (up to 72 h) was negligible. Less linear shrinkage over the course of 56 days was seen for all samples in comparison with the reference. Compressive strengths of SSP specimens tested after 7 and 28 days of curing were comparable to the reference, while PCE led to a decline. The SSPs had a small impact on porosity with a shift to the formation of more gel pores while PCE caused an increase in porosity. Throughout this research, SSPs were identified as promising superplasticizers for MK-geopolymer mortar and concrete.
Research into bio-based epoxy resins has intensified in recent decades. Here, it is of great importance to use raw materials whose use does not compete with food production. In addition, the performance of the newly developed materials should be comparable to that of conventional products. Possible starting materials are lignin degradation products, such as vanillin and syringaldehyde, for which new synthesis routes to the desired products must be found and their properties determined. In this article, the first synthesis of two amine hardeners, starting with vanillin and syringaldehyde, using the Smiles rearrangement reaction is reported. The amine hardeners were mixed with bisphenol A diglycidyl ether, and the curing was compared to isophorone diamine, 4-4′-diaminodiphenyl sulfone, and 4-Aminonbenzylamine by means of differential scanning calorimetry. It was found that the two amines prepared are cold-curing. As TG-MS studies showed, the thermal stability of at least one of the polymers prepared with the potentially bio-based amines is comparable to that of the polymer prepared with isophorone diamine, and similar degradation products are formed during pyrolysis.