Refine
Document Type
- Doctoral Thesis (21)
- Conference Proceeding (10)
- Article (5)
- Master's Thesis (2)
- Preprint (1)
- Report (1)
Institute
- F. A. Finger-Institut für Baustoffkunde (FIB) (13)
- Professur Werkstoffe des Bauens (6)
- Professur Baustatik und Bauteilfestigkeit (5)
- Professur Informatik im Bauwesen (5)
- Institut für Strukturmechanik (ISM) (4)
- Institut für Konstruktiven Ingenieurbau (IKI) (1)
- Juniorprofessur Polymere Bindemittel und Baustoffe im Bauwesen (1)
- Professur Allgemeine Baustoffkunde (1)
- Professur Bauphysik (1)
- Professur Holz- und Mauerwerksbau (1)
Keywords
- Beton (40) (remove)
Increasing structural robustness is the goal which is of interest for structural engineering community. The partial collapse of RC buildings is subject of this dissertation. Understanding the robustness of RC buildings will guide the development of safer structures against abnormal loading scenarios such as; explosions, earthquakes, fine, and/or long-term accumulation effects leading to deterioration or fatigue. Any of these may result in local immediate structural damage, that can propagate to the rest of the structure causing what is known by the disproportionate collapse.
This work handels collapse propagation through various analytical approaches which simplifies the mechanical description of damaged reinfoced concrete structures due to extreme acidental event.
Die Festigkeitsentwicklung des Zementbetons basiert auf der chemischen Reaktion des Zementes mit dem Anmachwasser. Durch Nachbehandlungsmaßnahmen muss dafür gesorgt werden, dass dem Zement genügend Wasser für seine Reaktion zur Verfügung steht, da sonst ein Beton mit minderer Qualität entsteht. Die vorliegende Arbeit behandelt die grundsätzlichen Fragen der Betonnachbehandlung bei Anwendung von Straßenbetonen. Im Speziellen wird die Frage des erforderlichen Nachbehandlungsbedarfs von hüttensandhaltigen Kompositzementen betrachtet. Die Wirkung der Nachbehandlung wird anhand des erreichten Frost-Tausalz-Widerstandes und der Gefügeausbildung in der unmittelbaren Betonrandzone bewertet. Der Fokus der Untersuchungen lag auf abgezogenen Betonoberflächen. Es wurde ein Modell zur Austrocknung des jungen Betons erarbeitet. Es konnte gezeigt werden, dass in einer frühen Austrocknung (Kapillarphase) keine kritische Austrocknung der Betonrandzone einsetzt, sondern der Beton annährend gleichmäßig über die Höhe austrocknet. Es wurde ein Nomogramm entwickelt, mit dem die Dauer der Kapillarphase in Abhängigkeit der Witterung für Straßenbetone abgeschätzt werden kann. Eine kritische Austrocknung der wichtigen Randzone setzt nach Ende der Kapillarphase ein. Für Betone unter Verwendung von Zementen mit langsamer Festigkeitsentwicklung ist die Austrocknung der Randzone nach Ende der Kapillarphase besonders ausgeprägt. Im Ergebnis zeigen diese Betone dann einen geringen Frost-Tausalz-Widerstand. Mit Zementen, die eine 2d-Zementdruckfestigkeit ≥ 23,0 N/mm² aufweisen, wurde unabhängig von der Zementart (CEM I oder CEM II/B-S) auch dann ein hoher Frost-Tausalz-Widerstand erreicht, wenn keine oder eine schlechtere Nachbehandlung angewendet wurde. Für die Praxis ergibt sich damit eine einfache Möglichkeit der Vorauswahl von geeigneten Zementen für den Verkehrsflächenbau. Betone, die unter Verwendung von Zementen mit langsamere Festigkeitsentwicklung hergestellt werden, erreichen einen hohen Frost-Tausalz-Widerstand nur mit einer geeigneten Nachbehandlung. Die Anwendung von flüssigen Nachbehandlungsmitteln (NBM gemäß TL NBM-StB) erreicht eine ähnliche Wirksamkeit wie eine 5 tägige Feuchtnachbehandlung. Voraussetzung für die Wirksamkeit der NBM ist, dass sie auf eine Betonoberfläche ohne sichtbaren Feuchtigkeitsfilm (feuchter Glanz) aufgesprüht werden. Besonders wichtig ist die Beachtung des richtigen Auftragszeitpunktes bei kühler Witterung, da hier aufgrund der verlangsamten Zementreaktion der Beton länger Anmachwasser abstößt. Ein zu früher Auftrag des Nachbehandlungsmittels führt zu einer Verschlechterung der Qualität der Betonrandzone. Durch Bereitstellung hydratationsabhängiger Transportkenngrößen (Feuchtetransport im Beton) konnten numerische Berechnungen zum Zusammenspiel zwischen der Austrocknung, der Nachbehandlung und der Gefügeentwicklung durchgeführt werden. Mit dem erstellten Berechnungsmodell wurden Parameterstudien durchgeführt. Die Berechnungen bestätigen die wesentlichen Erkenntnisse der Laboruntersuchungen. Darüber hinaus lässt sich mit dem Berechnungsmodell zeigen, dass gerade bei langsam reagierenden Zementen und kühler Witterung ohne eine Nachbehandlung eine sehr dünne Randzone (ca. 500 µm – 1000 µm) mit stark erhöhter Kapillarporosität entsteht.
Einfluss der Porosität von Beton auf den Ablauf einer schädigenden Alkali-Kieselsäure-Reaktion
(2016)
Der Dissertation liegt die Frage zugrunde, welchen Einfluss die Porosität von Beton auf den Ablauf einer schädigenden AKR hat. Insbesondere soll geklärt werden, ob der Einsatz von Gleitschalungsfertigern – anstelle von klassischen schienengeführten Betondeckenfertigern – und die damit verbundene verringerte Porosität der Betone den Ablauf einer schädigenden AKR begünstigt. Eine verringerte Porosität führt zu einer reduzierten Duktilität des Betons, so dass infolge AKR entstehende Zugspannungen schlechter abgebaut werden können. Weiterhin steht ein geringerer Expansionsraum für das entstehende AKR-Gel zur Verfügung. Diese Faktoren können den Ablauf einer AKR begünstigen. Allerdings können extern anstehende Alkalien schlechter in den Beton mit einer verringerten Porosität eindringen. Ferner wird die Diffusion der Alkalien zu den potenziell reaktiven Gesteinskörnungen verlangsamt.
Zur Beantwortung der aufgeworfenen Frage wird unter Einsatz einer neuartigen Prüfmethodologie und bei variierender Porosität untersucht, welche Schädigungsparameter maßgebend für den Ablauf und die Intensität einer schädigenden AKR sind. Die berücksichtigten Schädigungsparameter sind die mechanischen Eigenschaften des Betons, der zur Verfügung stehende Expansionsraum und die im Beton ablaufenden Transportvorgänge. Um den Einfluss der jeweiligen Schädigungsparameter spezifizieren zu können, gehen die Prüfungen einerseits von einem hohen internen und andererseits von einem hohen externen AKR-Schädigungspotenzial aus. In beiden Fällen erfolgen die Untersuchungen an langsam reagierenden alkaliempfindlichen Gesteinskörnungen. Die unterschiedlichen Porositäten ergeben sich hauptsächlich durch Variation des w/z-Wertes.
Bei dem hohen internen AKR-Schädigungspotenzial stehen die mechanischen Eigenschaften und der Expansionsraum im Vordergrund; außerdem ist der Einfluss der Zugabe eines LP-Bildners zu analysieren. Um ein hohes internes AKR-Schädigungspotenzial zu erreichen, kommt bei der Herstellung der Betonprobekörper ein Zement mit einem hohen Alkaligehalt zum Einsatz. Die Betonprobekörper werden der 40 °C-Nebelkammerlagerung und dem 60 °C-Betonversuch über Wasser unterzogen. Dabei findet eine neue Prüfmethodologie Anwendung, die der kontinuierlichen Messung der Dehnung und der ablaufenden Erhärtungs- und Rissbildungsprozesse dient. Diese Prüfmethodologie umfasst die Messung der Ultraschallgeschwindigkeit, die Schallemissionsanalyse und die µ-3D-Computertomografie.
Hingegen richtet sich der Fokus bei dem hohen externen AKR-Schädigungspotenzial auf die Transportvorgänge. Zur Provokation eines hohen externen AKR-Schädigungspotenzials werden die Probekörper der FIB-Klimawechsellagerung ausgesetzt.
Druckbeanspruchte Bauteile aus Beton können mit zugfesten Umschnürungen von außen verstärkt werden. Mit dieser etablierten Methode konnten axiale Traglast und Duktilität von unzureichend bewehrten Stützen bereits verbessert werden. Es wurde jedoch festgestellt, dass der umschnürte Betonkern dennoch an Festigkeit verliert. Um die Wirksamkeit der Umschnürung zu erhöhen, wird deshalb vorgeschlagen, das umschnürende Material vorzuspannen. Dieser Vorschlag wird insbesondere von der neuen Materialgruppe der Formgedächtnislegierungen inspiriert, die thermisch vorspannbar sind.
Bisher sind die Auswirkungen der Vorspannung einer Umschnürung auf das Tragverhalten von Betondruckgliedern kaum untersucht worden. Diese Lücke wird durch systematische Versuche an Betonzylindern mit vorgespannter Umschnürung aus Stahl und kohlenstofffaserverstärktem Kunststoff geschlossen. Die Abbildung der Versuchsergebnisse durch geeignete Modelle ermöglicht auch Aussagen zum Verhalten von Betondruckgliedern mit Umschnürungen aus anderen Materialien, beispielsweise Formgedächtnislegierungen. Um diese in den Berechnungen zu simulieren, wird eine für das Bauwesen infrage kommende eisenbasierte Legierung in separaten axialen Versuchen charakterisiert und thermisch vorgespannt. Die in der vorliegenden Arbeit entwickelten neuen Modelle orientieren sich im Wesentlichen an zwei Zielen: dem Abbilden des mehraxialen Spannungs-Dehnungs-Verhaltens des vorgespannt umschnürten Betons und dem Berechnen der Restfestigkeit des Betons.
Die durchgeführten Versuche und Parameterstudien auf Basis der Modelle zeigen: Die Vorspannung der Umschnürung beeinflusst vor allem die Restfestigkeit des Betons wesentlich. Die gewonnenen Erkenntnisse und neuen Methoden können eingesetzt werden, um das Tragverhalten von Betondruckgliedern mit Umschnürungen aus Stahl, faserverstärktem Kunststoff oder Formgedächtnislegierungen zu bewerten.
Das Hauptziel der Arbeit war es zu klären, ob alkalihaltige Enteisungsmittel eine Alkali-Kieselsäure-Reaktion (AKR) auslösen und/oder beschleunigen können und was die dabei ggf. zugrunde liegenden Mechanismen sind. Die Untersuchungen dazu ergaben, dass die auf Verkehrsflächen eingesetzten alkalihaltigen Enteisungsmittel auf Basis von Natriumchlorid (Fahrbahndecken) bzw. auf Basis der Alkaliacetate und -formiate (Flugbetriebsflächen) den Ablauf einer AKR in Betonen mit alkalireaktiven Gesteinskörnungen auslösen und mitunter stark beschleunigen können. Dabei nimmt die AKR-fördernde Wirkung der Enteisungsmittel in der Reihenfolge Natriumchlorid - Alkaliacetate - Alkaliformiate erheblich zu.
Es zeigte sich, dass im Fall der Alkaliacetate und -formiate nicht allein die Zufuhr von Alkalien von Bedeutung ist, sondern dass es außerdem zu einer Freisetzung von OH-Ionen aus dem Portlandit und folglich zu einem Anstieg des pH-Wertes in der Porenlösung kommt. Dadurch wird der Angriff auf alkalireaktives SiO2 in Gesteinskörnungen verstärkt und der Ablauf einer AKR beschleunigt. Unter äußerer NaCl-Zufuhr kommt es hingegen nicht zu einem Anstieg des pH-Wertes, was der Grund für die weniger stark AKR-fördernde Wirkung von NaCl ist. Von Bedeutung sind hier die zugeführten Na-Ionen und offenbar ein sich andeutender, direkter Einfluss von NaCl auf das SiO2-Löseverhalten. Sind pH-Wert und Na-Konzentration in der Porenlösung ausreichend hoch, wird sich thermodynamisch bedingt AKR-Gel bilden. Die Bildung von FRIEDEL’schem Salz ist dabei nur eine Begleiterscheinung, aber keine Voraussetzung für den Ablauf einer AKR unter äußerer NaCl-Zufuhr.
Es zeigte sich weiter, dass sich mit der FIB-Klimawechsellagerung als Performance-Prüfung das AKR-Schädigungspotential von Betonen für Fahrbahndecken und Flugbetriebsflächen zuverlässig beurteilen lässt. Die Vorteile der FIB-Klimawechsellagerung liegen in der Prüfung kompletter, projektspezifischer Betonzusammensetzungen unter Beachtung aller praxisrelevanten klimatischen Einwirkungen und vor allem in der Berücksichtigung einer äußeren Alkalizufuhr. Innerhalb von 36 Wochen kann das AKR-Schädigungspotential einer Betonzusammensetzung für eine Nutzungsdauer von 20-30 Jahren in der Praxis sicher beurteilt werden.
In dieser Arbeit werden die Ergebnisse von experimentellen Untersuchungen an unbewehrten und bewehrten modifizierten Betonen unter monoton steigender Belastung bis zum Bruch, einfacher Kurzzeitbelastung im Grenzbereich der Tragfähigkeit und mehrfach wiederholter Belastung mit kontinuierlicher Be- und Entlastungsgeschwindigkeit vorgestellt und ausgewertet. Für die Modifizierung der Betone wurden zwei grundsätzliche Vorgehens¬weisen angewendet: die Variation der Gesteinskörnung und die Modifizierung der Bindemittelphase mit thermoplastischen Polymeren. Die Auswirkungen der Modifikationen auf die Festigkeitseigenschaften und das Formänderungsverhalten des Betons bei Kurzzeitbelastung waren dabei von besonderem Interesse.
Die beobachteten Veränderungen der Festbetoneigenschaften sowie der nichtlineare Zu-sammenhang zwischen den elastischen und nichtelastischen Verformungsanteilen signali-sieren, dass derartige Modifizierungen das Verformungs- und Bruchverhalten von Beton sig-nifikant beeinflussen und somit beim Nachweis der Tragfähigkeit und Gebrauchstauglichkeit berücksichtigt werden müssen. Neben der Evaluierung des beanspruchungsabhängigen Formänderungsverhaltens werden die etablierten Ansätze zur Beschreibung der Gefügezu-standsbereiche bei Druckbelastung weiter entwickelt, so dass die Übergänge zwischen den Bereichen exakt ermittelt und die Ausprägung der Bereiche quantifiziert werden können. Damit ist ein genauerer Vergleich der durch die Modifizierungen hervorgerufenen Verände-rungen möglich.
The nonlinear behavior of concrete can be attributed to the propagation of microcracks within the heterogeneous internal material structure. In this thesis, a mesoscale model is developed which allows for the explicit simulation of these microcracks. Consequently, the actual physical phenomena causing the complex nonlinear macroscopic behavior of concrete can be represented using rather simple material formulations. On the mesoscale, the numerical model explicitly resolves the components of the internal material structure. For concrete, a three-phase model consisting of aggregates, mortar matrix and interfacial transition zone is proposed. Based on prescribed grading curves, an efficient algorithm for the generation of three-dimensional aggregate distributions using ellipsoids is presented. In the numerical model, tensile failure of the mortar matrix is described using a continuum damage approach. In order to reduce spurious mesh sensitivities, introduced by the softening behavior of the matrix material, nonlocal integral-type material formulations are applied. The propagation of cracks at the interface between aggregates and mortar matrix is represented in a discrete way using a cohesive crack approach. The iterative solution procedure is stabilized using a new path following constraint within the framework of load-displacement-constraint methods which allows for an efficient representation of snap-back phenomena. In several examples, the influence of the randomly generated heterogeneous material structure on the stochastic scatter of the results is analyzed. Furthermore, the ability of mesoscale models to represent size effects is investigated. Mesoscale simulations require the discretization of the internal material structure. Compared to simulations on the macroscale, the numerical effort and the memory demand increases dramatically. Due to the complexity of the numerical model, mesoscale simulations are, in general, limited to small specimens. In this thesis, an adaptive heterogeneous multiscale approach is presented which allows for the incorporation of mesoscale models within nonlinear simulations of concrete structures. In heterogeneous multiscale models, only critical regions, i.e. regions in which damage develops, are resolved on the mesoscale, whereas undamaged or sparsely damage regions are modeled on the macroscale. A crucial point in simulations with heterogeneous multiscale models is the coupling of sub-domains discretized on different length scales. The sub-domains differ not only in the size of the finite elements but also in the constitutive description. In this thesis, different methods for the coupling of non-matching discretizations - constraint equations, the mortar method and the arlequin method - are investigated and the application to heterogeneous multiscale models is presented. Another important point is the detection of critical regions. An adaptive solution procedure allowing the transfer of macroscale sub-domains to the mesoscale is proposed. In this context, several indicators which trigger the model adaptation are introduced. Finally, the application of the proposed adaptive heterogeneous multiscale approach in nonlinear simulations of concrete structures is presented.
From a macroscopic point of view, failure within concrete structures is characterized by the initiation and propagation of cracks. In the first part of the thesis, a methodology for macroscopic crack growth simulations for concrete structures using a cohesive discrete crack approach based on the extended finite element method is introduced. Particular attention is turned to the investigation of criteria for crack initiation and crack growth. A drawback of the macroscopic simulation is that the real physical phenomena leading to the nonlinear behavior are only modeled phenomenologically. For concrete, the nonlinear behavior is characterized by the initiation of microcracks which coalesce into macroscopic cracks. In order to obtain a higher resolution of this failure zones, a mesoscale model for concrete is developed that models particles, mortar matrix and the interfacial transition zone (ITZ) explicitly. The essential features are a representation of particles using a prescribed grading curve, a material formulation based on a cohesive approach for the ITZ and a combined model with damage and plasticity for the mortar matrix. Compared to numerical simulations, the response of real structures exhibits a stochastic scatter. This is e.g. due to the intrinsic heterogeneities of the structure. For mesoscale models, these intrinsic heterogeneities are simulated by using a random distribution of particles and by a simulation of spatially variable material parameters using random fields. There are two major problems related to numerical simulations on the mesoscale. First of all, the material parameters for the constitutive description of the materials are often difficult to measure directly. In order to estimate material parameters from macroscopic experiments, a parameter identification procedure based on Bayesian neural networks is developed which is universally applicable to any parameter identification problem in numerical simulations based on experimental results. This approach offers information about the most probable set of material parameters based on experimental data and information about the accuracy of the estimate. Consequently, this approach can be used a priori to determine a set of experiments to be carried out in order to fit the parameters of a numerical model to experimental data. The second problem is the computational effort required for mesoscale simulations of a full macroscopic structure. For this purpose, a coupling between mesoscale and macroscale model is developed. Representative mesoscale simulations are used to train a metamodel that is finally used as a constitutive model in a macroscopic simulation. Special focus is placed on the ability of appropriately simulating unloading.
Die Abkürzung PCC bezieht sie sich hier auf Polymer modified Cement Concrete, also mit Kunststoffen modifizierte Mörtel und Betone. Hierfür hat sich diese Abkürzung auch international durchgesetzt. Sie bezeichnet Baustoffe, die neben dem mineralischen Bindemittel Zement auch Kunststoffe enthalten. Zement und Kunststoff erzielen im späteren Mörtel bzw. Beton eine gemeinschaftliche Bindemittelwirkung. Wiederholter Gegenstand von Schadensfällen ist das Versagen des Haftverbundes zu anderer Bausubstanz. Da PCC häufig als dünne Schutzschicht auf vorhandenen Beton aufgetragen werden, führt ein Versagen der Adhäsion früher oder später auch zu einem Versagen dieser Schutzfunktion. Umgekehrt kann ein Versagen des Schutzes infolge von Rissen im PCC auch im Nachhinein zum Ablösen der Beschichtung führen. Ursächlich für dieses kohäsive Versagen sind dabei i. d. R. die Auswahl falscher bzw. nicht aufeinander abgestimmter Baustoffsysteme oder schlicht Verarbeitungsfehler. Das Ziel dieser Arbeit war es zu untersuchen, welchen Einfluss die kohäsiven und adhäsiven Eigenschaften von PCC auf deren Dauerhaftigkeit, insbesondere bei der Anwendung als Beschichtungsmaterial, haben. Dazu wurden vier maßgebliche Schwerpunkte bearbeitet. Eine zentrale Rolle für die Dauerhaftigkeit eines Beschichtungsmaterials spielt dessen Längenänderungsverhalten. Der Betrag der positiven und negativen Längenänderungen ist bestimmend für die Spannungen, die im Beschichtungsmaterial entstehen können. Sind die auftretenden Spannungen höher als die Zugfestigkeit des PCC erfolgt der Spannungsabbau durch Risse. Es kommt also zum Kohäsionsversagen im Mörtel. Wird der PCC als Beschichtungsmaterial genutzt, werden die Spannungen im Idealfall über die Verbundebene zum Beschichtungsuntergrund übertragen. Übersteigen dabei diese Spannungen die maximal aufnehmbaren Verbundspannungen, kommt es zum Adhäsionsversagen zwischen Beschichtung und Untergrund. In Modellversuchen werden die Effekte des Längenänderungsverhaltens kunststoffmodifizierter Zementsteine auf den Haftverbund zu einer Gesteinskörnung untersucht. Dadurch werden Rückschlüsse auf die Kohäsion innerhalb der PCC durch die Beschreibung des adhäsiven Verbundes zwischen Zementsteinmatrix und Gesteinskörnung gezogen. Neben der Längenänderung sind auch die Festigkeitseigenschaften der PCC bedeutsam für deren Dauerhaftigkeit. Es werden die Festigkeitseigenschaften kunststoffmodifizierter Mörtel und Betone nicht nur von der mechanischen Seite betrachtet. Der Focus liegt vielmehr auf der Beschreibung der durch die Kunststoffe beeinflussten kohäsiven Eigenschaften bei mechanischer Belastung. Es wird das Verhalten der polymeren Matrix nach einer Kurzzeitbelastung untersucht. Damit werden die Vorgänge, die letztlich zu einer Beeinflussung der Festigkeitseigenschaften führen, dargestellt. In diesem Zusammenhang wird auch der Einfluss der Temperatur auf die Festigkeit der PCC betrachtet. Die Untersuchung des Frost-Taumittel-Widerstandes mittels CDF- bzw. CIF-Verfahrens ist eine gute Möglichkeit, neben der Beurteilung der Dauerhaftigkeit auch Rückschlüsse auf die kohäsiven als auch, im mikroskopischen Maßstab betrachtet, die adhäsiven Eigenschaften der PCC zu ziehen. Damit ist gemeint, dass die Kohäsion von PCC durch deren adhäsive Eigenschaften zwischen kunststoffmodifizierter Zementsteinmatrix und Gesteinskörnern maßgeblich bestimmt wird. Einerseits kann bei starkem Abfall des relativen dynamischen E-Moduls von einer geringeren Kohäsion des PCC ausgegangen werden. Dies würde dann bei einem Mörtel eher zu Rissen führen, über die wiederum betonaggressive Medien eindringen können. Im Gegensatz dazu deutet ein konstant bleibender relativer dynamischer E-Modul auf eine hohe Kohäsion und damit, bei Anwendung des PCC als Beschichtungsmaterial, auf ein höheres adhäsives Versagensrisiko der Beschichtung hin. Andererseits stellt eine höhere Abwitterung, also sozusagen das schichtenweise kohäsive Versagen, eine Gefahr bei dünnen Beschichtungen dar. Dies könnte noch durch die Anwendung anderer Taumittel (z. B. organischer) verstärkt werden. Unter diesen Gesichtspunkten wurden Untersuchungen auf der Basis des CDF-Testes sowie zur Lösungsaufnahmefähigkeit der PCC durchgeführt. Der adhäsive Verbund von PCC zu Beton ist von vielen Faktoren abhängig. Bisher kaum betrachtet wurde die Art des Aufbringens oder der Einfluss der Probengeometrie bei Laborversuchen. Diese sowie der Einfluss einer Salzbelastung des Untergrundes bzw. der Beschichtung wurden untersucht. Ein Teil der durchgeführten Untersuchungen wurde im Rahmen des Teilprojektes B3 „Dauerhaftigkeit polymermodifizierter Mörtel und Betone“ des von der DFG geförderten Sonderforschungsbereiches 524 „Werkstoffe und Konstruktionen für die Revitalisierung von Bau-werken“ realisiert.
Im Rahmen dieser Arbeit wurden über verschiedene Herstellungsverfahren 48 Gelproben erzeugt und auf ihr Quellverhalten untersucht. Dabei wurde eine Wiederholbarkeit der Messungen mit anderen Bearbeitern überprüft und nachgewiesen. Es zeigt sich in den Quellversuchen, dass hohe Alkaligehalte in den Gelproben bei einer niedrigen Löslichkeit (durch geringe Mengen Calcium in der Probe hervorgerufen) hohe Quelldrücke erzeugen. Ein Einfluss des Natrium-Kalium-Verhältnisses (Alkaliverhältnis) auf das Quellverhalten der Gelproben ist nicht zu erkennen. Der Einfluss des Calciums im Gel zeichnet sich deutlich ab, ohne Calcium bauen die Proben keine Quelldrücke auf, bei zu hohen Calciumgehalten entstehen nicht quellfähige Alkali-Calcium-Silikat-Hydrate. Ein quellfähiger Bereich kann von ca. 5 % bis zu ca. 30 % Calciumanteil im Gel angegeben werden. Neben dem Einfluss des Calciumgehaltes auf das Quellverhalten der Gele ist auch ein Einfluss des Alkali-Silika-Verhältnisses in den Proben nachweisbar. Wird dieses Verhältnis in den Proben stark Richtung Kieselsäure verschoben, d. h. niedrige Alkalianteile im Gel, kommt es zu keinen Quellerscheinungen. Somit kann die Wirkung von AKR-vermeidenden Zusätzen (FA, Silika usw.) mit diesen Messungen bestätigt werden. Es kann gezeigt werden, dass die ermittelten Quelldrücke eines Alkalikiesel-Gels ein Gesteinskorn oder/und die umgebende Matrix zerstören können. Aus diesen oben genannten Erkenntnissen wird ein Bereich einer quellfähigen Zusammensetzung eines Gels in einem Dreistoffdiagramm angegeben und es können folgende Schlussfolgerungen gezogen werden: •Ein Quelldruck kann in einem AK-Gel nur bei einer bestimmten Menge an eingebautem Calcium aufgebaut werden. •Diese Quelldrücke können deutlich Werte über 10 N/mm² erreichen. •Die im Beton verwendeten Gesteinskörnungen und auch die sie umschließende Mörtelmatrix können mit Quelldrücken in den hier bestimmten Größenordnungen zerstört werden. •Die bekannten Modelle zur Alkali-Kieselsäure-Reaktion müssen um den Einbau des Calciums in ein entstandenes AK-Gel erweitert werden.