Filtern
Dokumenttyp
- Artikel (Wissenschaftlicher) (11)
- Dissertation (11)
- Konferenzveröffentlichung (1)
- Diplomarbeit (1)
- Habilitation (1)
Institut
- Professur Bauchemie und Polymere Werkstoffe (25) (entfernen)
Schlagworte
- Bindemittel (4)
- Wasserglas (4)
- Geopolymere (3)
- Mikrostruktur (3)
- Mörtel (3)
- Alkalisilikat (2)
- Alumosilikat (2)
- Bauchemie (2)
- Epoxidharz (2)
- Geopolymer (2)
Research into bio-based epoxy resins has intensified in recent decades. Here, it is of great importance to use raw materials whose use does not compete with food production. In addition, the performance of the newly developed materials should be comparable to that of conventional products. Possible starting materials are lignin degradation products, such as vanillin and syringaldehyde, for which new synthesis routes to the desired products must be found and their properties determined. In this article, the first synthesis of two amine hardeners, starting with vanillin and syringaldehyde, using the Smiles rearrangement reaction is reported. The amine hardeners were mixed with bisphenol A diglycidyl ether, and the curing was compared to isophorone diamine, 4-4′-diaminodiphenyl sulfone, and 4-Aminonbenzylamine by means of differential scanning calorimetry. It was found that the two amines prepared are cold-curing. As TG-MS studies showed, the thermal stability of at least one of the polymers prepared with the potentially bio-based amines is comparable to that of the polymer prepared with isophorone diamine, and similar degradation products are formed during pyrolysis.
Calcined clays are interesting starting materials to be used as SCMs (supplementary cementitious materials) in cements or to be converted to geopolymers by activation with a high alkaline activator. The adjustment of the properties in the fresh state, especially regarding the consistency of these binders, is almost exclusively achieved by the addition of water, since commercially available superplasticizers seem to be ineffective in low-calcium geopolymer systems. The aim of this study was a systematic investigation of various PCE (polycarboxylate ester/ether) superplasticizers (methacrylate ester PCE: MPEG, isoprenol ether PCE: IPEG, methallyl ether PCE: HPEG) with respect to their stability in different alkaline activators (NaOH, KOH, sodium and potassium silicate solutions). The effectiveness of superplasticizers (SPs) in low-calcium geopolymer binders was verified by rheological tests. Size exclusion chromatography was used to investigate if structural degradation of the superplasticizers occurs. The investigated PCE superplasticizers showed a thickening effect in the low-calcium geopolymer system. Depending on the alkalinity of the activator solution, a degradation process was detected for all the PCEs investigated. The side chains of the PCEs are cleaved off the backbone by basic ester and ether hydrolysis. The highest degree of degradation was found in sodium and potassium silicate solutions. In alkaline hydroxide solutions, the degradation process increases with increasing alkalinity.
Das Ziel dieser Arbeit war es, neuartige Fließmittel auf Basis von Stärke als nachwachsenden Rohstoff zu synthetisieren und die Wechselwirkung mit Portlandzement zu charakterisieren. Die Notwendigkeit, Alternativen zu synthetischen Zusatzmittel zu erforschen, ergibt sich aus der benötigten Menge zur Verarbeitung von ca. 4,1 Gt/a, wobei ca. 85 % der Zusatzmittel auf die Fließmittel entfallen.
Um Fließmittel aus Stärke zu synthetisieren, wurden drei Basisstärken unterschiedlicher Herkunft verwendet. Es wurde eine Maniokstärke mit einer niedrigen Molekularmasse und eine Weizenstärke mit einer hohen Molekularmasse verwendet. Darüber hinaus wurde eine Kartoffelstärke mit einer mittleren Molekularmasse, die ein Abfallprodukt der kartoffelverarbeitenden Industrie darstellt, genutzt. Die Stärkefließmittel wurden durch chemische Modifikation in einem zweistufigen Prozess synthetisiert. Im ersten Schritt wurde das Molekulargewicht der Weizen- und Kartoffelstärke durch säurehydrolytischen Abbau verringert. Für die kurzkettige Maniokstärke war eine Degradation der Molekularmasse nicht notwendig. Im zweiten Syntheseschritt wurden anionische Ladungen durch das Versetzen der degradierten Stärken und Maniokstärke mit Natriumvinylsulfonat in die Stärkemoleküle eingeführt.
Beurteilung der Synthesemethode zur Erzeugung von Stärkefließmitteln
In diesem Zusammenhang sollten molekulare Parameter der Stärkefließmittel gezielt eingestellt werden, um eine Fließwirkung im Portlandzement zu erhalten. Insbesondere die Molekularmasse und die Menge anionischer Ladungen sollte variiert werden, um Abhängigkeiten mit der Dispergierleistung zu identifizieren.
1. Es konnte durch GPC-Messungen gezeigt werden, dass die Molekularmasse der langkettigen Weizenstärke durch die gewählten Modifizierungsbedingungen zum säurehydrolytischen Abbau verringert werden konnte. Durch Variation der säurehydrolytischen Bedingungen wurden 4 degradierte Weizenstärken erzeugt, die eine Reduzierung der Molekularmasse um 27,5 – 43 % aufwiesen. Die Molekularmasse der Kartoffelstärke konnte durch säurehydrolytischen Abbau um ca. 26 % verringert werden.
2. Durch PCD-Messungen wurde gezeigt, dass anionische Ladungen durch Sulfoethylierung der freien Hydroxylgruppen in die degradierten Stärken eingeführt werden konnten. Durch Variation der Dauer der Sulfoethylierung konnte die Menge der anionischen Ladungen gesteuert und gezielt variiert werden, so dass Stärkefließmittel mit steigender Ladungsmenge in folgender Reihenfolge synthetisiert wurden:
W-3 < W-2 < K-1 < W¬-4 < W¬1 < M-1
Im Ergebnis der chemischen Modifizierung konnten 6 Stärkefließmittel mit variierten Molekularmassen und anionischen Ladungen erzeugt werden. Es konnte gezeigt werden, dass die Herkunft der Stärke für die chemische Modifizierung unerheblich ist. Die Fließmittel lagen synthesebedingt als basische, wässrige Suspensionen mit Wirkstoffgehalten im Bereich von 23,5 – 50 % vor.
Beurteilung der Dispergierleistung der synthetisierten Stärkefließmittel
Die Dispergierperformance wurde durch rheologische Experimente mit einem Rotationsviskosimeter erfasst. Dabei wurden der Einfluss auf die Fließkurven und die Viskositätskurven betrachtet. Durch Vergleich der Dispergierleistung mit einem Polykondensat- und einem PCE-Fließmittel konnte eine Einordnung und Bewertung der Fließmittel vorgenommen werden.
3. Die rheologische Experimente haben gezeigt, dass die Stärkefließmittel eine vergleichbar hohe Dispergierleistung aufweisen, wie das zum Vergleich herangezogen PCE-Fließmittel. Darüber hinaus zeigte sich, dass die Fließwirkung der 6 Stärkefließmittel gegenüber dem Polykondensatfließmittel deutlich höher ist. Das aus der Literatur bekannte Einbrechen der Dispergierleistung der Polykondensat-fließmittel bei w/z-Werten < 0,4 konnte bestätigt werden.
4. Alle 6 Stärkefließmittel führten zu einer Verringerung der Fließgrenze und der dynamischen Viskosität des Zementleimes bei einem w/z-Wert von 0,35.
5. Der Vergleich der Dispergierleistung der Stärkefließmittel untereinander zeigte, dass die anionische Ladungsmenge einen Schlüsselparameter darstellt. Die Stärkefließmittel M-1, K-1, W-1 und W-4 mit anionischen Ladungsmengen > 6 C/g zeigten die höchste Dispergier¬performance. Die vergleichend herangezogenen klassischen Fließmittel wiesen anionische Ladungsmengen im Bereich von 1,2 C/g (Polycondensat) und 1,6 C/g (PCE) auf. Die Molekularmasse schien für die Dispergierleistung zunächst unerheblich zu sein. Aus diesem Grund wurde die Basisweizenstärke erneut chemisch modifiziert, indem anionische Ladungen eingeführt wurden, ohne die Molekularmasse jedoch zu verringern. Das Stärkederivat wies verdickende Eigenschaften im Zementleim auf. Daraus konnte geschlussfolgert werden, dass eine definierte Grenzmolekularmasse (150.000 Da) existiert, die unterschritten werden muss, um Fließmittel aus Stärke zu erzeugen. Des Weiteren zeigen die Ergebnisse, dass durch die chemische Modifizierung sowohl Fließmittel als auch Verdicker aus Stärke erzeugt werden können.
Beurteilung der Beeinflussung der Hydratation und der Porenlösung des Portlandzementes
Aus der Literatur ist bekannt, dass Fließmittel die Hydratation von Portlandzement maßgeblich beeinflussen können. Aus diesem Grund wurden kalorimetrische und konduktometrische Untersuchungen an Zementsuspensionen, die mit den synthetisierten Stärkefließmitteln versetzt wurden, durchgeführt. Ergänzt wurden die Untersuchungen durch Porenlösungsanalysen zu verschiedenen Zeitpunkten der Hydratation.
6. Die kalorimetrischen Untersuchungen zur Beeinflussung der Hydratation des Portlandzementes zeigten, dass die dormante Periode durch die Zugabe der Stärkefließmittel z.T. erheblich verlängert wird. Es konnte gezeigt werden, dass, je höher die anionische Ladungsmenge der Stärkefließmittel ist, desto länger dauert die dormante Periode andauert. Darüber hinaus zeigte sich, dass eine niedrige Molekularmasse der Stärkefließmittel die Verlängerung der dormanten Periode begünstigt.
7. Durch die konduktometrischen Untersuchungen konnte gezeigt werden, dass alle Stärkefließmittel die Dauer des freien- und diffusionskontrollierten CSH-Phasenwachstums verlangsamen. Insbesondere die Ausfällung des Portlandits, welches mit dem Erstarrungsbeginn korreliert, erfolgt zu deutlich späteren Zeitpunkten. Des Weiteren korrelierten die konduktometrischen Untersuchungen mit der zeitlichen Entwicklung der Calciumkonzentration der Porenlösungen. Der Vergleich der Stärkefließmittel untereinander zeigte, dass die Molekularmasse ein Schlüsselparameter ist. Das Stärkefließmittel M-1 mit der geringsten Molekularmasse, welches geringe Mengen kurzkettiger Anhydroglucoseeinheiten aufweist, verzögert die Hydratphasenbildung am stärksten. Diese Wirkung ist vergleichbar mit der von Zuckern. Darüber hinaus deuteten die Ergebnisse daraufhin, dass die Stärkefließmittel auf den ersten Hydratationsprodukten adsorbieren, wodurch die Hydratphasenbildung verlangsamt wird.
Die kalorimetrischen und konduktometrischen Daten sowie die Ergebnisse der Porenlösungsanalytik des Zementes, erforderten eine genauere Betrachtung der Beeinflussung der Hydratation der Klinkerphasen C3A und C3S, durch die Stärkefließmittel. Demzufolge wurden die Untersuchungen mit den Klinkerphasen C3A und C3S in Analogie zum Portlandzement durchgeführt.
Beurteilung der Beeinflussung der Hydratation und der Porenlösung des C3A
Während die kalorimetrischen Untersuchungen zur C3A-Hydratation eine Tendenz zur verlangsamten Hydratphasenbildung durch die Stärkefließmittel aufzeigten, lieferten die konduktometrischen Ergebnisse grundlegende Erkenntnisse zur Beeinflussung der C3A-Hydratation. Das Stadium I der C3A-Hydratation ist durch einen Abfall der elektrischen Leitfähigkeit geprägt. Dies korreliert mit dem Absinken der Calciumionenkonzentration und dem Anstieg der Aluminiumionenkonzentration in der Porenlösung der C3A-Suspensionen. Im Anschluss an das Stadium I bildet sich ein Plateau in den elektrischen Leitfähigkeitskurven aus.
8. Es konnte gezeigt werden, dass die Stärkefließmittel das Stadium I der C3A-Hydratation, d.h. die Auflösung und Bildung erster Calciumaluminathydrate verlangsamen. Insbesondere die Stärkefließmittel mit höherer Molekularmasse erhöhten die Dauer des Stadium I. Das Stadium II wird durch die Stärkefließmittel in folgender Reihenfolge am stärksten verlängert: M-1 > W-3 > K-1 > W-2 ≥ W-4 und verdeutlicht, dass keine Abhängigkeit von der anionischen Ladungsmenge identifiziert werden konnte. Die Ergebnisse zeigten, dass speziell die kurzkettige Stärke M-1, das Stadium II länger aufrechterhalten.
9. Das Stadium III und IV der C3A-Hydratation wird insbesondere durch die Stärkefließmittel mit höherer Molekularmasse verlängert.
Die Ergebnisse der Porenlösungsanalytik korrelieren mit den Ergebnissen der elektrischen Leitfähigkeit. Speziell die zeitlichen Verläufe der Calciumionenkonzentration bildeten die Verläufe der Konduktivitätskurven der C3A-Hydratation mit großer Übereinstimmung ab.
Beurteilung der Beeinflussung der Hydratation und der Porenlösung des C3S
Die Ergebnisse der kalorimetrischen Untersuchungen zur Beeinflussung der C3S-Hydratation durch die Stärkefließmittel zeigen, dass diese maßgeblich verlangsamt wird. Das Maximum des Haupthydratationspeaks wird zu späteren Zeiten verschoben und auch die Höhe des Maximums wird deutlich verringert. Durch die konduktometrischen Experimente wurde aufgeklärt, welche Stadien der C3S-Hydrataion beeinflusst wurden.
10. Es konnte gezeigt werden, dass sowohl die Menge der eingebrachten anionischen Ladungen als auch das Vorhandensein sehr kleiner Stärkefließmittelmoleküle (Zucker), Schlüsselparameter der verzögerten Hydratationskinetik des C3S sind. Der grundlegende Mechanismus der Hydratationsverzögerung beruht auf einer Kombination aus verminderter CSH-Keimbildung und Adsorptionsprozessen auf den ersten gebildeten CSH-Phasen der C3S-Partikel.
Beurteilung des Adsorptionsverhaltens am Zement, C3A und C3S
Die Bestimmung des Adsorptionsverhaltens der Stärkefließmittel erfolgte mit der Phenol-Schwefelsäure-Methode an Zement,- C3A- und C3S-Suspensionen. Durch den Vergleich der Adsorptionsraten und Adsorptionsmengen in Abhängigkeit von den molekularen Parametern der Stärkefließmittel wurde ein Wechselwirkungsmodell identifiziert.
11. Die Ursache für die hohe Dispergierleistung der Stärkefließmittel liegt in Adsorptionsprozessen an den ersten gebildeten Hydratphasen des Zementes begründet. Die Molekularmasse der Stärkefließmittel ist ein Schlüsselparameter der entscheidend für den Mechanismus der Adsorption ist. Während anionische, langkettige Stärken an mehreren Zementpartikeln gleichzeitig adsorbieren und für eine Vernetzung der Zementpartikel untereinander sorgen (Verdickerwirkung), adsorbieren kurzkettige anionische Stärken lediglich an den ersten gebildeten Hydratphasen der einzelnen Zementpartikel und führen zu elektrostatischer Abstoßung (Fließmittelwirkung).
12. Es konnte gezeigt werden, dass die Stärkefließmittel mit geringerem Molekulargewicht bei höheren Konzentrationen an den Hydratphasen des Zementes adsorbieren. Die Stärkefließmittel mit höherer Molekularmasse erreichen bei einer Zugabemenge von 0,7 % ein Plateau. Daraus wird geschlussfolgert, dass die größeren Fließmittelmoleküle einen erhöhten Platzbedarf erfordern und zur Absättigung der hydratisierenden Oberflächen bei geringeren Zugabemengen führen. Darüber hinaus konnte gezeigt werden, dass die Stärkefließmittel mit höherer anionischer Ladungsmenge zu höheren Adsorptionsmengen auf den Zement-, C3A- und C3S-Partikeln führen.
13. Die Adsorptionsprozesse finden an den ersten gebildeten Hydratphasen der C3A-Partikel statt, wodurch sowohl die Auflösung des C3A als auch die Bildung der Calciumhydroaluminate verlangsamt wird. Darüber hinaus wurde festgestellt, dass die Verlangsamung des freien- und diffusionskontrollierten Hydratphasenwachstums des C3S, durch die Adsorption der Stärkefließmittel auf den ersten gebildeten CSH-Phasen hervorgerufen wird. Des Weiteren wurde festgestellt, dass sehr kleine zuckerähnliche Moleküle in der kurzkettigen Maniokstärke in der Lage sind, die Bildung der ersten CSH-Keime zu unterdrücken. Dadurch kann die langanhaltende Plateauphase der elektrischen Leitfähigkeit der C3S-Hydratation erklärt werden.
Beurteilung der Porenstruktur- und Festigkeitsausbildung
Die Beurteilung der Qualität der Mikrostruktur erfolgte durch die Bestimmung der Rohdichte und der Porenradienverteilung mit Hilfe der Quecksilberhochdruckporosimetrie. Durch das Versetzen der Zementleime mit den Stärkefließmitteln konnten bei gleichbleibender Verarbeitbarkeit Zementsteinprobekörper mit einem um 17,5 % geringeren w/z-Wert von 0,35 hergestellt werden. Die Absenkung des w/z-Wertes führt zu einem Anstieg der Rohdichte des Zementsteins.
14. Durch die Zugabe der Stärkefließmittel und den verringerten w/z-Wert wird die Porenstruktur der Zementsteinproben im Vergleich zum Referenzzementstein verfeinert, da die Gesamtporosität sinkt. Insbesondere der Kapillarporenanteil wird verringert und der Gelporenanteil erhöht. Im Unterschied zu den PCE-Fließmitteln führt die Zugabe der Stärkefließmittel zu keinem erhöhten Eintrag von Luftporen. Dies wiederum hat zur Folge, dass bei der Verwendung der Stärkefließmittel auf Entschäumer verzichtet werden kann.
15. Entsprechend der dichteren Zementsteinmatrix wurden für die Zementsteine mit den Stärkefließmitteln nach 7 d und 28 d, erhöhte Biegezug- und Druckfestigkeiten ermittelt. Insbesondere die 28 d Druckfestigkeit wurde durch den verringerten w/z-Wert um die Faktoren 3,5 - 6,6 erhöht.
This article is focused on the research and development of new cellulose ether derivatives as innovative superplasticizers for mortar systems. Several synthetic strategies have been pursued to obtain new compounds to study their properties on cementitious systems as new bio-based additives. The new water-soluble admixtures were synthesized using a complex carboxymethylcellulose-based backbone that was first hydrolyzed and then sulfo-ethylated in the presence of sodium vinyl sulphonate. Starting with a complex biopolymer that is widely known as a thickening agent was very challenging. Only by varying the hydrolysis times and temperatures of the reactions was achieved the aimed goal. The obtained derivatives showed different molecular weight (Mw) and anionic charges on their backbones. An improvement in shear stress and dynamic viscosity values of CEM II 42.5R cement was observed with the samples obtained with a longer time of higher temperature hydrolysis and sulfo-ethylation. Investigations into the chemical nature of the pore solution, calorimetric studies and adsorption experiments clearly showed the ability of carboxymethyl cellulose superplasticizer (CMC SP) to interact with cement grains and influence hydration processes within a 48-h time window, causing a delay in hydration reactions in the samples. The fluidity of the cementitious matrices was ascertained through slump test and preliminary studies of mechanical and flexural strength of the hardened mortar formulated with the new ecological additives yielded values in terms of mechanical properties. Finally, the computed tomography (CT) images completed the investigation of the pore network structure of hardened specimens, highlighting their promising structure porosity.
The amount of adsorbed styrene acrylate copolymer (SA) particles on cementitious surfaces at the early stage of hydration was quantitatively determined using three different methodological approaches: the depletion method, the visible spectrophotometry (VIS) and the thermo-gravimetry coupled with mass spectrometry (TG–MS). Considering the advantages and disadvantages of each method, including the respectively required sample preparation, the results for four polymer-modified cement pastes, varying in polymer content and cement fineness, were evaluated.
To some extent, significant discrepancies in the adsorption degrees were observed. There is a tendency that significantly lower amounts of adsorbed polymers were identified using TG-MS compared to values determined with the depletion method. Spectrophotometrically generated values were lying in between these extremes. This tendency was found for three of the four cement pastes examined and is originated in sample preparation and methodical limitations.
The main influencing factor is the falsification of the polymer concentration in the liquid phase during centrifugation. Interactions in the interface between sediment and supernatant are the cause. The newly developed method, using TG–MS for the quantification of SA particles, proved to be suitable for dealing with these revealed issues. Here, instead of the fluid phase, the sediment is examined with regard to the polymer content, on which the influence of centrifugation is considerably lower.
Conventional superplasticizers based on polycarboxylate ether (PCE) show an intolerance to clay minerals due to intercalation of their polyethylene glycol (PEG) side chains into the interlayers of the clay mineral. An intolerance to very basic media is also known. This makes PCE an unsuitable choice as a superplasticizer for geopolymers. Bio-based superplasticizers derived from starch showed comparable effects to PCE in a cementitious system. The aim of the present study was to determine if starch superplasticizers (SSPs) could be a suitable additive for geopolymers by carrying out basic investigations with respect to slump, hardening, compressive and flexural strength, shrinkage, and porosity. Four SSPs were synthesized, differing in charge polarity and specific charge density. Two conventional PCE superplasticizers, differing in terms of molecular structure, were also included in this study. The results revealed that SSPs improved the slump of a metakaolin-based geopolymer (MK-geopolymer) mortar while the PCE investigated showed no improvement. The impact of superplasticizers on early hardening (up to 72 h) was negligible. Less linear shrinkage over the course of 56 days was seen for all samples in comparison with the reference. Compressive strengths of SSP specimens tested after 7 and 28 days of curing were comparable to the reference, while PCE led to a decline. The SSPs had a small impact on porosity with a shift to the formation of more gel pores while PCE caused an increase in porosity. Throughout this research, SSPs were identified as promising superplasticizers for MK-geopolymer mortar and concrete.
This paper reports the formation and structure of fast setting geopolymers activated by using three sodium silicate solutions with different modules (1.6, 2.0 and 2.4) and a berlinite-type aluminum orthophosphate. By varying the concentration of the aluminum orthophosphate, different Si/Al-ratios were established (6, 3 and 2). Reaction kinetics of binders were determined by isothermal calorimetric measurements at 20 °C. X-ray diffraction analysis as well as nuclear magnetic resonance (NMR) measurements were performed on binders to determine differences in structure by varying the alkalinity of the sodium silicate solutions and the Si/Al-ratio. The calorimetric results indicated that the higher the alkalinity of the sodium silicate solution, the higher the solubility and degree of conversion of the aluminum orthophosphate. The results of X-ray diffraction and Rietveldt analysis, as well as the NMR measurements, confirmed the assumption of the calorimetric experiments that first the aluminum orthophosphate was dissolved and then a polycondensation to an amorphous aluminosilicate network occurred. The different amounts of amorphous phases formed as a function of the alkalinity of the sodium silicate solution, indicate that tetrahydroxoaluminate species were formed during the dissolution of the aluminum orthophosphate, which reduce the pH value. This led to no further dissolution of the aluminum orthophosphate, which remained unreacted.
Die Gase Sauerstoff und Stickstoff werden für eine Vielzahl an technischen, industriellen, biologischen und medizinischen Einsatzzwecken benötigt. So liegen Anwendungsgebiete dieser Gase neben der klassischen metallverarbeitenden und der chemischen Industrie bei Sauerstoff vor allem in der Medizin, Verbrennungs- und Kläranlagenoptimierung sowie der Fischzucht und bei Stickstoff als Schutz- beziehungsweise Inertgas in der Kunststoffindustrie, der Luft- und Raumfahrt sowie dem Brandschutz.
Die Bereitstellung der Gase Sauerstoff und Stickstoff wird nahezu ausschließlich durch die Abtrennung aus der Umgebungsluft realisiert, welche aus ca. 78 Vol.-% Stickstoff, 21 Vol.-% Sauerstoff und 1 Vol.-% Spurengasen (Ar, CO2, Ne, He, ...) besteht. Am Markt etablierte Verfahren der Luftzerlegung sind das Linde-, das PSA- (pressure swing adsorption/Druckwechseladsorption) oder verschiedene Membran-Verfahren. Hierdurch werden die benötigten Gase entweder direkt vor Ort beim Verbraucher erzeugt (PSA- und Polymer-Membranverfahren: geringe Reinheiten) oder zentral in großen Anlagen hergestellt (Linde-Verfahren: hohe Reinheiten) und anschließend zum Verbraucher in Form von Flaschen- oder Tankgasen geliefert (Tansportkosten).
Für kleinere Verbraucher mit hohen Ansprüchen an die Reinheit des benötigten Sauerstoffs beziehungsweise Stickstoffs ergibt sich nur die Möglichkeit, die Gase als kostenintensive Transportgase zentraler Gaseversorger zu beziehen und sich somit in eine Abhängigkeit (Lieferverträge, Flaschen-/Tankmieten, ...) zu diesen zu begeben sowie eine eigene Lagerhaltung für die benötigten Gase (Mehraufwand, Lagerkosten, Platzbedarf) zu betreiben.
Ziel dieser Arbeit ist es, keramische Material-Systeme auf Basis chemischer Hochtemperatur-Reaktionen als Reaktive Oxidkeramiken zu entwickeln und diese hinsichtlich eines möglichen Einsatzes für die Sauerstoffseparation in neuartigen Luftzerlegungsanlagen zu untersuchen.
Derartige Anlagen sollen in ihrem Prinzip an die regenerative Sauerstoffseparation angelehnt sein und in ihren Reaktoren die Reaktiven Oxidkeramiken als Festbett-Material abwechselnd mit Luft be- und Vakuum oder O2-armen Atmosphären entladen.
Die Verwendung Reaktiver Oxidkeramiken, welche im Vergleich zu den bisherigen Materialien höhere Sauerstoffaustauschmengen und -raten bei gleichzeitig hoher Lebensdauer und Korrosionsbeständigkeit sowie relativ einfacher Handhabe aufweisen würden, soll ein Schritt in Richtung einer effizienten alternativen Luftzerlegungstechnologie sein.
Mit den Reaktiven Oxidkeramiken in einer Luftzerlegungsanlage sollte es im besten Fall möglich sein, in kleinen Anlagen sehr reinen Sauerstoff und zugleich sauerstofffreies Inertgas zu erzeugen sowie eine Sauerstoffan- oder -abreicherung von Luft, Prozess- oder Abgasen zu generieren.
Somit besäße eine solche, auf Reaktiven Oxidkeramiken basierende Technologie sehr weit gefächerte Einsatzgebiete und demzufolge ein enormes wirtschaftliches Potential.
Polymer-modified cement concrete (PCC) is a heterogeneous building material with a hierarchically organized microstructure. Therefore, continuum micromechanics-based multiscale models represent a promising method to estimate the mechanical properties. By means of a bottom-up approach, homogenized properties at the macroscopic scale are derived considering microstructural characteristics. The extension of existing multiscale models for the application to PCC is the main objective of this work. For that, cross-scale experimental studies are required. Both macroscopic and microscopic mechanical tests are performed to characterize the elastic and viscoelastic properties of different PCC. The comparison between experiment and model prediction illustrates the success of the modeling approach.
Ziel der Arbeit war das Adsorptionsverhalten ausgewählter schutzkolloidstabilisierter Polymerpartikel mit variierender chemischer Basis im zementären System zu beschreiben und basierend auf den gewonnenen Erkenntnissen das Konkurrenzverhalten beim Angebot unterschiedlicher mineralischer Oberflächen zu klären.
Sowohl die Destabilisierung der Polymerpartikel im alkalischen Milieu, welche eine Voraussetzung für derartige Adsorptionsprozesse ist, als auch die Veränderung von Oberflächeneigenschaften verschiedener mineralischer Partikel durch Hydratations- und Ionenadsorptionsprozesse, wurden u. a. mit Hilfe elektrokinetischer Experimente erfasst. Die spektralphotometrische Erstellung von Adsorptionsisothermen ermöglichte zudem die Ermittlung der jeweiligen adsorbierten Polymermenge zu verschiedenen Zeitpunkten der frühen Hydratation. Weiterhin wurde die Polymeradsorption an Partikeln ausgewählter Zusatzstoffe in Abhängigkeit von der Ionenstärke der Flüssigphase beschrieben.
Rasterelektronenmikroskopische Untersuchungen cryo-präparierter polymermodifizierter Zementleimproben ermöglichten es außerdem deren Mikrostruktur im suspensiven Zustand zu visualisieren. Diese Aufnahmen, ebenso wie die Ergebnisse grundlegender hydratationskinetischer Untersuchungen wurden in Wechselbeziehung zu den Ergebnissen der Adsorptionsuntersuchungen gebracht.
Maßgelbliche intermolekulare und interpartikuläre Wechselwirkungen, infolge derer sich die Stabilitätsverhältnisse im Zementleim ändern und die Polymerpartikel adsorbieren sind im Wesentlichen die Desorption des Schutzkolloids von der Polymerpartikeloberfläche, die Ionisation funktioneller Gruppen der Polymerpartikel und der Schutzkolloidmakromoleküle im alkalischen Milieu und infolgedessen die Komplexbildung mit Ionen der Zementleimporenlösung. Die Auswirkungen dieser Vorgänge auf die Lösungs- und Fällungskinetik des Zementleimes wurden erfasst und mit der chemischen Zusammensetzung der polymeren Systeme korreliert.
Durch Reifungs- und Strukturbildungsprozesse kann es bei silikatischen und alumosilikatischen Bindern zu Rissbildung bei behinderter Verformung, Festigkeitsverlust und somit Verlust der Dauerhaftigkeit kommen. Die Bewertung dieser Prozesse erfolgt an silikatischen Materialien mit einem Ausblick auf die alumosilikatischen Binder.
Durch Reifungs- und Strukturbildungsprozesse kann es bei silikatischen und alumosilikatischen Bindern zu Rissbildung bei behinderter Verformung, Festigkeitsverlust und somit Verlust der Dauerhaftigkeit kommen. Die Bewertung dieser Prozesse erfolgt an silikatischen Materialien mit einem Ausblick auf die alumosilikatischen Binder
Traditionally, buildings in the Inner Himalayan valleys of Bhutan were constructed from rammed earth in the western regions and quarry stone in the central and eastern regions. Whilst basic architectural design elements have been retained, the construction methods have however changed over recent decades alongside expectations for indoor thermal comfort. Nevertheless, despite the need for space heating, thermal building performance remains largely unknown. Furthermore, no dedicated climate data is available for building performance assessments. This paper establishes such climatological information for the capital Thimphu and presents an investigation of building physics properties of traditional and contemporary building types. In a one month field study 10 buildings were surveyed, looking at building air tightness, indoor climate, wall U-values and water absorption of typical wall construction materials. The findings highlight comparably high wall U-values of 1.0 to 1.5 W/m²K for both current and historic constructions. Furthermore, air tightness tests show that, due to poorly sealed joints between construction elements, windows and doors, many buildings have high infiltration rates, reaching up to 5 air changes per hour. However, the results also indicate an indoor climate moderating effect of more traditional earth construction techniques. Based on these survey findings basic improvements are being suggested.
Diese Arbeit belegt, dass die Belastungen auf reversibel arbeitende keramische Materialien sehr gering ausfallen. Die regenerative Sauerstoffbereitstellung stellt damit grundsätzlich niedrigere Anforderungen an die keramischen Perowskit-Materialien zur Sauerstofferzeugung als die Membrantechnologie.
Das Absinken der Diffusionskoeffizienten bei niedrigen Temperaturen ist deutlich weniger nachteilig als bei den Membranen die vergleichbare Materialien nutzen.
Dies konnte gezeigt werde, indem mit der die O 2 -Entladetechnik und -Beladetechnik im Vergleich zur O 2 -Abtrennung durch keramische Membranen bei vergleichsweise niedrigen Temperaturen bereits große O 2 -Mengen erzeugt werden können. Infolge der niedrigen Temperaturen bestehen keine Probleme mit Reaktionen zwischen dem sauerstoffbereitstellenden Material und den Reaktorwerkstoffen. Dadurch gestaltet sich die Einbindung und Nutzung von Festbett-Schüttungen denkbar einfach. Im Vergleich dazu sind die Anbindung und der Betrieb von dünnen keramischen Membranen in einem Reaktor deutlich aufwendiger. Es ist weniger Peripherie und verfahrenstechnischer Aufwand zur Sauerstoffabtrennung durch reversibel arbeitende Materialien nötig als bei der kryogenen Luftzerlegung, der Druckwechseladsorption oder den Membrantechnologien.
Die regenerative Sauerstoffbereitstellung kann sowohl bei neuen als auch bestehenden Anlagen, die Sauerstoff benötigen implementiert werden. Damit ist es möglich den Transport des Sauerstoffs entfallen zu lassen. Eine partielle Phasenumwandlung des BSCF8020 bei erhöhter Temperatur und hohem Sauerstoffangebot spielt für die regenerative Sauerstoffbereitstellung eine untergeordnete Rolle, da die nötigen Zieltemperaturen (450 ggf. bis 650 °C) zur O 2 -Beladung und -Entladung niedriger sind, als der Temperaturbereich in dem die Zersetzung auftreten kann (750 bis 800 °C). Des Weiteren ist die Zeitspanne (O 2 -Beladungsteilzyklus) in der das BSCF8020 ausreichend hohen Sauerstoffgehalten (p O2 > 10 -3 bar) ausgesetzt ist, zu kurz um diese Umwandlungen zu vollziehen. Der O 2 -Entladungsteilzyklus sorgt zusätzlich immer dafür, dass sich u. U. beginnende Zersetzung zurückbildet, da die kubische Phase in Richtung niedrigerer p O2 stabilisiert wird.
Es konnte belegt werden, dass die elektronische Steuerung des zyklischen Sauerstoffausbaus und -einbaus beherrschbar ist. Der hohe Abtrenngrad der keramischen Materialien führt dazu, dass der Sauerstoff elektrolytisch rein zu Verfügung gestellt wird. Grundsätzlich sind weitere Forschungen zur Steigerung der Sauerstoffmengen, die pro eingesetzter Masseeinheit an Keramik gewonnen werden können, immer anzustreben, da damit u. U. der Materialeinsatz weiter gesenkt oder auch die energetischen Aufwendungen weiter reduziert werden können. Bei dem, für die multizyklischen Untersuchungen dieser Arbeit ausgewählten BSCF8020(SVT) hat die Cobalt-Komponente mit ca. 80 % den überwiegenden Kostenanteil am Sauerstoff bereitstellenden Material. BSCF-Keramiken mit höherem Eisen-Anteil sollten für multizyklische Anwendungen in Festbett-Reaktoren einer vertiefenden Charakterisierung unterzogen werden, um weitere geeignete Perowskite mit niedrigen Materialkosten zu erschließen.
Zur Erstellung von dekorativen Plastiken sollten Mörtel entwickelt werden, die eine hohe Biegezugfestigkeit aufweisen und eine breite Palette von Konsistenzen für verschiedene Anwendungsarten, wie Gießen, Spachteln oder Stampfen abdecken. Als Basis für die Rezepturen wurde ein niedrigviskoses Epoxidharzsystem gewählt, dessen Aminhärter einen Wasseranteil von 44 % beinhaltet. Dies ermöglichte es, durch Wasserzugabe verschiedene Viskositäten einzustellen. Um dieses Wasser in massiveren Bauteilen zu binden, wurde neben Sand auch Zement als Füllstoff eingesetzt.
Die erstellten Rezepturen zeigten nach 56 Tagen hohe Druckfestigkeiten von über 50 N/mm². Mit zunehmendem Epoxidharzgehalt ergaben sich zwar steigende Biegezugfestigkeiten, jedoch unter Laborlagerung auch größere Längenänderungen. Diese konnten durch den Einsatz eines PCE-Fließmittels, PVA-Kurzfasern und einer optimierten Sieblinie verringert werden. Das Fließmittel verlängerte die Erhärtungszeiten jedoch auf bis zu 1,5 Tage.
Zur Ermittlung der Dauerhaftigkeit des Materials wurde es für drei Wochen Temperaturen von -20 bis +60 °C, einer künstlichen Sonnenbestrahlung sowie künstlicher Beregnung ausgesetzt. Im Vergleich zur Laborlagerung ergab sich bei steigendem Epoxidharzanteil ein geringerer Schwund, während die Biegezugfestigkeit der Probeköper nur geringfügig abnahm.
Rasterelektronenmikroskopische Untersuchungen zeigten, dass auch bei geringeren Epoxidharzzusätzen Störungen der Zementhydratation auftraten. Weiterhin zeigen sich bei geringen Epoxidharzzusätzen in der Matrix kugelförmige Einschlüsse, die von dispergierten Epoxidharzpartikeln stammen.
The mechanism and the kinetics of hydration reactions are important for the application of a salt hydrate as a thermochemical heat storage material. MgSO4·H2O and Na2SO4 were chosen in this study because they are both promising candidates for such an application. Considering that the hydration of these salts yields MgSO4·7H2O and Na2SO4·10H2O as the reaction products, the maximum overall heat effect can be calculated from the heat of condensation of water vapor (44 kJ mol–1) and the heats of hydration of 75 kJ·mol-1 (for MgSO4·H2O) and 81 kJ mol-1 (for Na2SO4). Based on the densities of the two hydrated phases, this results in the very high theoretical energy densities of 2.3 GJ·m-3 and 2.4 GJ·m-3, respectively, for MgSO4·7H2O and Na2SO4·10H2O. Not only the energy density is important for the dimensioning of a storage system, but also the kinetics of hydration reactions play a major role for the application as storage material. In the present study, hydration reactions under varying climatic conditions were investigated by using water vapor sorption measurements and in-situ Raman microscopy. Using the phase diagrams, it can be clearly shown that the mechanism and the kinetics depend on the climatic conditions. Below the deliquescence humidity of the lower hydrated phase the hydration proceeds as solid state reaction, whilst above the deliquescence humidity a through solution mechanism takes place.
Strain measurement is important in mechanical testing. A wide variety of techniques exists for measuring strain in the tensile test; namely the strain gauge, extensometer, stress and strain determined by machine crosshead motion, Geometric Moire technique, optical strain measurement techniques and others. Each technique has its own advantages and disadvantages. The purpose of this study is to quantitatively compare the strain measurement techniques. To carry out the tensile test experiments for S 235, sixty samples were cut from the web of the I-profile in longitudinal and transverse directions in four different dimensions. The geometry of samples are analysed by 3D scanner and vernier caliper. In addition, the strain values were determined by using strain gauge, extensometer and machine crosshead motion. Three techniques of strain measurement are compared in quantitative manner based on the calculation of mechanical properties (modulus of elasticity, yield strength, tensile strength, percentage elongation at maximum force) of structural steel. A statistical information was used for evaluating the results. It is seen that the extensometer and strain gauge provided reliable data, however the extensometer offers several advantages over the strain gauge and crosshead motion for testing structural steel in tension. Furthermore, estimation of measurement uncertainty is presented for the basic material parameters extracted through strain measurement.
Bentonite sind quellfähige Tone, die häufig in der Umwelttechnik (in Abdichtungsbauwerken oder in der Bodensanierung) eingesetzt werden. Ziel der Arbeit war die Klärung, wie eine unterschiedliche Kationenbelegung mit Cu2+ und NH4+ die Eigenschaften der Bentonite bei Raumtemperatur und nach moderater Wärmebehandlung (300 – 450°C) beeinflusst. Im Blickpunkt stand insbesondere die gleichzeitige Präsenz von Kupfer- und Ammoniumionen, die als Vertreter für häufig auftretende Inhaltsstoffe von Wässern in der Umgebung von technischen Bentoniten ausgewählt wurden.
Die Untersuchungen zur Cu2+-Sorption bei Raumtemperatur und nach moderater Wärmebehandlung (300 – 450°C) erfolgten an Pulverproben von zwei technischen Bentoniten, die sich in der ursprünglichen Kationenbelegung, Art und Anteil an Nebengemengteilen, sowie der Schichtladungsverteilung in den Montmorilloniten unterscheiden. Vor der Wärmebehandlung wurden die Bentonite durch Kontakt mit verschieden konzentrierten Kupfer- und Ammoniumlösungen mit unterschiedlichen Gehalten der Kationen Cu2+, NH4+, Na+, Ca2+, Mg2+ belegt.
Der Eintrag von Kupferionen in die Bentonite durch Kationenaustausch bei Raumtemperatur wurde erwartungsgemäß durch präsente Nebengemengteile (wie Carbonat) beeinflusst, so dass die Kupferionen zusätzlich spezifisch adsorbiert und in festen Phasen angereichert wurden.
Die Cu2+-Fixierung infolge der Wärmebehandlung wurde vom Cu2+-Totalgehalt in den Bentoniten, der Präsenz von Nebengemengteilen und die Schichtladungsverteilung in den Montmorilloniten beeinflusst. Es waren generell Behandlungstemperaturen von > 400°C erforderlich, um Cu2+-Fixierungsraten von > 95% zu erzielen.
Waren während der Wärmebehandlung neben Cu2+-Ionen gleichzeitig NH4+-Ionen in den Bentoniten präsent, konnte die Cu2+-Fixierungstemperatur herabgesetzt werden. Die Deammonisierung (NH4+ --> NH3 + H+) der NH4+-belegten Bentonite fand größtenteils unterhalb der Dehydroxylierungstemperatur der Bentonite statt.
Durch Untersuchungen (XRD, FTIR, NMR, ESR) zum Mechanismus der Cu2+-Einbindung in die Bentonite an speziell aufbereiteten Proben (carbonatfrei, < 2 µm) konnte nachgewiesen werden, dass in den Cu2+-belegten Montmorilloniten die Cu2+-Ionen infolge der Wärmebehandlung nicht bis in die Oktaederschicht der Tonminerale vordringen, sondern nur bis in die Tetraederschicht wandern. In den NH4+-belegten Montmorilloniten treten im Zusammenhang mit der Deammonisierung keine zusätzlichen Strukturänderungen (wie Auflösung der Oktaederschicht) infolge der Wärmebehandlung auf.
Die thermochemische Wärmespeicherung über reversible Salzhydratation stellt einen aussichtsreichen Weg zur Speicherung von Niedertemperaturwärme, wie z.B. solarer Energie, dar.
Untersuchungen an Magnesiumsulfat-Hydraten zeigen, dass das bei 130°C entwässerte Magnesiumsulfat-Heptahydrat seinen thermodynamisch stabilen Endzustand während der Reaktion mit gasförmigem Wasser nicht wieder erreicht. Um diese kinetische Hemmung zu überwinden und den Einfluss von unterschiedlichen Porenräumen auf die Hydratation bzw. Sorption des Magnesiumsulfates zu charakterisieren, wurde das Magnesiumsulfat in Trägermaterialien auf Basis offenporiger Gläser mit durchschnittlichen Porendurchmessern von 4 nm bis 1,4 µm eingebracht und diese Kompositmaterialien untersucht. Dabei ist festgestellt worden, dass jede salzbezogene Sorptionswärme im Porenraum höher ist, als die des ungeträgerten Salzes und mit kleiner werdendem Porenradius weiter zunimmt.
Weiterhin wurden Teile des Magnesiumsulfates mit niedrig deliqueszierenden Salzen substituiert, um die Wasseraufnahme und somit die Wärmespeicherkapazität zu erhöhen. Dies stellt einen neuen Weg zur Herstellung von Kompositmaterialien dar, über den man Eigenschaften wie Deliqueszenzfeuchte und Desorptionstemperatur einstellen und an die Sorptionsbedingungen eines Speichers anpassen kann. Als niedrig deliqueszierende Salze wurden Magnesiumchlorid und Lithiumchlorid
als Zusätze untersucht, wobei ein Ansteigen der Sorptionswärme und Wasseraufnahme mit steigendem Chloridanteil festgestellt wurde. Aufgrund der geringeren Deliqueszenzfeuchte des Lithiumchlorides gegenüber dem Magnesiumchlorid wurden bei gleichen Massenverhältnissen höhere Sorptionswärmen erzielt. Untersuchungen zu Zinksulfat in Verbindung mit Chloriden bescheinigen diesem Salz -speziell bei tieferen Entwässerungstemperaturen- eine gute Eignung als Aktivstoff zur Wärmespeicherung.
Zusammenfassend konnte festgestellt werden, dass sich die Wärmespeicherkapazitäten über die Porengröße, in die das Salz eingebracht wird, und die gewählte Mischungszusammensetzung steuern lassen. Die gemessenen Sorptionswärmen ermöglichen insbesondere bei niedrigen Sorptionstemperaturen und hohen Luftfeuchtigkeiten den Schluss, dass die Verwendung von Salzmischungen als Aktivkomponente in Kompositmaterialien einen geeigneten Weg zur thermochemischen Speicherung solarer Wärme (≤130 °C) darstellt.