TY - THES A1 - Buchwald, Anja T1 - Der Einfluss des Kalziums auf die Kondensation von (Alumo-)Silikaten in alkali-aktivierten Bindern N2 - Es werden geopolymere und alkali-aktivierte Bindemittel definiert und ihre prinzipiellen technischen und ökologischen Eigenschaften diskutiert. KW - Bindemittel KW - Geopolymer Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20140124-21046 ER - TY - JOUR A1 - Cappachione, Clotilde A1 - Partschefeld, Stephan A1 - Osburg, Andrea A1 - Gliubizzi, Rocco A1 - Gaeta, Carmine T1 - Modified Carboxymethylcellulose-Based Scaffolds as New Potential Ecofriendly Superplasticizers with a Retardant Effect for Mortar: From the Synthesis to the Application JF - Materials N2 - This article is focused on the research and development of new cellulose ether derivatives as innovative superplasticizers for mortar systems. Several synthetic strategies have been pursued to obtain new compounds to study their properties on cementitious systems as new bio-based additives. The new water-soluble admixtures were synthesized using a complex carboxymethylcellulose-based backbone that was first hydrolyzed and then sulfo-ethylated in the presence of sodium vinyl sulphonate. Starting with a complex biopolymer that is widely known as a thickening agent was very challenging. Only by varying the hydrolysis times and temperatures of the reactions was achieved the aimed goal. The obtained derivatives showed different molecular weight (Mw) and anionic charges on their backbones. An improvement in shear stress and dynamic viscosity values of CEM II 42.5R cement was observed with the samples obtained with a longer time of higher temperature hydrolysis and sulfo-ethylation. Investigations into the chemical nature of the pore solution, calorimetric studies and adsorption experiments clearly showed the ability of carboxymethyl cellulose superplasticizer (CMC SP) to interact with cement grains and influence hydration processes within a 48-h time window, causing a delay in hydration reactions in the samples. The fluidity of the cementitious matrices was ascertained through slump test and preliminary studies of mechanical and flexural strength of the hardened mortar formulated with the new ecological additives yielded values in terms of mechanical properties. Finally, the computed tomography (CT) images completed the investigation of the pore network structure of hardened specimens, highlighting their promising structure porosity. KW - Mörtel KW - Verflüssigung KW - superplasticizers KW - carboxymethylcellulose KW - mortar KW - OA-Publikationsfonds2021 Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20210804-44689 UR - https://www.mdpi.com/1996-1944/14/13/3569 VL - 2021 IS - volume 14, issue 13, article 3569 SP - 1 EP - 17 PB - MDPI CY - Basel ER - TY - THES A1 - Göbel, Luise T1 - Experimental and semi-analytical multiscale approaches for the characterization of the elastic and viscoelastic behavior of polymer-modified cement-based materials T1 - Experimentelle und semi-analytische Multiskalenmethoden für die Charakterisierung des elastischen und viskoelastischen Verhaltens polymermodifizierter zementgebundener Materialien N2 - Polymer-modified cement concrete (PCC) is a heterogeneous building material with a hierarchically organized microstructure. Therefore, continuum micromechanics-based multiscale models represent a promising method to estimate the mechanical properties. By means of a bottom-up approach, homogenized properties at the macroscopic scale are derived considering microstructural characteristics. The extension of existing multiscale models for the application to PCC is the main objective of this work. For that, cross-scale experimental studies are required. Both macroscopic and microscopic mechanical tests are performed to characterize the elastic and viscoelastic properties of different PCC. The comparison between experiment and model prediction illustrates the success of the modeling approach. N2 - Polymermodifizierter Beton (PCC) ist ein heterogener Baustoff mit einer hierarchisch organisierten Mikrostruktur. Deshalb sind Multiskalenmodelle, die auf Prinzipien der Kontinuumsmikromechanik beruhen, sehr gut für die Abschätzung mechanischer Eigenschaften geeignet. Mit Hilfe eines Bottom-Up-Ansatzes werden unter Berücksichtigung mikrostruktureller Charakteristika homogenisierte Eigenschaften auf der makroskopischen Materialebene erhalten. Die Erweiterung bestehender Multiskalenmodelle für die Anwendung auf PCC ist das Hauptziel dieser Arbeit. Dafür werden skalenübergreifende Experimente herangezogen. Sowohl makroskopische als auch mikroskopische mechanische Tests werden durchgeführt, um das elastische und viskoelastische Verhalten verschiedener PCC zu charakterisieren. Ein Vergleich zwischen experimentellen Ergebnissen und der entsprechenden Modellvorhersage verdeutlicht den Erfolg des Modellierungsansatzes. T3 - Schriftenreihe des DFG Graduiertenkollegs 1462 Modellqualitäten // Graduiertenkolleg Modellqualitäten - 19 KW - Elastizitätsmodul KW - Zementstein KW - Kunststoffadditiv KW - Modellierung KW - Mehrphasensystem KW - Multiskalenmodellierung KW - Multiscale modeling KW - Mikrostruktur KW - Polymermodifizierung KW - Kriechen KW - Elastizitätsmodul KW - Microstructure KW - Polymer modification KW - Creep KW - Young's modulus Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20181211-38279 SN - 978-3-95773-269-9 PB - Bauhaus-Universitätsverlag CY - Weimar ER - TY - THES A1 - Heidenreich, Manuel T1 - Untersuchungen zur Sauerstoffbereitstellung mit Perowskit- Keramik-Schüttungen in einem Festbett-Reaktor N2 - Diese Arbeit belegt, dass die Belastungen auf reversibel arbeitende keramische Materialien sehr gering ausfallen. Die regenerative Sauerstoffbereitstellung stellt damit grundsätzlich niedrigere Anforderungen an die keramischen Perowskit-Materialien zur Sauerstofferzeugung als die Membrantechnologie. Das Absinken der Diffusionskoeffizienten bei niedrigen Temperaturen ist deutlich weniger nachteilig als bei den Membranen die vergleichbare Materialien nutzen. Dies konnte gezeigt werde, indem mit der die O 2 -Entladetechnik und -Beladetechnik im Vergleich zur O 2 -Abtrennung durch keramische Membranen bei vergleichsweise niedrigen Temperaturen bereits große O 2 -Mengen erzeugt werden können. Infolge der niedrigen Temperaturen bestehen keine Probleme mit Reaktionen zwischen dem sauerstoffbereitstellenden Material und den Reaktorwerkstoffen. Dadurch gestaltet sich die Einbindung und Nutzung von Festbett-Schüttungen denkbar einfach. Im Vergleich dazu sind die Anbindung und der Betrieb von dünnen keramischen Membranen in einem Reaktor deutlich aufwendiger. Es ist weniger Peripherie und verfahrenstechnischer Aufwand zur Sauerstoffabtrennung durch reversibel arbeitende Materialien nötig als bei der kryogenen Luftzerlegung, der Druckwechseladsorption oder den Membrantechnologien. Die regenerative Sauerstoffbereitstellung kann sowohl bei neuen als auch bestehenden Anlagen, die Sauerstoff benötigen implementiert werden. Damit ist es möglich den Transport des Sauerstoffs entfallen zu lassen. Eine partielle Phasenumwandlung des BSCF8020 bei erhöhter Temperatur und hohem Sauerstoffangebot spielt für die regenerative Sauerstoffbereitstellung eine untergeordnete Rolle, da die nötigen Zieltemperaturen (450 ggf. bis 650 °C) zur O 2 -Beladung und -Entladung niedriger sind, als der Temperaturbereich in dem die Zersetzung auftreten kann (750 bis 800 °C). Des Weiteren ist die Zeitspanne (O 2 -Beladungsteilzyklus) in der das BSCF8020 ausreichend hohen Sauerstoffgehalten (p O2 > 10 -3 bar) ausgesetzt ist, zu kurz um diese Umwandlungen zu vollziehen. Der O 2 -Entladungsteilzyklus sorgt zusätzlich immer dafür, dass sich u. U. beginnende Zersetzung zurückbildet, da die kubische Phase in Richtung niedrigerer p O2 stabilisiert wird. Es konnte belegt werden, dass die elektronische Steuerung des zyklischen Sauerstoffausbaus und -einbaus beherrschbar ist. Der hohe Abtrenngrad der keramischen Materialien führt dazu, dass der Sauerstoff elektrolytisch rein zu Verfügung gestellt wird. Grundsätzlich sind weitere Forschungen zur Steigerung der Sauerstoffmengen, die pro eingesetzter Masseeinheit an Keramik gewonnen werden können, immer anzustreben, da damit u. U. der Materialeinsatz weiter gesenkt oder auch die energetischen Aufwendungen weiter reduziert werden können. Bei dem, für die multizyklischen Untersuchungen dieser Arbeit ausgewählten BSCF8020(SVT) hat die Cobalt-Komponente mit ca. 80 % den überwiegenden Kostenanteil am Sauerstoff bereitstellenden Material. BSCF-Keramiken mit höherem Eisen-Anteil sollten für multizyklische Anwendungen in Festbett-Reaktoren einer vertiefenden Charakterisierung unterzogen werden, um weitere geeignete Perowskite mit niedrigen Materialkosten zu erschließen. KW - Perowskit KW - Sauerstoff KW - Keramik KW - Festbett KW - Schüttung KW - BSCF KW - LSCF KW - SrMnO3 KW - CSMF KW - Dynamische Messungen Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20171027-36077 ER - TY - JOUR A1 - Jentsch, Mark F. A1 - Kulle, Christoph A1 - Bode, Tobias A1 - Pauer, Toni A1 - Osburg, Andrea A1 - Namgyel, Karma A1 - Euthra, Karma A1 - Dukjey, Jamyang A1 - Tenzin, Karma T1 - Field study of the building physics properties of common building types in the Inner Himalayan valleys of Bhutan JF - Energy for Sustainable Development 38 N2 - Traditionally, buildings in the Inner Himalayan valleys of Bhutan were constructed from rammed earth in the western regions and quarry stone in the central and eastern regions. Whilst basic architectural design elements have been retained, the construction methods have however changed over recent decades alongside expectations for indoor thermal comfort. Nevertheless, despite the need for space heating, thermal building performance remains largely unknown. Furthermore, no dedicated climate data is available for building performance assessments. This paper establishes such climatological information for the capital Thimphu and presents an investigation of building physics properties of traditional and contemporary building types. In a one month field study 10 buildings were surveyed, looking at building air tightness, indoor climate, wall U-values and water absorption of typical wall construction materials. The findings highlight comparably high wall U-values of 1.0 to 1.5 W/m²K for both current and historic constructions. Furthermore, air tightness tests show that, due to poorly sealed joints between construction elements, windows and doors, many buildings have high infiltration rates, reaching up to 5 air changes per hour. However, the results also indicate an indoor climate moderating effect of more traditional earth construction techniques. Based on these survey findings basic improvements are being suggested. KW - Luftdichtheit KW - Wärmedurchgangszahl KW - Raumklima KW - Monitoring KW - Himalaja KW - Building monitoring KW - Air tightness KW - U-value KW - Indoor climate KW - Himalaya Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20170419-31393 UR - http://dx.doi.org/10.1016/j.esd.2017.03.001 SP - 48 EP - 66 ER - TY - THES A1 - Kirsten, Heike T1 - Herkunft, Eigenschaften und Konservierungsmöglichkeiten von Lettenkeuper- und Schilfsandsteinen an Baudenkmalen in Thüringen T1 - Occurrences, parameters and damage appearances of the Lower and Middle Keuper sandstones on historic buildings in Thuringia N2 - Lettenkeuper- und Schilfsandsteine sind in Thüringen weit verbreitet und wurden häufig als Werk- und Bildhauersandsteine verwendet. Die überwiegend tonig-ferritisch gebundenen Steine sind stark witterungsanfällig. Inzwischen droht ein unwiederbringlicher Substanzverlust an vielen denkmalpflegerisch wertvollen Gebäuden und an plastischen Bildwerken. Die Dissertation gibt einen Überblick über die Vorkommen, Eigenschaften und Schadbilder dieser Sandsteine in Thüringen. Konservierungsmaßnahmen, die in Thüringen in den vergangenen 20 Jahren an Lettenkeuper- und Schilfsandsteinen vorgenommen wurden, werden ausgewertet und neue Erkenntnisse zur Konservierung dieser Sandsteine vorgestellt. N2 - Sandstones of the Lower and Middle Keuper are widely spread in Thuringia. They were often used as building stones or as material for exposed masonry as well as for sculptures. Lower and Middle Keuper sandstones contain a high percentage of cements and are therefore very susceptible to weathering damages. Many valuable historic buildings and plastics are facing an irrecoverable stone erosion. This thesis provides an overview of the occurrences, the parameters and damage appearances of the Lower and Middle Keuper sandstone in Thuringia. Previous conservation strategies will be described and their results analysed. KW - Konservierung KW - Restaurierung KW - Denkmalpflege KW - Naturstein KW - Baustein KW - Steinkonservierung KW - Steinfestigung KW - Lettenkeupersandstein KW - Schilfsandstein KW - natural building stone KW - stone decay KW - stone consolidation KW - Lower Keuper Sandstone KW - Middle Keuper Sandstone Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20091116-14900 ER - TY - CHAP A1 - Kleiner, Florian A1 - Wiegand, Torben A1 - Osburg, Andrea T1 - Eigenschaftsentwicklung epoxidharzmodifizierter Mörtel auf Zementbasis bei unterschiedlichen klimatischen Bedingungen T2 - Tagung Bauchemie der GDCh-Fachgruppe Bauchemie, 18.-20. September 2017 in Weimar N2 - Zur Erstellung von dekorativen Plastiken sollten Mörtel entwickelt werden, die eine hohe Biegezugfestigkeit aufweisen und eine breite Palette von Konsistenzen für verschiedene Anwendungsarten, wie Gießen, Spachteln oder Stampfen abdecken. Als Basis für die Rezepturen wurde ein niedrigviskoses Epoxidharzsystem gewählt, dessen Aminhärter einen Wasseranteil von 44 % beinhaltet. Dies ermöglichte es, durch Wasserzugabe verschiedene Viskositäten einzustellen. Um dieses Wasser in massiveren Bauteilen zu binden, wurde neben Sand auch Zement als Füllstoff eingesetzt. Die erstellten Rezepturen zeigten nach 56 Tagen hohe Druckfestigkeiten von über 50 N/mm². Mit zunehmendem Epoxidharzgehalt ergaben sich zwar steigende Biegezugfestigkeiten, jedoch unter Laborlagerung auch größere Längenänderungen. Diese konnten durch den Einsatz eines PCE-Fließmittels, PVA-Kurzfasern und einer optimierten Sieblinie verringert werden. Das Fließmittel verlängerte die Erhärtungszeiten jedoch auf bis zu 1,5 Tage. Zur Ermittlung der Dauerhaftigkeit des Materials wurde es für drei Wochen Temperaturen von -20 bis +60 °C, einer künstlichen Sonnenbestrahlung sowie künstlicher Beregnung ausgesetzt. Im Vergleich zur Laborlagerung ergab sich bei steigendem Epoxidharzanteil ein geringerer Schwund, während die Biegezugfestigkeit der Probeköper nur geringfügig abnahm. Rasterelektronenmikroskopische Untersuchungen zeigten, dass auch bei geringeren Epoxidharzzusätzen Störungen der Zementhydratation auftraten. Weiterhin zeigen sich bei geringen Epoxidharzzusätzen in der Matrix kugelförmige Einschlüsse, die von dispergierten Epoxidharzpartikeln stammen. KW - Bauchemie KW - Mörtel KW - Epoxidharz KW - Dauerhaftigkeit Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20211004-45067 SN - 978-3-947197-02-6 PB - Gesellschaft Deutscher Chemiker ER - TY - JOUR A1 - Linnow, Kirsten A1 - Niermann, Michael A1 - Bonatz, Dennis A1 - Posern, Konrad A1 - Steiger, Michael T1 - Experimental Studies of the Mechanism and Kinetics of Hydration Reactions JF - Energy Procedia N2 - The mechanism and the kinetics of hydration reactions are important for the application of a salt hydrate as a thermochemical heat storage material. MgSO4·H2O and Na2SO4 were chosen in this study because they are both promising candidates for such an application. Considering that the hydration of these salts yields MgSO4·7H2O and Na2SO4·10H2O as the reaction products, the maximum overall heat effect can be calculated from the heat of condensation of water vapor (44 kJ mol–1) and the heats of hydration of 75 kJ·mol-1 (for MgSO4·H2O) and 81 kJ mol-1 (for Na2SO4). Based on the densities of the two hydrated phases, this results in the very high theoretical energy densities of 2.3 GJ·m-3 and 2.4 GJ·m-3, respectively, for MgSO4·7H2O and Na2SO4·10H2O. Not only the energy density is important for the dimensioning of a storage system, but also the kinetics of hydration reactions play a major role for the application as storage material. In the present study, hydration reactions under varying climatic conditions were investigated by using water vapor sorption measurements and in-situ Raman microscopy. Using the phase diagrams, it can be clearly shown that the mechanism and the kinetics depend on the climatic conditions. Below the deliquescence humidity of the lower hydrated phase the hydration proceeds as solid state reaction, whilst above the deliquescence humidity a through solution mechanism takes place. KW - Wärmespeicherung KW - Hydratation KW - Magnesiumsulfat KW - Natriumsulfat KW - hermochemical heat storage, hydration mechanism, magnesium sulfate; sodium sulfate Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20170425-31484 SP - 394 EP - 404 ER - TY - JOUR A1 - Motra, Hem Bahadur A1 - Hildebrand, Jörg A1 - Dimmig-Osburg, Andrea T1 - Assessment of strain measurement techniques to characterise mechanical properties of structural steel JF - Engineering Science and Technology, an International Journal N2 - Strain measurement is important in mechanical testing. A wide variety of techniques exists for measuring strain in the tensile test; namely the strain gauge, extensometer, stress and strain determined by machine crosshead motion, Geometric Moire technique, optical strain measurement techniques and others. Each technique has its own advantages and disadvantages. The purpose of this study is to quantitatively compare the strain measurement techniques. To carry out the tensile test experiments for S 235, sixty samples were cut from the web of the I-profile in longitudinal and transverse directions in four different dimensions. The geometry of samples are analysed by 3D scanner and vernier caliper. In addition, the strain values were determined by using strain gauge, extensometer and machine crosshead motion. Three techniques of strain measurement are compared in quantitative manner based on the calculation of mechanical properties (modulus of elasticity, yield strength, tensile strength, percentage elongation at maximum force) of structural steel. A statistical information was used for evaluating the results. It is seen that the extensometer and strain gauge provided reliable data, however the extensometer offers several advantages over the strain gauge and crosshead motion for testing structural steel in tension. Furthermore, estimation of measurement uncertainty is presented for the basic material parameters extracted through strain measurement. KW - Baustahl KW - Werkstoffprüfung KW - Zugversuch KW - Affecting factors; Measurement uncertainty; Materials testing; Quantitative comparison; Strain comparison; Tensile test Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20170425-31540 SP - 260 EP - 269 ER - TY - THES A1 - Partschefeld, Stephan T1 - Synthese von Fließmitteln aus Stärke und Untersuchung der Wechselwirkung mit Portlandzement N2 - Das Ziel dieser Arbeit war es, neuartige Fließmittel auf Basis von Stärke als nachwachsenden Rohstoff zu synthetisieren und die Wechselwirkung mit Portlandzement zu charakterisieren. Die Notwendigkeit, Alternativen zu synthetischen Zusatzmittel zu erforschen, ergibt sich aus der benötigten Menge zur Verarbeitung von ca. 4,1 Gt/a, wobei ca. 85 % der Zusatzmittel auf die Fließmittel entfallen. Um Fließmittel aus Stärke zu synthetisieren, wurden drei Basisstärken unterschiedlicher Herkunft verwendet. Es wurde eine Maniokstärke mit einer niedrigen Molekularmasse und eine Weizenstärke mit einer hohen Molekularmasse verwendet. Darüber hinaus wurde eine Kartoffelstärke mit einer mittleren Molekularmasse, die ein Abfallprodukt der kartoffelverarbeitenden Industrie darstellt, genutzt. Die Stärkefließmittel wurden durch chemische Modifikation in einem zweistufigen Prozess synthetisiert. Im ersten Schritt wurde das Molekulargewicht der Weizen- und Kartoffelstärke durch säurehydrolytischen Abbau verringert. Für die kurzkettige Maniokstärke war eine Degradation der Molekularmasse nicht notwendig. Im zweiten Syntheseschritt wurden anionische Ladungen durch das Versetzen der degradierten Stärken und Maniokstärke mit Natriumvinylsulfonat in die Stärkemoleküle eingeführt. Beurteilung der Synthesemethode zur Erzeugung von Stärkefließmitteln In diesem Zusammenhang sollten molekulare Parameter der Stärkefließmittel gezielt eingestellt werden, um eine Fließwirkung im Portlandzement zu erhalten. Insbesondere die Molekularmasse und die Menge anionischer Ladungen sollte variiert werden, um Abhängigkeiten mit der Dispergierleistung zu identifizieren. 1. Es konnte durch GPC-Messungen gezeigt werden, dass die Molekularmasse der langkettigen Weizenstärke durch die gewählten Modifizierungsbedingungen zum säurehydrolytischen Abbau verringert werden konnte. Durch Variation der säurehydrolytischen Bedingungen wurden 4 degradierte Weizenstärken erzeugt, die eine Reduzierung der Molekularmasse um 27,5 – 43 % aufwiesen. Die Molekularmasse der Kartoffelstärke konnte durch säurehydrolytischen Abbau um ca. 26 % verringert werden. 2. Durch PCD-Messungen wurde gezeigt, dass anionische Ladungen durch Sulfoethylierung der freien Hydroxylgruppen in die degradierten Stärken eingeführt werden konnten. Durch Variation der Dauer der Sulfoethylierung konnte die Menge der anionischen Ladungen gesteuert und gezielt variiert werden, so dass Stärkefließmittel mit steigender Ladungsmenge in folgender Reihenfolge synthetisiert wurden: W-3 < W-2 < K-1 < W¬-4 < W¬1 < M-1 Im Ergebnis der chemischen Modifizierung konnten 6 Stärkefließmittel mit variierten Molekularmassen und anionischen Ladungen erzeugt werden. Es konnte gezeigt werden, dass die Herkunft der Stärke für die chemische Modifizierung unerheblich ist. Die Fließmittel lagen synthesebedingt als basische, wässrige Suspensionen mit Wirkstoffgehalten im Bereich von 23,5 – 50 % vor. Beurteilung der Dispergierleistung der synthetisierten Stärkefließmittel Die Dispergierperformance wurde durch rheologische Experimente mit einem Rotationsviskosimeter erfasst. Dabei wurden der Einfluss auf die Fließkurven und die Viskositätskurven betrachtet. Durch Vergleich der Dispergierleistung mit einem Polykondensat- und einem PCE-Fließmittel konnte eine Einordnung und Bewertung der Fließmittel vorgenommen werden. 3. Die rheologische Experimente haben gezeigt, dass die Stärkefließmittel eine vergleichbar hohe Dispergierleistung aufweisen, wie das zum Vergleich herangezogen PCE-Fließmittel. Darüber hinaus zeigte sich, dass die Fließwirkung der 6 Stärkefließmittel gegenüber dem Polykondensatfließmittel deutlich höher ist. Das aus der Literatur bekannte Einbrechen der Dispergierleistung der Polykondensat-fließmittel bei w/z-Werten < 0,4 konnte bestätigt werden. 4. Alle 6 Stärkefließmittel führten zu einer Verringerung der Fließgrenze und der dynamischen Viskosität des Zementleimes bei einem w/z-Wert von 0,35. 5. Der Vergleich der Dispergierleistung der Stärkefließmittel untereinander zeigte, dass die anionische Ladungsmenge einen Schlüsselparameter darstellt. Die Stärkefließmittel M-1, K-1, W-1 und W-4 mit anionischen Ladungsmengen > 6 C/g zeigten die höchste Dispergier¬performance. Die vergleichend herangezogenen klassischen Fließmittel wiesen anionische Ladungsmengen im Bereich von 1,2 C/g (Polycondensat) und 1,6 C/g (PCE) auf. Die Molekularmasse schien für die Dispergierleistung zunächst unerheblich zu sein. Aus diesem Grund wurde die Basisweizenstärke erneut chemisch modifiziert, indem anionische Ladungen eingeführt wurden, ohne die Molekularmasse jedoch zu verringern. Das Stärkederivat wies verdickende Eigenschaften im Zementleim auf. Daraus konnte geschlussfolgert werden, dass eine definierte Grenzmolekularmasse (150.000 Da) existiert, die unterschritten werden muss, um Fließmittel aus Stärke zu erzeugen. Des Weiteren zeigen die Ergebnisse, dass durch die chemische Modifizierung sowohl Fließmittel als auch Verdicker aus Stärke erzeugt werden können. Beurteilung der Beeinflussung der Hydratation und der Porenlösung des Portlandzementes Aus der Literatur ist bekannt, dass Fließmittel die Hydratation von Portlandzement maßgeblich beeinflussen können. Aus diesem Grund wurden kalorimetrische und konduktometrische Untersuchungen an Zementsuspensionen, die mit den synthetisierten Stärkefließmitteln versetzt wurden, durchgeführt. Ergänzt wurden die Untersuchungen durch Porenlösungsanalysen zu verschiedenen Zeitpunkten der Hydratation. 6. Die kalorimetrischen Untersuchungen zur Beeinflussung der Hydratation des Portlandzementes zeigten, dass die dormante Periode durch die Zugabe der Stärkefließmittel z.T. erheblich verlängert wird. Es konnte gezeigt werden, dass, je höher die anionische Ladungsmenge der Stärkefließmittel ist, desto länger dauert die dormante Periode andauert. Darüber hinaus zeigte sich, dass eine niedrige Molekularmasse der Stärkefließmittel die Verlängerung der dormanten Periode begünstigt. 7. Durch die konduktometrischen Untersuchungen konnte gezeigt werden, dass alle Stärkefließmittel die Dauer des freien- und diffusionskontrollierten CSH-Phasenwachstums verlangsamen. Insbesondere die Ausfällung des Portlandits, welches mit dem Erstarrungsbeginn korreliert, erfolgt zu deutlich späteren Zeitpunkten. Des Weiteren korrelierten die konduktometrischen Untersuchungen mit der zeitlichen Entwicklung der Calciumkonzentration der Porenlösungen. Der Vergleich der Stärkefließmittel untereinander zeigte, dass die Molekularmasse ein Schlüsselparameter ist. Das Stärkefließmittel M-1 mit der geringsten Molekularmasse, welches geringe Mengen kurzkettiger Anhydroglucoseeinheiten aufweist, verzögert die Hydratphasenbildung am stärksten. Diese Wirkung ist vergleichbar mit der von Zuckern. Darüber hinaus deuteten die Ergebnisse daraufhin, dass die Stärkefließmittel auf den ersten Hydratationsprodukten adsorbieren, wodurch die Hydratphasenbildung verlangsamt wird. Die kalorimetrischen und konduktometrischen Daten sowie die Ergebnisse der Porenlösungsanalytik des Zementes, erforderten eine genauere Betrachtung der Beeinflussung der Hydratation der Klinkerphasen C3A und C3S, durch die Stärkefließmittel. Demzufolge wurden die Untersuchungen mit den Klinkerphasen C3A und C3S in Analogie zum Portlandzement durchgeführt. Beurteilung der Beeinflussung der Hydratation und der Porenlösung des C3A Während die kalorimetrischen Untersuchungen zur C3A-Hydratation eine Tendenz zur verlangsamten Hydratphasenbildung durch die Stärkefließmittel aufzeigten, lieferten die konduktometrischen Ergebnisse grundlegende Erkenntnisse zur Beeinflussung der C3A-Hydratation. Das Stadium I der C3A-Hydratation ist durch einen Abfall der elektrischen Leitfähigkeit geprägt. Dies korreliert mit dem Absinken der Calciumionenkonzentration und dem Anstieg der Aluminiumionenkonzentration in der Porenlösung der C3A-Suspensionen. Im Anschluss an das Stadium I bildet sich ein Plateau in den elektrischen Leitfähigkeitskurven aus. 8. Es konnte gezeigt werden, dass die Stärkefließmittel das Stadium I der C3A-Hydratation, d.h. die Auflösung und Bildung erster Calciumaluminathydrate verlangsamen. Insbesondere die Stärkefließmittel mit höherer Molekularmasse erhöhten die Dauer des Stadium I. Das Stadium II wird durch die Stärkefließmittel in folgender Reihenfolge am stärksten verlängert: M-1 > W-3 > K-1 > W-2 ≥ W-4 und verdeutlicht, dass keine Abhängigkeit von der anionischen Ladungsmenge identifiziert werden konnte. Die Ergebnisse zeigten, dass speziell die kurzkettige Stärke M-1, das Stadium II länger aufrechterhalten. 9. Das Stadium III und IV der C3A-Hydratation wird insbesondere durch die Stärkefließmittel mit höherer Molekularmasse verlängert. Die Ergebnisse der Porenlösungsanalytik korrelieren mit den Ergebnissen der elektrischen Leitfähigkeit. Speziell die zeitlichen Verläufe der Calciumionenkonzentration bildeten die Verläufe der Konduktivitätskurven der C3A-Hydratation mit großer Übereinstimmung ab. Beurteilung der Beeinflussung der Hydratation und der Porenlösung des C3S Die Ergebnisse der kalorimetrischen Untersuchungen zur Beeinflussung der C3S-Hydratation durch die Stärkefließmittel zeigen, dass diese maßgeblich verlangsamt wird. Das Maximum des Haupthydratationspeaks wird zu späteren Zeiten verschoben und auch die Höhe des Maximums wird deutlich verringert. Durch die konduktometrischen Experimente wurde aufgeklärt, welche Stadien der C3S-Hydrataion beeinflusst wurden. 10. Es konnte gezeigt werden, dass sowohl die Menge der eingebrachten anionischen Ladungen als auch das Vorhandensein sehr kleiner Stärkefließmittelmoleküle (Zucker), Schlüsselparameter der verzögerten Hydratationskinetik des C3S sind. Der grundlegende Mechanismus der Hydratationsverzögerung beruht auf einer Kombination aus verminderter CSH-Keimbildung und Adsorptionsprozessen auf den ersten gebildeten CSH-Phasen der C3S-Partikel. Beurteilung des Adsorptionsverhaltens am Zement, C3A und C3S Die Bestimmung des Adsorptionsverhaltens der Stärkefließmittel erfolgte mit der Phenol-Schwefelsäure-Methode an Zement,- C3A- und C3S-Suspensionen. Durch den Vergleich der Adsorptionsraten und Adsorptionsmengen in Abhängigkeit von den molekularen Parametern der Stärkefließmittel wurde ein Wechselwirkungsmodell identifiziert. 11. Die Ursache für die hohe Dispergierleistung der Stärkefließmittel liegt in Adsorptionsprozessen an den ersten gebildeten Hydratphasen des Zementes begründet. Die Molekularmasse der Stärkefließmittel ist ein Schlüsselparameter der entscheidend für den Mechanismus der Adsorption ist. Während anionische, langkettige Stärken an mehreren Zementpartikeln gleichzeitig adsorbieren und für eine Vernetzung der Zementpartikel untereinander sorgen (Verdickerwirkung), adsorbieren kurzkettige anionische Stärken lediglich an den ersten gebildeten Hydratphasen der einzelnen Zementpartikel und führen zu elektrostatischer Abstoßung (Fließmittelwirkung). 12. Es konnte gezeigt werden, dass die Stärkefließmittel mit geringerem Molekulargewicht bei höheren Konzentrationen an den Hydratphasen des Zementes adsorbieren. Die Stärkefließmittel mit höherer Molekularmasse erreichen bei einer Zugabemenge von 0,7 % ein Plateau. Daraus wird geschlussfolgert, dass die größeren Fließmittelmoleküle einen erhöhten Platzbedarf erfordern und zur Absättigung der hydratisierenden Oberflächen bei geringeren Zugabemengen führen. Darüber hinaus konnte gezeigt werden, dass die Stärkefließmittel mit höherer anionischer Ladungsmenge zu höheren Adsorptionsmengen auf den Zement-, C3A- und C3S-Partikeln führen. 13. Die Adsorptionsprozesse finden an den ersten gebildeten Hydratphasen der C3A-Partikel statt, wodurch sowohl die Auflösung des C3A als auch die Bildung der Calciumhydroaluminate verlangsamt wird. Darüber hinaus wurde festgestellt, dass die Verlangsamung des freien- und diffusionskontrollierten Hydratphasenwachstums des C3S, durch die Adsorption der Stärkefließmittel auf den ersten gebildeten CSH-Phasen hervorgerufen wird. Des Weiteren wurde festgestellt, dass sehr kleine zuckerähnliche Moleküle in der kurzkettigen Maniokstärke in der Lage sind, die Bildung der ersten CSH-Keime zu unterdrücken. Dadurch kann die langanhaltende Plateauphase der elektrischen Leitfähigkeit der C3S-Hydratation erklärt werden. Beurteilung der Porenstruktur- und Festigkeitsausbildung Die Beurteilung der Qualität der Mikrostruktur erfolgte durch die Bestimmung der Rohdichte und der Porenradienverteilung mit Hilfe der Quecksilberhochdruckporosimetrie. Durch das Versetzen der Zementleime mit den Stärkefließmitteln konnten bei gleichbleibender Verarbeitbarkeit Zementsteinprobekörper mit einem um 17,5 % geringeren w/z-Wert von 0,35 hergestellt werden. Die Absenkung des w/z-Wertes führt zu einem Anstieg der Rohdichte des Zementsteins. 14. Durch die Zugabe der Stärkefließmittel und den verringerten w/z-Wert wird die Porenstruktur der Zementsteinproben im Vergleich zum Referenzzementstein verfeinert, da die Gesamtporosität sinkt. Insbesondere der Kapillarporenanteil wird verringert und der Gelporenanteil erhöht. Im Unterschied zu den PCE-Fließmitteln führt die Zugabe der Stärkefließmittel zu keinem erhöhten Eintrag von Luftporen. Dies wiederum hat zur Folge, dass bei der Verwendung der Stärkefließmittel auf Entschäumer verzichtet werden kann. 15. Entsprechend der dichteren Zementsteinmatrix wurden für die Zementsteine mit den Stärkefließmitteln nach 7 d und 28 d, erhöhte Biegezug- und Druckfestigkeiten ermittelt. Insbesondere die 28 d Druckfestigkeit wurde durch den verringerten w/z-Wert um die Faktoren 3,5 - 6,6 erhöht. KW - Zusatzmittel KW - Fließmittel KW - Stärkefließmittel KW - Zementhydratation KW - Synthese KW - Bauchemie KW - Betonverflüssiger Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20220505-46402 ER -