TY - JOUR A1 - Patzelt, Max A1 - Erfurt, Doreen A1 - Ludwig, Horst-Michael T1 - Quantification of cracks in concrete thin sections considering current methods of image analysis JF - Journal of Microscopy N2 - Image analysis is used in this work to quantify cracks in concrete thin sections via modern image processing. Thin sections were impregnated with a yellow epoxy resin, to increase the contrast between voids and other phases of the concrete. By the means of different steps of pre-processing, machine learning and python scripts, cracks can be quantified in an area of up to 40 cm2. As a result, the crack area, lengths and widths were estimated automatically within a single workflow. Crack patterns caused by freeze-thaw damages were investigated. To compare the inner degradation of the investigated thin sections, the crack density was used. Cracks in the thin sections were measured manually in two different ways for validation of the automatic determined results. On the one hand, the presented work shows that the width of cracks can be determined pixelwise, thus providing the plot of a width distribution. On the other hand, the automatically measured crack length differs in comparison to the manually measured ones. KW - Beton KW - Rissbildung KW - Bildanalyse KW - Maschinelles Lernen KW - Mikroskopie KW - concrete KW - crack KW - degradation KW - transmitted light microscopy Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20220811-46754 UR - https://onlinelibrary.wiley.com/doi/full/10.1111/jmi.13091 VL - 2022 IS - Volume 286, Issue 2 SP - 154 EP - 159 ER - TY - THES A1 - Dimmig, Andrea T1 - Einflüsse von Polymeren auf die Mikrostruktur und die Dauerhaftigkeit kunststoffmodifizierter Mörtel (PCC) T1 - The effects of polymers on microstructure and durability of polymer-modified mortars (PCC) N2 - Die Einflüsse polymerer Zusätze auf die Ausbildung der Mikrostruktur im frühen Stadium der Erhärtung und auf die Eigenschaften, insbesondere die Dauerhaftigkeit der modifizierten Mörtel wurden erforscht. Es sollte die Frage beantwortet werden, ob durch die Modifizierung die Dauerhaftigkeit von Mörteln mehr verbessert werden kann, als dies durch übliche betontechnologische Maßnahmen möglich ist. Die Ausbildung der Mikrostruktur in den ersten 24 Stunden der Erhärtung wurde mit verschiedenen Methoden, u.a. mittels ESEM, untersucht. Es wurden Modellvorstellungen zur Ausbildung der organischen Matrix und der anorganischen Matrix entwickelt: Interaktionen sind Adsorptionsreaktionen, Agglomerationen und Behinderung der Hydratation. Es wurden Frisch- und Festmörteluntersuchungen beschrieben und interpretiert. Unterschiedliche Dauerhaftigkeitsuntersuchungen wurden durchgeführt und bewertet. Die Mikrostruktur der Festmörtel wurde hinsichtlich ihres Einflusses auf die Dauerhaftigkeit betrachtet. N2 - The effects of polymeric additives on the formation of the microstructure at an early stage of hardening and on the properties, especially the durabiliy of modified mortars, were investigated. The question was whether the durability of mortars may be increased to a larger extent by the modification or by the usual measures taken in concrete technology. The formation of the microstructure within the first 24 hours of hardening was investigated by various methods, e.g. by ESEM (environmental scanning electron microscope). Models of the formation of the organic and anorganic matrix were developed: interactions are adsorbtion reactions, agglomerations, and impediments to hydration. Tests on fresh and hardened mortar are described and interpreted. Several durability tests were conducted and evaluated. The microstructure of the hardened mortars was studied with regard to its influence on the durability. KW - Kunststoffmörtel KW - Gefüge KW - Erhärtungsprüfung KW - Langzeitverhalten KW - Kunstharzmodifizierter Zementbeton KW - Mikrostruktur KW - Mikroskopie KW - Porenlösung KW - Frischmörtel KW - Festmörtel KW - microstructure KW - microscopy KW - pore solution KW - fresh mortar KW - hardened mortar Y1 - 2002 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20040311-653 ER - TY - THES A1 - Schirmer, Ulrike T1 - Die Adsorption von Dispersionspartikeln und Schutzkolloiden an Oberflächen von Zementphasen und Phasen der Zusatzstoffe N2 - Ziel der Arbeit war das Adsorptionsverhalten ausgewählter schutzkolloidstabilisierter Polymerpartikel mit variierender chemischer Basis im zementären System zu beschreiben und basierend auf den gewonnenen Erkenntnissen das Konkurrenzverhalten beim Angebot unterschiedlicher mineralischer Oberflächen zu klären. Sowohl die Destabilisierung der Polymerpartikel im alkalischen Milieu, welche eine Voraussetzung für derartige Adsorptionsprozesse ist, als auch die Veränderung von Oberflächeneigenschaften verschiedener mineralischer Partikel durch Hydratations- und Ionenadsorptionsprozesse, wurden u. a. mit Hilfe elektrokinetischer Experimente erfasst. Die spektralphotometrische Erstellung von Adsorptionsisothermen ermöglichte zudem die Ermittlung der jeweiligen adsorbierten Polymermenge zu verschiedenen Zeitpunkten der frühen Hydratation. Weiterhin wurde die Polymeradsorption an Partikeln ausgewählter Zusatzstoffe in Abhängigkeit von der Ionenstärke der Flüssigphase beschrieben. Rasterelektronenmikroskopische Untersuchungen cryo-präparierter polymermodifizierter Zementleimproben ermöglichten es außerdem deren Mikrostruktur im suspensiven Zustand zu visualisieren. Diese Aufnahmen, ebenso wie die Ergebnisse grundlegender hydratationskinetischer Untersuchungen wurden in Wechselbeziehung zu den Ergebnissen der Adsorptionsuntersuchungen gebracht. Maßgelbliche intermolekulare und interpartikuläre Wechselwirkungen, infolge derer sich die Stabilitätsverhältnisse im Zementleim ändern und die Polymerpartikel adsorbieren sind im Wesentlichen die Desorption des Schutzkolloids von der Polymerpartikeloberfläche, die Ionisation funktioneller Gruppen der Polymerpartikel und der Schutzkolloidmakromoleküle im alkalischen Milieu und infolgedessen die Komplexbildung mit Ionen der Zementleimporenlösung. Die Auswirkungen dieser Vorgänge auf die Lösungs- und Fällungskinetik des Zementleimes wurden erfasst und mit der chemischen Zusammensetzung der polymeren Systeme korreliert. KW - Kunststoffmörtel KW - Interpartikuläre Wechselwirkungen KW - Suspensionsanalytik KW - Lösungsanalytik KW - Mikroskopie KW - Polymeradsorption KW - Kunststoffadditiv KW - Mikrostruktur KW - Mehrphasensystem Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20180327-37383 ER -