TY - THES A1 - Müller, Matthias T1 - Salt-frost Attack on Concrete - New Findings regarding the Damage Mechanism N2 - The reduction of the cement clinker content is an important prerequisite for the improvement of the CO2-footprint of concrete. Nevertheless, the durability of such concretes must be sufficient to guarantee a satisfactory service life of structures. Salt frost scaling resistance is a critical factor in this regard, as it is often diminished at increased clinker substitution rates. Furthermore, only insufficient long-term experience for such concretes exists. A high salt frost scaling resistance thus cannot be achieved by applying only descriptive criteria, such as the concrete composition. It is therefore to be expected, that in the long term a performance based service life prediction will replace the descriptive concept. To achieve the important goal of clinker reduction for concretes also in cold and temperate climates it is important to understand the underlying mechanisms for salt frost scaling. However, conflicting damage theories dominate the current State of the Art. It was consequently derived as the goal of this thesis to evaluate existing damage theories and to examine them experimentally. It was found that only two theories have the potential to describe the salt frost attack satisfactorily – the glue spall theory and the cryogenic suction theory. The glue spall theory attributes the surface scaling to the interaction of an external ice layer with the concrete surface. Only when moderate amounts of deicing salt are present in the test solution the resulting mechanical properties of the ice can cause scaling. However, the results in this thesis indicate that severe scaling also occurs at deicing salt levels, at which the ice is much too soft to damage concrete. Thus, the inability of the glue spall theory to account for all aspects of salt frost scaling was shown. The cryogenic suction theory is based on the eutectic behavior of salt solutions, which consist of two phases – water ice and liquid brine – between the freezing point and the eutectic temperature. The liquid brine acts as an additional moisture reservoir, which facilitates the growth of ice lenses in the surface layer of the concrete. The experiments in this thesis confirmed, that the ice formation in hardened cement paste increases due to the suction of brine at sub-zero temperatures. The extent of additional ice formation was influenced mainly by the porosity and by the chloride binding capacity of the hardened cement paste. Consequently, the cryogenic suction theory plausibly describes the actual generation of scaling, but it has to be expanded by some crucial aspects to represent the salt frost scaling attack completely. The most important aspect is the intensive saturation process, which is ascribed to the so-called micro ice lens pump. Therefore a combined damage theory was proposed, which considers multiple saturation processes. Important aspects of this combined theory were confirmed experimentally. As a result, the combined damage theory constitutes a good basis to understand the salt frost scaling attack on concrete on a fundamental level. Furthermore, a new approach was identified, to account for the reduced salt frost scaling resistance of concretes with reduced clinker content. T2 - Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechnismus KW - Beton KW - Frost KW - Concrete KW - Salt frost attack KW - Damage mechanism KW - Glue Spall KW - Cryogenic Suction Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20230103-48681 UR - https://e-pub.uni-weimar.de/opus4/frontdoor/index/index/docId/4502 N1 - Englische Fassung meiner deutschsprachigen Dissertation mit dem Titel "Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechnismus". ER - TY - THES A1 - Piethe, Vivienne T1 - Konfektionierung eines Calciumsulfat-Bindemittelsystems zur Herstellung volumenstabiler Fließestrichmörtel N2 - Bei einem marktüblichen Calciumsulfat-Fließestrich wurden in der Praxis schädigende Volu-menexpansionen festgestellt. Diese sind ein Resultat aus dem Zusammenwirken des einge-setzten Bindemittel-Compounds und einer kritischen Gesteinskörnung. Das Ziel dieser Arbeit ist es, ein Calciumsulfat-Bindemittelsystem zu konfektionieren, welches in der Lage ist, die im Mörtel festgestellten Volumenexpansionen zu unterbinden. Es sollen verschiedene Bindemittel- und Additivzusammensetzungen untersucht werden, welche in Verbindung mit der kritischen Gesteinskörnung die Herstellung eines volumenstabilen Fließestrichs ermöglichen. Dazu soll folgende Fragestellung beantwortet werden: Welche Ursachen hat die Volumenzunahme und wie ist diese zu minimieren bzw. unterbinden? Dabei werden unterschiedliche Bindemittelrezepturen aus α-Halbhydrat, Thermoanhydrit und Naturanhydrit, sowie verschiedene Additivzusammensetzungen hergestellt und untersucht. Durch Längenänderungsmessungen in der Schwindrinne werden die Einflüsse der Binde-mittel, der Additivzusammensetzungen und der Wasser/Bindemittel-Werte auf das Län-genänderungsverhalten untersucht. Mittels Variation der einzelnen Compound-Bestandteile kann festgestellt werden, dass der Stabilisierer die Längenänderung negativ beeinflusst. Dieser bindet freies Wasser, welches für eine Reaktion zwischen Bindemittel und Gesteins-körnung im plastischen Zustand nicht mehr zur Verfügung steht. Diese Reaktion kann folglich erst im erhärteten Zustand ablaufen und verursacht die schädigende Volumenexpansion. Abschließend wurde ein Bindemittel-Compound konfektioniert, welcher ohne Zusatz von Stabilisierern in Zusammenhang mit der kritischen Gesteinskörnung volumenstabil ist und keine Schäden auslöst. KW - Calciumsulfat KW - Gips KW - Fließestrich KW - Volumenstabilität KW - Calciumsulfatfließestrich Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20190902-39445 ER -