TY - THES A1 - Müller, Matthias T1 - Salt-frost Attack on Concrete - New Findings regarding the Damage Mechanism N2 - The reduction of the cement clinker content is an important prerequisite for the improvement of the CO2-footprint of concrete. Nevertheless, the durability of such concretes must be sufficient to guarantee a satisfactory service life of structures. Salt frost scaling resistance is a critical factor in this regard, as it is often diminished at increased clinker substitution rates. Furthermore, only insufficient long-term experience for such concretes exists. A high salt frost scaling resistance thus cannot be achieved by applying only descriptive criteria, such as the concrete composition. It is therefore to be expected, that in the long term a performance based service life prediction will replace the descriptive concept. To achieve the important goal of clinker reduction for concretes also in cold and temperate climates it is important to understand the underlying mechanisms for salt frost scaling. However, conflicting damage theories dominate the current State of the Art. It was consequently derived as the goal of this thesis to evaluate existing damage theories and to examine them experimentally. It was found that only two theories have the potential to describe the salt frost attack satisfactorily – the glue spall theory and the cryogenic suction theory. The glue spall theory attributes the surface scaling to the interaction of an external ice layer with the concrete surface. Only when moderate amounts of deicing salt are present in the test solution the resulting mechanical properties of the ice can cause scaling. However, the results in this thesis indicate that severe scaling also occurs at deicing salt levels, at which the ice is much too soft to damage concrete. Thus, the inability of the glue spall theory to account for all aspects of salt frost scaling was shown. The cryogenic suction theory is based on the eutectic behavior of salt solutions, which consist of two phases – water ice and liquid brine – between the freezing point and the eutectic temperature. The liquid brine acts as an additional moisture reservoir, which facilitates the growth of ice lenses in the surface layer of the concrete. The experiments in this thesis confirmed, that the ice formation in hardened cement paste increases due to the suction of brine at sub-zero temperatures. The extent of additional ice formation was influenced mainly by the porosity and by the chloride binding capacity of the hardened cement paste. Consequently, the cryogenic suction theory plausibly describes the actual generation of scaling, but it has to be expanded by some crucial aspects to represent the salt frost scaling attack completely. The most important aspect is the intensive saturation process, which is ascribed to the so-called micro ice lens pump. Therefore a combined damage theory was proposed, which considers multiple saturation processes. Important aspects of this combined theory were confirmed experimentally. As a result, the combined damage theory constitutes a good basis to understand the salt frost scaling attack on concrete on a fundamental level. Furthermore, a new approach was identified, to account for the reduced salt frost scaling resistance of concretes with reduced clinker content. T2 - Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechnismus KW - Beton KW - Frost KW - Concrete KW - Salt frost attack KW - Damage mechanism KW - Glue Spall KW - Cryogenic Suction Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20230103-48681 UR - https://e-pub.uni-weimar.de/opus4/frontdoor/index/index/docId/4502 N1 - Englische Fassung meiner deutschsprachigen Dissertation mit dem Titel "Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechnismus". ER - TY - JOUR A1 - Müller, Matthias A1 - Ludwig, Horst-Michael A1 - Tange Hasholt, Marianne T1 - Salt frost attack on concrete: the combined effect of cryogenic suction and chloride binding on ice formation JF - Materials and Structures N2 - Scaling of concrete due to salt frost attack is an important durability issue in moderate and cold climates. The actual damage mechanism is still not completely understood. Two recent damage theories—the glue spall theory and the cryogenic suction theory—offer plausible, but conflicting explanations for the salt frost scaling mechanism. The present study deals with the cryogenic suction theory, which assumes that freezing concrete can take up unfrozen brine from a partly frozen deicing solution during salt frost attack. According to the model hypothesis, the resulting saturation of the concrete surface layer intensifies the ice formation in this layer and causes salt frost scaling. In this study an experimental technique was developed that makes it possible to quantify to which extent brine uptake can increase ice formation in hardened cement paste (used as a model material for concrete). The experiments were carried out with low temperature differential scanning calorimetry, where specimens were subjected to freeze–thaw cycles while being in contact with NaCl brine. Results showed that the ice content in the specimens increased with subsequent freeze–thaw cycles due to the brine uptake at temperatures below 0 °C. The ability of the hardened cement paste to bind chlorides from the absorbed brine at the same time affected the freezing/melting behavior of the pore solution and the magnitude of the ice content. KW - Beton KW - Frost KW - Beton KW - Frostangriff KW - salt frost attack KW - cryogenic suction KW - chloride binding Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20211207-45392 UR - https://link.springer.com/article/10.1617/s11527-021-01779-7 VL - 2021 IS - issue 54, article 189 SP - 1 EP - 16 ER - TY - THES A1 - Müller, Matthias T1 - Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechanismus N2 - Für die Verminderung der betonspezifischen CO2-Emissionen wird ein verstärkter Einsatz klinkerreduzierter Zemente bzw. Betone angestrebt. Die Reduzierung des Klinkergehaltes darf jedoch nicht zu einer lebensdauerrelevanten Beeinträchtigung der Betondauerhaftigkeit führen. In diesem Zusammenhang stellt der Frost-Tausalz-Widerstand eine kritische Größe dar, da er bei höheren Klinkersubstitutionsraten häufig negativ beeinflusst wird. Erschwerend kommt hinzu, dass für klinkerreduzierte Betone nur ein unzureichender Erfahrungsschatz vorliegt. Ein hoher Frost-Tausalz-Widerstand kann daher nicht ausschließlich anhand deskriptiver Vorgaben gewährleistet werden. Demgemäß sollte perspektivisch auch für frost-tausalzbeanspruchte Bauteile eine performancebasierte Lebensdauerbetrachtung erfolgen. Eine unverzichtbare Grundlage für das Erreichen dieser Ziele ist ein Verständnis für die Schadensvorgänge beim Frost-Tausalz-Angriff. Der Forschungsstand ist jedoch geprägt von widersprüchlichen Schadenstheorien. Somit wurde als Zielstellung für diese Arbeit abgeleitet, die existierenden Schadenstheorien unter Berücksichtigung des aktuellen Wissensstandes zu bewerten und mit eigenen Untersuchungen zu prüfen und einzuordnen. Die Sichtung des Forschungsstandes zeigte, dass nur zwei Theorien das Potential haben, den Frost-Tausalz-Angriff umfassend abzubilden – die Glue Spall Theorie und die Cryogenic Suction Theorie. Die Glue Spall Theorie führt die Entstehung von Abwitterungen auf die mechanische Schädigung der Betonoberfläche durch eine anhaftende Eisschicht zurück. Dabei sollen nur bei moderaten Tausalzkonzentrationen in der einwirkenden Lösung kritische Spannungszustände in der Eisschicht auftreten, die eine Schädigung der Betonoberfläche hervorrufen können. In dieser Arbeit konnte jedoch nachgewiesen werden, dass starke Abwitterungen auch bei Tausalz¬konzentrationen auftreten, bei denen eine mechanische Schädigung des Betons durch das Eis auszuschließen ist. Damit wurde die fehlende Eignung der Glue Spall Theorie aufgezeigt. Die Cryogenic Suction Theorie fußt auf den eutektischen Eigenschaften von Tausalz-lösungen, die im gefrorenen Zustand immer als Mischung auf festem Wassereis und flüssiger, hochkonzentrierter Salzlösung bestehen, solange ihre Eutektikumstemperatur nicht unter¬schritten wird. Die flüssige Phase im salzhaltigen Eis stellt für gefrorenen Beton ein bisher nicht berücksichtigtes Flüssigkeitsreservoir dar, welches trotz der hohen Salzkonzentration die Eisbildung in der Betonrandzone verstärken und so die Entstehung von Abwitterungen verursachen soll. In dieser Arbeit wurde bestätigt, dass die Eisbildung im Zementstein beim Gefrieren in hochkonzentrierter Tausalzlösung tatsächlich verstärkt wird. Das Ausmaß der zusätzlichen Eisbildung wurde dabei auch von der Fähigkeit des Zementsteins zur Bindung von Chloridionen aus der Tausalzlösung beeinflusst. Zusammenfassend wurde festgestellt, dass die Cryogenic Suction Theorie eine gute Beschreibung des Frost-Tausalz-Angriffes darstellt, aber um weitere Aspekte ergänzt werden muss. Die Berücksichtigung der intensiven Sättigung von Beton durch den Prozess der Mikroeislinsenpumpe stellt hier die wichtigste Erweiterung dar. Basierend auf dieser Überlegung wurde eine kombinierte Schadenstheorie aufgestellt. Wichtige Annahmen dieser Theorie konnten experimentell bestätigt werden. Im Ergebnis wurde so die Grundlage für ein tiefergehendes Verständnis des Frost-Tausalz-Angriffes geschaffen. Zudem wurde ein neuer Ansatz identifiziert, um die (potentielle) Verringerung des Frost-Tausalz-Widerstandes klinkerreduzierter Betone zu erklären. N2 - The reduction of the cement clinker content is an important prerequisite for the improvement of the CO2-footprint of concrete. Nevertheless, the durability of such concretes must be sufficient to guarantee a satisfactory service life of structures. Salt frost scaling resistance is a critical factor in this regard, as it is often diminished at increased clinker substitution rates. Furthermore, only insufficient long-term experience for such concretes exists. A high salt frost scaling resistance thus cannot be achieved by applying only descriptive criteria, such as the concrete composition. It is therefore to be expected, that in the long term a performance based service life prediction will replace the descriptive concept. To achieve the important goal of clinker reduction for concretes also in cold and temperate climates it is important to understand the underlying mechanisms for salt frost scaling. However, conflicting damage theories dominate the current State of the Art. It was consequently derived as the goal of this thesis to evaluate existing damage theories and to examine them experimentally. It was found that only two theories have the potential to describe the salt frost attack satisfactorily – the glue spall theory and the cryogenic suction theory. The glue spall theory attributes the surface scaling to the interaction of an external ice layer with the concrete surface. Only when moderate amounts of deicing salt are present in the test solution the resulting mechanical properties of the ice can cause scaling. However, the results in this thesis indicate that severe scaling also occurs at deicing salt levels, at which the ice is much too soft to damage concrete. Thus, the inability of the glue spall theory to account for all aspects of salt frost scaling was shown. The cryogenic suction theory is based on the eutectic behavior of salt solutions, which consist of two phases – water ice and liquid brine – between the freezing point and the eutectic temperature. The liquid brine acts as an additional moisture reservoir, which facilitates the growth of ice lenses in the surface layer of the concrete. The experiments in this thesis confirmed, that the ice formation in hardened cement paste increases due to the suction of brine at sub-zero temperatures. The extent of additional ice formation was influenced mainly by the porosity and by the chloride binding capacity of the hardened cement paste. Consequently, the cryogenic suction theory plausibly describes the actual generation of scaling, but it has to be expanded by some crucial aspects to represent the salt frost scaling attack completely. The most important aspect is the intensive saturation process, which is ascribed to the so-called micro ice lens pump. Therefore a combined damage theory was proposed, which considers multiple saturation processes. Important aspects of this combined theory were confirmed experimentally. As a result, the combined damage theory constitutes a good basis to understand the salt frost scaling attack on concrete on a fundamental level. Furthermore, a new approach was identified, to account for the reduced salt frost scaling resistance of concretes with reduced clinker content. KW - Beton KW - Frost KW - Beton KW - Frost-Tausalz-Angriff KW - Schadensmechanismus KW - Concrete KW - Salt-Frost-Attack Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20210922-45025 ER - TY - CHAP A1 - Gründel, Hendrik A1 - Ludwig, Horst-Michael A1 - Geisenhanslüke, Carsten A1 - Müller, Matthias T1 - Einfluss der Zusammensetzung von Portlandzementklinker und Sulfatträger auf das Erstarrungsverhalten von Spritzbeton T2 - Tagungsband 19. Ibausil - 19. Internationale Baustofftagung : 16.-18. September 2015, Weimar N2 - In der vorliegenden Studie wurde der Einfluss der Klinkerzusammensetzung sowie der Sulfatträgerart auf die Leistungsfähigkeit eines Spritzzementes untersucht. Um eine Untersulfatisierung im System mit einen Aluminiumsulfat / -hydroxid Beschleuniger zu vermeiden, sollte ein anhydritbasierter Sulfatträger eingesetzt werden. Dies führt zu einer besseren Festigkeitsentwicklung im jungen Alter. N2 - In the present study, the influence of the clinker composition as well as the setting agent type on the performance of a sprayed cement was investigated. To avoid undersulfatization in the system with an aluminum sulfate/hydroxide accelerator, an anhydrite-based setting agent should be used. This leads to a better strength development at a young age. KW - Beton KW - Spritzbeton KW - Zement KW - Spritzbeton KW - Spritzzement KW - Sulfatträger KW - Sprayed concrete KW - Setting agent Y1 - 2015 SN - 978-3-00-050225-5 (Bauhaus-Universitätsverlag Weimar) U6 - http://dx.doi.org/10.25643/bauhaus-universitaet.4885 ER - TY - CHAP A1 - Müller, Matthias A1 - Ludwig, Horst-Michael ED - Ludwig, Horst-Michael T1 - Sulfatangriff magnesiumhaltiger Wässer auf Mörtel unterschiedlicher Zusammensetzung T2 - Tagungsband 18. Ibausil - 18. Internationale Baustofftagung : 12.-15. September 2012, Weimar N2 - Die besondere Aggressivität von hochkonzentrierten Magnesiumsulfatlösungen bei Einwirkung auf Beton ist seit vielen Jahrzehnten bekannt. Neben dem Sulfat greift zusätzlich auch das Magnesium den Zementstein an. Bei hohen Lösungskonzentrationen nimmt der Magnesiumangriff gegenüber dem Sulfatangriff sogar eine dominante Rolle ein. Magnesiumgehalte unter 300 mg/l im Grundwasser gelten allerdings bislang als nicht angreifend. In Auslagerungs- und Laborversuchen wurde jedoch festgestellt, dass auch bei praxisrelevanten Magnesium- (<300 mg/l) und Sulfatgehalten (1.500 mg/l) das Magnesium zu einer deutlichen Verschärfung des Sulfatangriffes bei niedrigen Temperaturen führte. Diese Verschärfung trat bei Mörteln und Betonen auf, bei denen der erhöhte Sulfatwiderstand durch einen teilweisen Zementersatz mit 20 % Flugasche zu einem CEM II/A-LL erreicht werden sollte, gemäß der Flugascheregelung nach EN 206-1/DIN 1045-2. Bei einem teilweisen Zementersatz durch 30 % Flugasche konnte auch in magnesiumhaltigen Sulfatlösungen eine deutliche Verbesserung des Sulfatwiderstandes erreicht werden. Mörtel mit HS-Zement als Bindemittel wiesen keinerlei Schäden auf. Schadensverursachend war eine Kombination mehrerer Einflüsse. Zum einen wurde der Sulfatwiderstand des Zement-Flugasche-Systems durch die unzureichende Reaktion der Flugasche infolge der niedrigen Lagerungstemperatur geschwächt. Zum anderen konnte durch die Einwirkung des Magnesiums in der Randzone vermutlich eine Destabilisierung der C-S-H-Phasen erfolgen, wodurch die Thaumasitbildung an dieser Stelle forciert wurde. Zusätzlich wurde durch den Portlanditverbrauch und die pH-Wert-Absenkung in der Randzone die puzzolanische Reaktion der Flugasche behindert. KW - Beton KW - Beton KW - Sulfatangriff KW - Flugasche KW - Magnesiumsulfat KW - Thaumasit Y1 - 2012 SN - 978-3-00-034075-8 (Bauhaus-Universitätsverlag Weimar) U6 - http://dx.doi.org/10.25643/bauhaus-universitaet.4873 ER - TY - RPRT A1 - Müller, Christoph A1 - Seidel, Maik A1 - Ludwig, Horst-Michael A1 - Müller, Matthias T1 - Prüfung des Frost-Tausalz-Widerstandes von Beton für die Expositionsklasse XF2 N2 - In cold and moderate climates concrete can be subjected to a combined salt frost attack, which can cause scaling damage. Consequently, numerous test procedures were developed to determine the resistance of concrete compositions against this kind of attack. These tests typically mimic a severe attack with high levels of saturation, e.g. as for concrete pavements. Very few approaches exist for testing the salt frost scaling resistance of concretes, which are subjected only to medium levels of saturation, as such concrete elements typically don’t show notable scaling damage. However, the increasing use of low carbon cements with high clinker substitution rates might affect the salt frost scaling resistance of such concrete elements to some extent. To ensure adequate durability of such concretes it is thus desirable to determine their performance in an actual test procedure instead of relying on past experience. Thus, less severe test methods was developed, which are based on the Slab test and the CDF test, repectively. N2 - In kalten und gemäßigten Klimazonen kann Beton einem kombinierten Frost-Tausalz-Angriff ausgesetzt sein, der zu Schäden in Form von Abwitterungen führen kann. Daher wurden zahlreiche Prüfverfahren entwickelt, um die Widerstandsfähigkeit von Betonzusammensetzungen gegen diese Art des Angriffs zu bestimmen. Diese Tests simulieren in der Regel einen starken Angriff mit hohen Sättigungsgraden, wie z. B. bei Betonfahrbahnen. Es gibt nur sehr wenige Ansätze für die Prüfung des Widerstands von Betonen, die nur einem mittleren Sättigungsgrad ausgesetzt sind, da solche Betonelemente in der Regel keine nennenswerten Abwitterungen aufweisen. Die zunehmende Verwendung von klinkereffizienten Zementen könnte sich jedoch in gewissem Maße auf den Frost-Tausalz-Widerstand solcher Betonelemente auswirken. Um eine angemessene Dauerhaftigkeit zu gewährleisten ist es daher wünschenswert, ihre Leistungsfähigkeit in einem tatsächlichen Prüfverfahren zu ermitteln, anstatt sich auf Erfahrungswerte zu verlassen. Daher wurden Ansätze für abgeschwächte Prüfverfahren entwickelt, die auf dem Slab-Test bzw. dem CDF-Test beruhen. KW - Beton KW - Frost KW - Prüfverfahren KW - Beton KW - Frost-Tausalz-Widerstand KW - XF2 KW - CDF KW - Slab-Test Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20240226-48877 ER - TY - CHAP A1 - Müller, Matthias A1 - Ehrhardt, Dirk A1 - Ludwig, Horst-Michael ED - Ludwig, Horst-Michael T1 - Optimierung der Nachbehandlung von Waschbetonoberflächen T2 - Tagungsband 18. Ibausil - 18. Internationale Baustofftagung : 12.-15. September 2012, Weimar N2 - Der Nachbehandlung eines Fahrbahndeckenbetons kommt zum Erzielen eines hohen Frost-Tausalz-Widerstandes der fertigen Betondecke eine besondere Bedeutung zu. Bei der Waschbetonbauweise erfolgt die Nachbehandlung in mehreren Schritten. Eine erste Nachbehandlung gewährleistet den Verdunstungsschutz des Betons bis zum Zeitpunkt des Ausbürstens des verzögerten Oberflächenmörtels. Daran schließt sich die zweite Nachbehandlung an, in der Regel durch Aufsprühen eines flüssigen Nachbehandlungsmittels. Der zweite Nachbehandlungsschritt ist entscheidend für den Frost-Tausalz-Widerstand der Betondecke. Im Rahmen eines Forschungsprojektes wurde daher untersucht, inwiefern durch eine Optimierung der zweiten Nachbehandlung der Frost-Tausalz-Widerstand von Waschbetonoberflächen erhöht werden kann, insbesondere bei Verwendung hüttensandhaltiger Zemente. Schon durch eine einmalige Nassnachbehandlung wurde eine deutlich höherer Widerstand der Waschbetons gegen Frost-Tausalz-Angriff erzielt. KW - Beton KW - Straßenbeton KW - Waschbeton KW - Nachbehandlung KW - Frost-Tausalz-Widerstand Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:gbv:wim2-20240226-48722 SN - 978-3-00-034075-8 ER - TY - CHAP A1 - Müller, Matthias A1 - Ludwig, Horst-Michael A1 - Ben Haha, Mohsen A1 - Zajac, Maciej ED - Ludwig, Horst-Michael T1 - Optimization of multi-component cements containing clinker, slag, V-fly ash, limestone T2 - Tagungsband 19. Ibausil - 19. Internationale Baustofftagung, 16. - 18.09.2015, Weimar. Band 2 N2 - The aim of this study was to investigate the optimization of the strength development of quaternary cements with 50 % clinker by a variation of the particle size distribution of the components GGBFS, fly ash and limestone powder. By balancing the overall PSD of the cement by using unprocessed fly ash and coarse limestone powder in combination with a very fine GGBFS, the water demand of the resulting quaternary cements remained unaltered, while the compressive strength of the cements was increased significantly after 7d, 28 and 56d. As can be expected, the quaternary cement with 30 wt.% of the fine slag exhibited a stronger strength increase (about 18 % after 28 d) than the cements with only 20 wt.% slag (about 10% after 28d). KW - Zement KW - Cement KW - Slag KW - Fly ash KW - Limestone powder KW - Particle size distribution Y1 - 2015 SN - 978-3-00-050225-5 (Bauhaus-Universitätsverlag Weimar) U6 - http://dx.doi.org/10.25643/bauhaus-universitaet.4870 ER -