@phdthesis{Eberhardt2010,
  author    = {Eberhardt, Arnd Bernd},
  title     = {On the mechanisms of shrinkage reducing admixtures in self con-solidating mortars and concretes},
  isbn      = {978-3-8440-0027-6},
  doi       = {10.25643/bauhaus-universitaet.1454},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20110620-15491},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  year      = {2010},
  abstract  = {'Zur Wirkungsweise schwindreduzierender Zusatzmittel in selbstverdichtenden M{\"o}rteln und Betonen' Problemstellung und Zielsetzung 1. Der Einsatz selbstverdichtender M{\"o}rtel und Betone im Bauwesen erbringt klare Vorteile. Dies sind im Wesentlichen eine erh{\"o}hte Betonierleistung, verbesserte Betonierqualit{\"a}t f{\"u}r bewehrten Beton im Allgemeinen und f{\"u}r filigrane, eng bewehrte Bauteile im Besonderen. Die mit den traditionellen Methoden des Betonbaus verbundenen L{\"a}rmemissionen werden erheblich reduziert. Der Wegfall der f{\"u}r herk{\"o}mmlichen Beton notwendigen Verdichtungsarbeit reduziert den manuellen Aufwand und die damit verbundenen Gesundheitsrisiken. Das im selbstverdichtenden Beton ben{\"o}tigte hohe Bindemittelleimvolumen ist der Betondauerhaftigkeit abtr{\"a}glich. Es bewirkt, dass selbstverdichtende Betone ein erh{\"o}htes Schwindmaß sowie eine h{\"o}here Rissneigung aufweisen. Ersteres kann f{\"u}r Betonbauteile zu erheblichen Verformungen oder Zwangsspannungen f{\"u}hren, w{\"a}hrend Letzteres die Dauerhaftigkeit des Baustoffes Beton aufgrund einer Beg{\"u}nstigung rissinduzierter Sch{\"a}digungsmechanismen stark beeintr{\"a}chtigt. 2. Herk{\"o}mmliche Methoden zur Schwindreduktion und Rissvermeidung verfolgen haupts{\"a}chlich das Ziel, die im Beton einzusetzenden Bindemittelmengen zu reduzieren. F{\"u}r selbstverdichtende Betone ist dieses Konzept nur sehr begrenzt anwendbar, da die Selbstverdichtung dieser Betone relativ hohe Bindemittelleimvolumen erfordert. Eine M{\"o}glichkeit das Ausmaß des Schwindens und damit die Rissanf{\"a}lligkeit selbstverdichtender Betone zu senken, besteht in der Anwendung schwindreduzierender Betonzusatzmittel. Eingef{\"u}hrt in den achtziger Jahren des 20ten Jahrhunderts in Japan, erweisen sich diese Zusatzmittel als effiziente Methode zur Verbesserung der Qualit{\"a}t bindemittelreicher Hochleistungsbetone im Allgemeinen und selbstverdichtender Betone im Besonderen. 3. W{\"a}hrend die Wirksamkeit schwindreduzierender Betonzusatzmittel in zahlreichen anwendungsorientierten Studien nachgewiesen werden konnte, ist das Wirkprinzip nur unzureichend erforscht. Eines der Hauptziele dieser Arbeit ist deshalb die gr{\"u}ndliche Erforschung des Wirkmechanismus schwindreduzierender Betonzusatzmittel. 4. Weiterhin besteht Unklarheit, wie diese Zus{\"a}tze in den Chemismus der Zementhydratation eingreifen und ob dies der allgemeinen Dauerhaftigkeit des Baustoffes Beton abtr{\"a}glich ist. Ein wichtiges Ziel dieser Arbeit ist deshalb die gr{\"u}ndliche Erforschung der Zementhydratation in Gegenwart einer repr{\"a}sentativen Auswahl verschiedener Typen schwindreduzierender Betonzusatzmittel. 5. Die Nachhaltigkeit der Anwendung schwindreduzierender Zusatzmittel ist bedeutend f{\"u}r die Betondauerhaftigkeit. Ob schwindreduzierende Zusatzmittel auslaugbar sind und ob eine Auslaugung die Schwindreduktion langfristig beeintr{\"a}chtigt, sind weitere Fragen, denen im Rahmen dieser Arbeit nachgegangen wird. Stand der Wissenschaft 6. Schwinden und Quellen von zement{\"a}ren Baustoffen wird im Allgemeinen mittels makroskopisch-thermodynamischer Ans{\"a}tze beschrieben. Der stark vereinfachte Ansatz kapillaren Unterdrucks bzw. hydrostatischen Drucks als treibende Kraft f{\"u}r hygrische Verformungen wird weitgehend abgelehnt. Vielmehr wird im Bereich moderater Luftfeuchten der Spaltdruck und im Bereich niedriger Luftfeuchten die Oberfl{\"a}chenenergie zur Beschreibung der hygrischen Volumenstabilit{\"a}t herangezogen. 7. Schwindreduzierende Betonzusatzmittel bestehen {\"u}berwiegend aus synergistischen Abmischungen nicht-ionischer Tenside mit Glykolen. Die amphiphilen Eigenschaften der nicht-ionischen Tenside f{\"u}hren zu einer Senkung der Oberfl{\"a}chenspannung des Zementporenwassers. In Abh{\"a}ngigkeit ihrer Konzentration in w{\"a}ssrigen Elektrolyten bilden nicht-ionische Tenside Mizellen und/oder Fl{\"u}ssigkristalle. Beobachtet wurden Mischungsl{\"u}cken und Aussalzungen dieser organischen, oberfl{\"a}chenaktiven Substanzen. Durch die Zugabe von Glykolen wird die Mischbarkeit nicht-ionischer Tenside mit w{\"a}ssrigen Elektrolyten stark erh{\"o}ht und f{\"u}hrt zu einer Absenkung der Bildung von Fl{\"u}ssigkristallen und organischen Aussalzungen sowie zu einer verminderten Adsorption des Tensides an Feststoffoberfl{\"a}chen. Der ausschließlich in der Patentliteratur erw{\"a}hnte Synergieeffekt bei der Abmischung nicht-ionischer Tenside mit Glykolen zu Schwindreduzierern bezieht sich auf eine erh{\"o}hte Schwindreduktionskapazit{\"a}t des Zusatzmittels und beruht auf der Abmilderung aller Effekte, die zu einer Abscheidung des Tensides aus der w{\"a}ssrigen L{\"o}sung f{\"u}hren. 8. Eine Implementierung der spezifischen chemisch-physikalischen Eigenschaften schwind-reduzierender Zusatzmittel in bestehende Modelle zur Beschreibung des Trocknungsschwindens ist der Fachliteratur nicht zu entnehmen. Mit Ausnahme des Kapillardruckmodells zur Vorhersage des Trocknungsschwindens lassen sich Charakteristika schwindreduzierender Betonzusatzmittel, im Speziellen ihrer Oberfl{\"a}chenaktivit{\"a}t, nicht bzw. nur unzureichend in bestehende Modelle zum Trocknungsschwinden implementieren. Methodik 9. Die Oberfl{\"a}chenaktivit{\"a}t einer repr{\"a}sentativen Auswahl an Schwindreduzierern wurde in makroskopischen Versuchen an synthetischen als auch an extrahierten Zementporenw{\"a}ssern quantifiziert. Dies umfasste auch die Quantifizierung von Mischungsl{\"u}cken und organischen Aussalzungen. 10. Ein in dieser Arbeit entwickelter theoretischer Ansatz zur Auswertung herk{\"o}mmlicher Messungen der Oberfl{\"a}chenspannung erlaubt eine Absch{\"a}tzung der Oberfl{\"a}chenspannung der Porenl{\"o}sung im trocknenden, zement{\"a}ren Porensystem. 11. Der Einfluss schwindreduzierender Zusatzmittel auf den Hydratationsmechanismus, d.h. Hydratphasenbestand und Hydratationskinetik, wurde mittels Thermogravimetrie, R{\"o}ntgenphasenanalyse bzw. isothermer W{\"a}rmeleitungskalorimetrie erfasst. Zus{\"a}tzlich wurde Elektronenmikroskopie zur Beschreibung der Mikrostrukturen und energiedispersive R{\"o}ntgenspektroskopie zur qualitativen Bestimmung von niedrig konzentrierten Hydratphasen eingesetzt. Die Ver{\"a}nderungen der Komposition des Zementporenwassers in Gegenwart schwindreduzierender Zusatzmittel wurden analysiert. Die spezifische Adsorption schwindreduzierender Zusatzmittel an Zementhydraten wurde an hydratisierendem Zement als auch an synthetischen Hydratphasen untersucht. 12. Der Mechanismus der Auslaugung schwindreduzierender Zusatzmittel wurde in Standtests untersucht, w{\"a}hrend praxisnahe Konditionen mittels zyklischer Auslaugung und Trocknung in Langzeittests simuliert wurden. 13. Die Beschreibung der hygrischen Eigenschaften von Zementstein und M{\"o}rteln erfolgte anhand von Schwind- und Desorptionsisothermen. Basierend auf thermodynamischen Ans{\"a}tzen wurden unter Verwendung dieser Schwind- und Desorptionsisothermen Energiebilanzen erstellt, die eine Unterscheidung zwischen Verformungsenergie und Energie zur Erzeugung von Oberfl{\"a}che im Trocknungsprozess zement{\"a}rer Baustoffe zulassen und somit eine Abgrenzung der Einflussnahme von Schwindreduzierern auf diese spezifische Energieverteilung erm{\"o}glichen. Im Wesentlichen erzielte Ergebnisse 14. Schwindreduzierende Betonzusatzmittel nehmen aufgrund ihrer amphiphilen Eigenschaften Einfluss auf den Hydratationsmechanismus von Portlandzementen. In Gegenwart dieser Zusatzmittel ist die L{\"o}slichkeit f{\"u}r anorganische Salze verringert. Die Konzentration von Calcium-, Kalium- und Sulfationen sinkt mit zunehmender Konzentration des Zusatzmittels. W{\"a}hrend der Induktionsperiode der Portlandzementhydratation f{\"u}hrt dies zur tempor{\"a}ren Ausf{\"a}llung von Calcium-Kalium-Sulfathydrat. Eine Ver{\"a}nderung des Hydratphasenbestandes in Gegenwart von schwindreduzierenden Zusatzmitteln kann nicht signifikant unterschieden werden. Somit sind nachteilige Auswirkungen auf die Dauerhaftigkeit derartig modifizierter Betone aufgrund eines ver{\"a}nderten Hydratphasenbestandes nicht zu erwarten. 15. Die stark verz{\"o}gernde Wirkung von Schwindreduzierern in Kombination mit polycarboxylat-basierten Fließmitteln beruht nicht auf der Adsorption des Schwindreduzierers am hydratisierenden Klinker. Vielmehr kann davon ausgegangen werden, dass die verminderte L{\"o}slichkeit f{\"u}r Salze in der Porenl{\"o}sung den Reaktionsumsatz absenkt und/oder eine spezifische Adsorption des nicht-ionischen Tensides an Portlanditkeimen deren Wachstum hemmt und damit die Aufl{\"o}sung von silikatischen Klinkerphasen. 16. Schwindreduzierende Zusatzmittel weisen eine spezifische Adsorption an Portlandit auf, einem Nebenprodukt der Hydratationsreaktionen eines Hauptbestandteils von Portlandzement. Ein verst{\"a}rktes Kristallwachstum von Portlandit in lateraler Dimension f{\"u}hrt zu einer Zunahme der spezifischen Oberfl{\"a}che des hydratisierten Zementsteines. F{\"u}r nass nachbehandelte Zementsteine bedeutet dies eine Zunahme der Gelporosit{\"a}t auf Kosten der Kapillarporosit{\"a}t. Eine Einflussnahme auf die Gesamtporosit{\"a}t l{\"a}sst sich nicht feststellen. 17. Die Zunahme der spezifischen Oberfl{\"a}che von Zementstein in Gegenwart von Schwindreduzierern bewirkt eine verst{\"a}rkte physikalische Adsorption von Zementporenwasser am Feststoff. F{\"u}r Betone mit niedrigem w/z-Wert oder unzureichender Nachbehandlung kann dieser Prozess zu einer Reduktion des f{\"u}r die Hydratation verf{\"u}gbaren Wassers f{\"u}hren und in einem vermindertem Hydratationsgrad resultieren. Dies k{\"o}nnte eine Ursache f{\"u}r die in der Literatur beschriebenen Einbußen bez{\"u}glich mechanischer Eigenschaften beim Einsatz von Schwindreduzieren sein. 18. Schwindreduzierer sind im hohen Maße auslaugbar. Jedoch zeigen zyklische Langzeittests, dass ein signifikanter Austrag des Zusatzmittels in vorwiegend trockener Exposition nicht zu erwarten ist. Die Nachhaltigkeit des Einsatzes dieser Zusatzmittel ist gegeben, wenn die Anwendung im Beton das Ziel der Reduktion des Trocknungsschwindens verfolgt. 19. Die schwindreduzierende Wirkung der nicht-ionischen Tenside beruht vorwiegend auf der Reduktion der Oberfl{\"a}chenspannung der Grenzfl{\"a}che „fl{\"u}ssig/gasf{\"o}rmig" des trocknenden Zementsteines. Inwieweit diese Oberfl{\"a}chenspannung durch das nicht-ionischeTensid herabgesetzt wird, ist von der Gesamtkonzentration im Allgemeinen und im Speziellen von der Konzentration des Tensides in der Oberfl{\"a}che abh{\"a}ngig. Da im Zuge des Trocknens diese Grenzfl{\"a}che w{\"a}chst, kann bei gegebener Gesamtkonzentration des Zusatzmittels im Beton dessen Konzentration in der Grenzfl{\"a}che sinken, woraufhin die Oberfl{\"a}chenspannung ansteigt und die Schwindreduktion sinkt. 20. Im Ergebnis dieser Arbeit ist es m{\"o}glich, die Entwicklung sowohl der Oberfl{\"a}che als auch ihrer Oberfl{\"a}chenspannung im Trocknungsprozess zu quantifizieren und diese Ergebnisse in einen einfachen konzeptionellen, thermodynamischen Ansatz zur Minimierung der freien Energie des trocknenden, zement{\"a}ren Porensystems zu {\"u}berf{\"u}hren. Die Verwendung dieses konzeptionellen Ansatzes erlaubt es, den Wirkmechanismus schwindreduzierender Betonzusatzmittel zu beschreiben.},
  subject      = {Schwinden},
  language  = {en}
}
@phdthesis{Ehrhardt,
  author    = {Ehrhardt, Dirk},
  title     = {ZUM EINFLUSS DER NACHBEHANDLUNG AUF DIE GEF{\"U}GEAUSBILDUNG UND DEN FROST-TAUMITTELWIDERSTAND DER BETONRANDZONE},
  doi       = {10.25643/bauhaus-universitaet.3688},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20171120-36889},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {235},
  abstract  = {Die Festigkeitsentwicklung des Zementbetons basiert auf der chemischen Reaktion des Zementes mit dem Anmachwasser. Durch Nachbehandlungsmaßnahmen muss daf{\"u}r gesorgt werden, dass dem Zement gen{\"u}gend Wasser f{\"u}r seine Reaktion zur Verf{\"u}gung steht, da sonst ein Beton mit minderer Qualit{\"a}t entsteht. Die vorliegende Arbeit behandelt die grunds{\"a}tzlichen Fragen der Betonnachbehandlung bei Anwendung von Straßenbetonen. Im Speziellen wird die Frage des erforderlichen Nachbehandlungsbedarfs von h{\"u}ttensandhaltigen Kompositzementen betrachtet. Die Wirkung der Nachbehandlung wird anhand des erreichten Frost-Tausalz-Widerstandes und der Gef{\"u}geausbildung in der unmittelbaren Betonrandzone bewertet. Der Fokus der Untersuchungen lag auf abgezogenen Betonoberfl{\"a}chen. Es wurde ein Modell zur Austrocknung des jungen Betons erarbeitet. Es konnte gezeigt werden, dass in einer fr{\"u}hen Austrocknung (Kapillarphase) keine kritische Austrocknung der Betonrandzone einsetzt, sondern der Beton ann{\"a}hrend gleichm{\"a}ßig {\"u}ber die H{\"o}he austrocknet. Es wurde ein Nomogramm entwickelt, mit dem die Dauer der Kapillarphase in Abh{\"a}ngigkeit der Witterung f{\"u}r Straßenbetone abgesch{\"a}tzt werden kann. Eine kritische Austrocknung der wichtigen Randzone setzt nach Ende der Kapillarphase ein. F{\"u}r Betone unter Verwendung von Zementen mit langsamer Festigkeitsentwicklung ist die Austrocknung der Randzone nach Ende der Kapillarphase besonders ausgepr{\"a}gt. Im Ergebnis zeigen diese Betone dann einen geringen Frost-Tausalz-Widerstand. Mit Zementen, die eine 2d-Zementdruckfestigkeit ≥ 23,0 N/mm² aufweisen, wurde unabh{\"a}ngig von der Zementart (CEM I oder CEM II/B-S) auch dann ein hoher Frost-Tausalz-Widerstand erreicht, wenn keine oder eine schlechtere Nachbehandlung angewendet wurde. F{\"u}r die Praxis ergibt sich damit eine einfache M{\"o}glichkeit der Vorauswahl von geeigneten Zementen f{\"u}r den Verkehrsfl{\"a}chenbau. Betone, die unter Verwendung von Zementen mit langsamere Festigkeitsentwicklung hergestellt werden, erreichen einen hohen Frost-Tausalz-Widerstand nur mit einer geeigneten Nachbehandlung. Die Anwendung von fl{\"u}ssigen Nachbehandlungsmitteln (NBM gem{\"a}ß TL NBM-StB) erreicht eine {\"a}hnliche Wirksamkeit wie eine 5 t{\"a}gige Feuchtnachbehandlung. Voraussetzung f{\"u}r die Wirksamkeit der NBM ist, dass sie auf eine Betonoberfl{\"a}che ohne sichtbaren Feuchtigkeitsfilm (feuchter Glanz) aufgespr{\"u}ht werden. Besonders wichtig ist die Beachtung des richtigen Auftragszeitpunktes bei k{\"u}hler Witterung, da hier aufgrund der verlangsamten Zementreaktion der Beton l{\"a}nger Anmachwasser abst{\"o}ßt. Ein zu fr{\"u}her Auftrag des Nachbehandlungsmittels f{\"u}hrt zu einer Verschlechterung der Qualit{\"a}t der Betonrandzone. Durch Bereitstellung hydratationsabh{\"a}ngiger Transportkenngr{\"o}ßen (Feuchtetransport im Beton) konnten numerische Berechnungen zum Zusammenspiel zwischen der Austrocknung, der Nachbehandlung und der Gef{\"u}geentwicklung durchgef{\"u}hrt werden. Mit dem erstellten Berechnungsmodell wurden Parameterstudien durchgef{\"u}hrt. Die Berechnungen best{\"a}tigen die wesentlichen Erkenntnisse der Laboruntersuchungen. Dar{\"u}ber hinaus l{\"a}sst sich mit dem Berechnungsmodell zeigen, dass gerade bei langsam reagierenden Zementen und k{\"u}hler Witterung ohne eine Nachbehandlung eine sehr d{\"u}nne Randzone (ca. 500 µm - 1000 µm) mit stark erh{\"o}hter Kapillarporosit{\"a}t entsteht.},
  subject      = {Beton},
  language  = {de}
}
@phdthesis{Flohr,
  author    = {Flohr, Alexander},
  title     = {Der Einfluss von Polymermodifikationen, unterschiedlichen Gesteinsk{\"o}rnungen und Gesteinsk{\"o}rnungssubstitutionsmaterial auf das Verformungs- und Bruchverhalten von Beton},
  doi       = {10.25643/bauhaus-universitaet.2003},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20130806-20035},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {148},
  abstract  = {In dieser Arbeit werden die Ergebnisse von experimentellen Untersuchungen an unbewehrten und bewehrten modifizierten Betonen unter monoton steigender Belastung bis zum Bruch, einfacher Kurzzeitbelastung im Grenzbereich der Tragf{\"a}higkeit und mehrfach wiederholter Belastung mit kontinuierlicher Be- und Entlastungsgeschwindigkeit vorgestellt und ausgewertet. F{\"u}r die Modifizierung der Betone wurden zwei grunds{\"a}tzliche Vorgehens¬weisen angewendet: die Variation der Gesteinsk{\"o}rnung und die Modifizierung der Bindemittelphase mit thermoplastischen Polymeren. Die Auswirkungen der Modifikationen auf die Festigkeitseigenschaften und das Form{\"a}nderungsverhalten des Betons bei Kurzzeitbelastung waren dabei von besonderem Interesse. Die beobachteten Ver{\"a}nderungen der Festbetoneigenschaften sowie der nichtlineare Zu-sammenhang zwischen den elastischen und nichtelastischen Verformungsanteilen signali-sieren, dass derartige Modifizierungen das Verformungs- und Bruchverhalten von Beton sig-nifikant beeinflussen und somit beim Nachweis der Tragf{\"a}higkeit und Gebrauchstauglichkeit ber{\"u}cksichtigt werden m{\"u}ssen. Neben der Evaluierung des beanspruchungsabh{\"a}ngigen Form{\"a}nderungsverhaltens werden die etablierten Ans{\"a}tze zur Beschreibung der Gef{\"u}gezu-standsbereiche bei Druckbelastung weiter entwickelt, so dass die {\"U}berg{\"a}nge zwischen den Bereichen exakt ermittelt und die Auspr{\"a}gung der Bereiche quantifiziert werden k{\"o}nnen. Damit ist ein genauerer Vergleich der durch die Modifizierungen hervorgerufenen Ver{\"a}nde-rungen m{\"o}glich.},
  subject      = {Beton},
  language  = {de}
}
@phdthesis{Giebson,
  author    = {Giebson, Colin},
  title     = {Die Alkali-Kiesels{\"a}ure-Reaktion in Beton f{\"u}r Fahrbahndecken und Flugbetriebsfl{\"a}chen unter Einwirkung alkalihaltiger Enteisungsmittel},
  isbn      = {978-3-00-044366-4 (Druckversion)},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20131217-20916},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {208},
  abstract  = {Das Hauptziel der Arbeit war es zu kl{\"a}ren, ob alkalihaltige Enteisungsmittel eine Alkali-Kiesels{\"a}ure-Reaktion (AKR) ausl{\"o}sen und/oder beschleunigen k{\"o}nnen und was die dabei ggf. zugrunde liegenden Mechanismen sind. Die Untersuchungen dazu ergaben, dass die auf Verkehrsfl{\"a}chen eingesetzten alkalihaltigen Enteisungsmittel auf Basis von Natriumchlorid (Fahrbahndecken) bzw. auf Basis der Alkaliacetate und -formiate (Flugbetriebsfl{\"a}chen) den Ablauf einer AKR in Betonen mit alkalireaktiven Gesteinsk{\"o}rnungen ausl{\"o}sen und mitunter stark beschleunigen k{\"o}nnen. Dabei nimmt die AKR-f{\"o}rdernde Wirkung der Enteisungsmittel in der Reihenfolge Natriumchlorid - Alkaliacetate - Alkaliformiate erheblich zu. Es zeigte sich, dass im Fall der Alkaliacetate und -formiate nicht allein die Zufuhr von Alkalien von Bedeutung ist, sondern dass es außerdem zu einer Freisetzung von OH-Ionen aus dem Portlandit und folglich zu einem Anstieg des pH-Wertes in der Porenl{\"o}sung kommt. Dadurch wird der Angriff auf alkalireaktives SiO2 in Gesteinsk{\"o}rnungen verst{\"a}rkt und der Ablauf einer AKR beschleunigt. Unter {\"a}ußerer NaCl-Zufuhr kommt es hingegen nicht zu einem Anstieg des pH-Wertes, was der Grund f{\"u}r die weniger stark AKR-f{\"o}rdernde Wirkung von NaCl ist. Von Bedeutung sind hier die zugef{\"u}hrten Na-Ionen und offenbar ein sich andeutender, direkter Einfluss von NaCl auf das SiO2-L{\"o}severhalten. Sind pH-Wert und Na-Konzentration in der Porenl{\"o}sung ausreichend hoch, wird sich thermodynamisch bedingt AKR-Gel bilden. Die Bildung von FRIEDEL'schem Salz ist dabei nur eine Begleiterscheinung, aber keine Voraussetzung f{\"u}r den Ablauf einer AKR unter {\"a}ußerer NaCl-Zufuhr. Es zeigte sich weiter, dass sich mit der FIB-Klimawechsellagerung als Performance-Pr{\"u}fung das AKR-Sch{\"a}digungspotential von Betonen f{\"u}r Fahrbahndecken und Flugbetriebsfl{\"a}chen zuverl{\"a}ssig beurteilen l{\"a}sst. Die Vorteile der FIB-Klimawechsellagerung liegen in der Pr{\"u}fung kompletter, projektspezifischer Betonzusammensetzungen unter Beachtung aller praxisrelevanten klimatischen Einwirkungen und vor allem in der Ber{\"u}cksichtigung einer {\"a}ußeren Alkalizufuhr. Innerhalb von 36 Wochen kann das AKR-Sch{\"a}digungspotential einer Betonzusammensetzung f{\"u}r eine Nutzungsdauer von 20-30 Jahren in der Praxis sicher beurteilt werden.},
  subject      = {Beton},
  language  = {de}
}
@phdthesis{Le,
  author    = {Le, Ha Thanh},
  title     = {Behaviour of Rice Husk Ash in Self-Compacting High Performance Concrete},
  publisher = {Bauhaus-Universit{\"a}t Weimar, F.A. Finger- Institut f{\"u}r Baustoffkunde, Professur Werkstoffe des Bauens},
  address   = {Weimar},
  isbn      = {978-3-00-048928-0},
  doi       = {10.25643/bauhaus-universitaet.2373},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20150310-23730},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {181},
  abstract  = {The main objective of this thesis is to investigate the characteristics of rice husk ash RHA) and then its behaviour in self-compacting high performance concrete (SCHPC) with respects to rheological properties, hydration and microstructure development and alkali silica reaction, in comparison with silica fume (SF). The main results show that the RHA is a macro-mesoporous amorphous siliceous material with a very high silica content comparable with SF. The pore size distribution is the most important parameter of RHA besides amorphous silica content. This parameter affects pore volume, specific surface area, and thus the water demand and the pozzolanic reactivity of RHA and its behaviour in SCHPC. The incorporation of RHA decreases filling and passing abilities, but significantly increases plastic viscosity and segregation resistance of SCHPC. Therefore, RHA can be used as a viscosity modifying admixture for SCHPC. The incorporation of RHA increases the superplasticizer adsorption, the superplasticizer saturation dosage, yield stress and plastic viscosity of mortar. Fresh mortar formulated from SCHPC is a shear-thickening material. The incorporation of RHA/SF ecreases the shearthickening degree. The incorporation of RHA/SF increases the degree of cement hydration. SF appears more effective at 3 days possibly due to the better nucleation site effect, whereas RHA dominates at the later ages possibly due to the internal water curing effect. The incorporation of RHA/SF increases the degree of C3S hydration, particularly the C3S hydration rate from 3 to 14 days. The pozzolanic reaction takes place outside and inside RHA particles. The internal pozzolanic eaction products consolidate the pores inside RHA particles rather than contribute to the pore refinement in the cement matrix. In the presence of the high alkali concentration, RHA particles act as microreactive aggregates and react with alkali hydroxide to generate the expansive alkali silica reaction products. Increasing the particle size and temperature increases the alkali silica reactivity of RHA. The mechanism for the successive pozzolanic and alkali silica reactions of RHA is theorized. Additionally, a new simple mix design method is proposed for SCHPC containing various supplementary cementitious materials, i.e. RHA, SF, fly ash and limestone powder.},
  subject      = {Werkstoffkunde},
  language  = {en}
}
@phdthesis{Link,
  author    = {Link, Tim},
  title     = {Entwicklung und Untersuchung von alternativen Dicalciumsilicat-Bindern auf der Basis von alpha-C2SH},
  doi       = {10.25643/bauhaus-universitaet.3722},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20180205-37228},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {292},
  abstract  = {Um den Klimawandel zu begrenzen, m{\"u}ssen die CO2-Emissionen drastisch gesenkt werden [100]. Bis 2050 soll bei der Herstellung von Zement eine Einsparung um 51-60 \% auf 0,425-0,350 tCO2/tZement erfolgen [7]. Um dieses Ziel zu erreichen, sind alternative Bindemittelkonzepte notwendig [70]. Diese Arbeit widmet sich alternativen, hochreaktiven Dicalciumsilicat-Bindemitteln, die durch die thermische Aktivierung von α-Dicalcium-Silicat-Hydrat (α-C2SH) erzeugt werden. Das α-C2SH ist eine kristalline C S H-Phase, die im hydrothermalen Prozess, beispielsweise aus Branntkalk und Quarz, herstellbar ist. Die thermische Aktivierung kann bei sehr niedrigen Temperaturen erfolgen (>420 °C) und f{\"u}hrt zu einem Multiphasen-C2S-Binder. Als besonders reaktive Bestandteile k{\"o}nnen x-C2S und r{\"o}ntgenamorphe Anteile enthalten sein. Weiterhin k{\"o}nnen β C2S, γ C2S und Dellait (Ca6(SiO4)(Si2O7)(OH)2) entstehen. Im Rahmen der Arbeit wird zun{\"a}chst der Stand des Wissens zur Polymorphie und Hydratation von C2S zusammengefasst. Es werden bekannte C2S-basierte Bindemittelkonzepte vorgestellt und bewertet. Die Herstellung von C2S-Bindern wird experimentell im Labormaßstab untersucht. Dabei kommen unterschiedliche Autoklaven und ein Muffelofen zum Einsatz. Die Herstellungsparameter werden hinsichtlich Phasenbestand und Reaktivit{\"a}t optimiert. Die Bindemittel werden durch quantitative R{\"o}ntgen-Phasenanalyse (QXRD), Rasterelektronenmikroskopie (REM), N2-Adsorption (BET-Methode), Heliumpycnometer, Thermoanalyse (TGA/DSC) und 29Si-MAS- sowie 29Si-1H-CP/MAS-NMR-Spektroskopie charakterisiert. Das Hydratationsverhalten der Bindemittel wird vorrangig mithilfe von W{\"a}rmeflusskalorimetrie untersucht. Weiterhin werden in situ und ex situ XRD-, TGA/DSC- und REM-Untersuchungen durchgef{\"u}hrt. Anhand von zwei Bindemitteln wird die F{\"a}higkeit zur Erzielung hoher Festigkeiten demonstriert. Abschließend erfolgt eine Absch{\"a}tzung zu Energiebedarf und CO2-Emissionen f{\"u}r die Herstellung der untersuchten C2S-Binder. Die Ergebnisse zeigen, dass f{\"u}r eine hohe Reaktivit{\"a}t der Binder eine niedrige Brenntemperatur und ein geringer Wasserdampfpartialdruck w{\"a}hrend der thermischen Aktivierung entscheidend sind. Weiterhin muss das hydrothermal hergestellte α-C2SH eine m{\"o}glichst hohe spezifische Oberfl{\"a}che aufweisen. Diese Parameter beeinflussen den Phasenbestand und die phasenspezifische Reaktivit{\"a}t. Brenntemperaturen von ca. 420-500 °C f{\"u}hren zu hochreaktiven Bindern, die im Rahmen dieser Arbeit als Niedertemperatur-C2S-Binder bezeichnet werden. Temperaturen von ca. 600-800 °C f{\"u}hren zu Bindern mit geringerer Reaktivit{\"a}t, die im Rahmen dieser Arbeit als Hochtemperatur-C2S bezeichnet werden. H{\"o}here Brenntemperaturen (1000 °C) f{\"u}hren zu Bindemitteln, die innerhalb der ersten drei Tage keine hydraulische Aktivit{\"a}t zeigen. Die untersuchten Bindemittel k{\"o}nnen sehr hohe Reaktionsgeschwindigkeiten erreichen. Die W{\"a}rmeflusskalorimetrie deutet bei einigen Bindemitteln einen nahezu vollst{\"a}ndigen Umsatz innerhalb von drei Tagen an. Durch XRD wurde f{\"u}r einen Binder der vollst{\"a}ndige Verbrauch von x-C2S innerhalb von drei Tagen nachgewiesen. F{\"u}r einen mittels in-situ-XRD und W{\"a}rmeflusskalorimetrie untersuchten Binder wurde gezeigt, dass die Phasen vorrangig in der Reihenfolge r{\"o}ntgenamorph > x-C2S > β-C2S > γ-C2S hydratisieren. Hydratationsprodukte sind nadelige C S H-Phasen und Portlandit. Die Herstellung durch thermische Aktivierung von α-C2SH f{\"u}hrt zu tafeligen Bindemittelpartikeln, die teilweise Zwickelr{\"a}ume und Poren zwischen den einzelnen Partikeln einschließen. Um eine verarbeitbare Bindemittelpaste zu erzeugen, sind daher sehr hohe Wasser/Bindemittel-Werte (z. B. 1,4) erforderlich. Der Wasseranspruch kann durch Mahlung etwa auf das Niveau von Zement gesenkt werden. Die Druckfestigkeitsentwicklung wurde an zwei Niedertemperatur-C2S-Kompositbindern mit 40 \% Kalksteinmehl bzw. 40 \% H{\"u}ttensand untersucht. Aufgrund von theoretischen Betrachtungen zur Porosit{\"a}t in Abh{\"a}ngigkeit des w/b-Wertes wurde dieser auf 0,3 festgelegt. Durch Zugabe von PCE-Fließmittel wurde ein verarbeitbarer M{\"o}rtel erhalten. Die Festigkeitsentwicklung ist sehr schnell. Der Kalksteinmehl-Binder erreichte nach zwei Tagen 46 N/mm². Bis Tag 28 trat keine weitere Festigkeitssteigerung ein. Der H{\"u}ttensand-Binder erreichte nach zwei Tagen 62 N/mm². Durch die H{\"u}ttensandreaktion stieg die Festigkeit bis auf 85 N/mm² nach 28 Tagen an. F{\"u}r den Herstellungsprozess von Niedertemperatur-C2S-Binder wurden Energieverbr{\"a}uche und CO2-Emissionen abgesch{\"a}tzt. Es deutet sich an, dass, bezogen auf die Bindemittelmenge, keine wesentlichen Einsparungen im Vergleich zur Portlandzementherstellung m{\"o}glich sind. F{\"u}r die tats{\"a}chlichen Emissionen muss jedoch zus{\"a}tzlich die Leistungsf{\"a}higkeit der Bindemittel ber{\"u}cksichtigt werden. Die Leistungsf{\"a}higkeit kann als erforderliche Bindemittelmenge betrachtet werden, die je m³ Beton eingesetzt werden muss, um bestimmte Festigkeits-, Dauerhaftigkeits- und Verarbeitungseigenschaften zu erreichen. Aus verschiedenen Ver{\"o}ffentlichungen [94, 201, 206] wurde die These abgeleitet, dass die Leistungsf{\"a}higkeit eines Bindemittels maßgeblich von der C-S-H-Menge bestimmt wird, die w{\"a}hrend der Hydratation gebildet wird. Daher wird f{\"u}r NT-C2S-Binder eine außergew{\"o}hnlich hohe Leistungsf{\"a}higkeit erwartet. Auf Basis der Leistungsf{\"a}higkeitsthese verringern sich die abgesch{\"a}tzten CO2-Emissionen von NT-C2S-Bindern, sodass gegen{\"u}ber Portlandzement ein m{\"o}gliches Einsparpotenzial von 42 \% ermittelt wurde.},
  subject      = {Belit},
  language  = {de}
}
@phdthesis{Mansfeld2008,
  author    = {Mansfeld, Thomas},
  title     = {Das Quellverhalten von Alkalisilikatgelen unter Beachtung ihrer Zusammensetzung},
  doi       = {10.25643/bauhaus-universitaet.1375},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20090106-14572},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  year      = {2008},
  abstract  = {Im Rahmen dieser Arbeit wurden {\"u}ber verschiedene Herstellungsverfahren 48 Gelproben erzeugt und auf ihr Quellverhalten untersucht. Dabei wurde eine Wiederholbarkeit der Messungen mit anderen Bearbeitern {\"u}berpr{\"u}ft und nachgewiesen. Es zeigt sich in den Quellversuchen, dass hohe Alkaligehalte in den Gelproben bei einer niedrigen L{\"o}slichkeit (durch geringe Mengen Calcium in der Probe hervorgerufen) hohe Quelldr{\"u}cke erzeugen. Ein Einfluss des Natrium-Kalium-Verh{\"a}ltnisses (Alkaliverh{\"a}ltnis) auf das Quellverhalten der Gelproben ist nicht zu erkennen. Der Einfluss des Calciums im Gel zeichnet sich deutlich ab, ohne Calcium bauen die Proben keine Quelldr{\"u}cke auf, bei zu hohen Calciumgehalten entstehen nicht quellf{\"a}hige Alkali-Calcium-Silikat-Hydrate. Ein quellf{\"a}higer Bereich kann von ca. 5 \% bis zu ca. 30 \% Calciumanteil im Gel angegeben werden. Neben dem Einfluss des Calciumgehaltes auf das Quellverhalten der Gele ist auch ein Einfluss des Alkali-Silika-Verh{\"a}ltnisses in den Proben nachweisbar. Wird dieses Verh{\"a}ltnis in den Proben stark Richtung Kiesels{\"a}ure verschoben, d. h. niedrige Alkalianteile im Gel, kommt es zu keinen Quellerscheinungen. Somit kann die Wirkung von AKR-vermeidenden Zus{\"a}tzen (FA, Silika usw.) mit diesen Messungen best{\"a}tigt werden. Es kann gezeigt werden, dass die ermittelten Quelldr{\"u}cke eines Alkalikiesel-Gels ein Gesteinskorn oder/und die umgebende Matrix zerst{\"o}ren k{\"o}nnen. Aus diesen oben genannten Erkenntnissen wird ein Bereich einer quellf{\"a}higen Zusammensetzung eines Gels in einem Dreistoffdiagramm angegeben und es k{\"o}nnen folgende Schlussfolgerungen gezogen werden: •Ein Quelldruck kann in einem AK-Gel nur bei einer bestimmten Menge an eingebautem Calcium aufgebaut werden. •Diese Quelldr{\"u}cke k{\"o}nnen deutlich Werte {\"u}ber 10 N/mm² erreichen. •Die im Beton verwendeten Gesteinsk{\"o}rnungen und auch die sie umschließende M{\"o}rtelmatrix k{\"o}nnen mit Quelldr{\"u}cken in den hier bestimmten Gr{\"o}ßenordnungen zerst{\"o}rt werden. •Die bekannten Modelle zur Alkali-Kiesels{\"a}ure-Reaktion m{\"u}ssen um den Einbau des Calciums in ein entstandenes AK-Gel erweitert werden.},
  subject      = {Alkalil{\"o}sliche Kiesels{\"a}ure},
  language  = {de}
}
@phdthesis{Marschetzky,
  author    = {Marschetzky, Manuela},
  title     = {Einfluss von Alkalisalzen und Fließmitteln auf die Hydratation von Calciumsulfathalbhydrat},
  isbn      = {978-3-00-044319-0},
  doi       = {10.25643/bauhaus-universitaet.2086},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20131211-20861},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {124},
  abstract  = {In der praktischen Anwendung werden den Calciumsulfatbindemitteln Kombinationen verschiedenster Zus{\"a}tze beigegeben. Ein Verst{\"a}ndnis f{\"u}r die Wirkungsweise der verschiedenen Zus{\"a}tze wird folglich mit steigender Komplexit{\"a}t moderner Bindemittelrezepturen zunehmend wichtiger. In der vorliegenden Arbeit werden die Auswirkungen von Alkalisalzen und Fließmitteln auf die verschiedenen Phasen der Hydratation von Calciumsulfathalbhydrat systematisch analysiert und anschließend diskutiert. Im ersten Teil der Arbeit wird gezeigt, dass Alkalisulfate und Alkalichloride die Hydratation von Calciumsulfathalbhydrat in unterschiedlicher Weise beeinflussen. Die Beschleunigungswirkung der gleichionigen Zus{\"a}tzen K2SO4 und Na2SO4 wird sowohl durch eine verbesserte Keimbildung als auch durch einen Anstieg der Kristallwachstumsgeschwindigkeit verursacht. W{\"a}hrend Alkalisulfate die Dihydratkeimbildung beg{\"u}nstigen, wird diese bei Zugabe von KCl und NaCl verz{\"o}gert. Ein Beschleunigungseffekt setzt erst sp{\"a}ter in der Phase des Kristallwachstums ein. Die Wirkung der zugegebenen Ionen l{\"a}sst sich entsprechend der Hofmeister-Serie einordnen. Der zweite Teil der vorliegenden Arbeit pr{\"a}sentiert eine systematische Betrachtung der Wirkungsweise dreier Fließmittelgruppen im Calciumsulfatsystem (Polykondensat, Polycarboxylatether, Kammpolymer mit Phosphatgruppen). Untersuchungen zur Verfl{\"u}ssigungswirkung der Fließmittel zeigen, dass diese in der Reihenfolge Polykondensat < Polycarboxylatether < Kammpolymer mit Phosphatgruppen zunimmt. Eine direkte Korrelation zwischen Verfl{\"u}ssigungswirkung und Adsorptionsneigung besteht nicht. Neben den gew{\"u}nschten Effekten weisen Fließmittel h{\"a}ufig auch eine Verz{\"o}gerung der Hydratation des Bindemittels als unerw{\"u}nschte Nebenwirkung auf. Urs{\"a}chlich f{\"u}r diese fließmittelinduzierte Verz{\"o}gerung ist eine Behinderung der Keimbildung und des Kristallwachstums. Untersuchungen zur Aufl{\"o}sung von Calciumsulfathalbhydrat zeigen eine Behinderung des Aufl{\"o}sungsprozesses in Anwesenheit der Fließmittel. Die Ergebnisse lassen eine partielle Belegung der Halbhydratoberfl{\"a}chen mit Fließmittelmolek{\"u}len vermuten. Die ver{\"a}nderte Morphologie der Dihydratkristalle verweist auf eine selektive Belegung der Dihydratoberfl{\"a}chen mit Fließmittelmolek{\"u}len.},
  subject      = {Calciumsulfat},
  language  = {de}
}
@phdthesis{Mueller,
  author    = {M{\"u}ller, Matthias},
  title     = {Frost-Tausalz-Angriff auf Beton - Neue Erkenntnisse zum Schadensmechanismus},
  doi       = {10.25643/bauhaus-universitaet.4502},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20210922-45025},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {226},
  abstract  = {F{\"u}r die Verminderung der betonspezifischen CO2-Emissionen wird ein verst{\"a}rkter Einsatz klinkerreduzierter Zemente bzw. Betone angestrebt. Die Reduzierung des Klinkergehaltes darf jedoch nicht zu einer lebensdauerrelevanten Beeintr{\"a}chtigung der Betondauerhaftigkeit f{\"u}hren. In diesem Zusammenhang stellt der Frost-Tausalz-Widerstand eine kritische Gr{\"o}ße dar, da er bei h{\"o}heren Klinkersubstitutionsraten h{\"a}ufig negativ beeinflusst wird. Erschwerend kommt hinzu, dass f{\"u}r klinkerreduzierte Betone nur ein unzureichender Erfahrungsschatz vorliegt. Ein hoher Frost-Tausalz-Widerstand kann daher nicht ausschließlich anhand deskriptiver Vorgaben gew{\"a}hrleistet werden. Demgem{\"a}ß sollte perspektivisch auch f{\"u}r frost-tausalzbeanspruchte Bauteile eine performancebasierte Lebensdauerbetrachtung erfolgen. Eine unverzichtbare Grundlage f{\"u}r das Erreichen dieser Ziele ist ein Verst{\"a}ndnis f{\"u}r die Schadensvorg{\"a}nge beim Frost-Tausalz-Angriff. Der Forschungsstand ist jedoch gepr{\"a}gt von widerspr{\"u}chlichen Schadenstheorien. Somit wurde als Zielstellung f{\"u}r diese Arbeit abgeleitet, die existierenden Schadenstheorien unter Ber{\"u}cksichtigung des aktuellen Wissensstandes zu bewerten und mit eigenen Untersuchungen zu pr{\"u}fen und einzuordnen. Die Sichtung des Forschungsstandes zeigte, dass nur zwei Theorien das Potential haben, den Frost-Tausalz-Angriff umfassend abzubilden - die Glue Spall Theorie und die Cryogenic Suction Theorie. Die Glue Spall Theorie f{\"u}hrt die Entstehung von Abwitterungen auf die mechanische Sch{\"a}digung der Betonoberfl{\"a}che durch eine anhaftende Eisschicht zur{\"u}ck. Dabei sollen nur bei moderaten Tausalzkonzentrationen in der einwirkenden L{\"o}sung kritische Spannungszust{\"a}nde in der Eisschicht auftreten, die eine Sch{\"a}digung der Betonoberfl{\"a}che hervorrufen k{\"o}nnen. In dieser Arbeit konnte jedoch nachgewiesen werden, dass starke Abwitterungen auch bei Tausalz¬konzentrationen auftreten, bei denen eine mechanische Sch{\"a}digung des Betons durch das Eis auszuschließen ist. Damit wurde die fehlende Eignung der Glue Spall Theorie aufgezeigt. Die Cryogenic Suction Theorie fußt auf den eutektischen Eigenschaften von Tausalz-l{\"o}sungen, die im gefrorenen Zustand immer als Mischung auf festem Wassereis und fl{\"u}ssiger, hochkonzentrierter Salzl{\"o}sung bestehen, solange ihre Eutektikumstemperatur nicht unter¬schritten wird. Die fl{\"u}ssige Phase im salzhaltigen Eis stellt f{\"u}r gefrorenen Beton ein bisher nicht ber{\"u}cksichtigtes Fl{\"u}ssigkeitsreservoir dar, welches trotz der hohen Salzkonzentration die Eisbildung in der Betonrandzone verst{\"a}rken und so die Entstehung von Abwitterungen verursachen soll. In dieser Arbeit wurde best{\"a}tigt, dass die Eisbildung im Zementstein beim Gefrieren in hochkonzentrierter Tausalzl{\"o}sung tats{\"a}chlich verst{\"a}rkt wird. Das Ausmaß der zus{\"a}tzlichen Eisbildung wurde dabei auch von der F{\"a}higkeit des Zementsteins zur Bindung von Chloridionen aus der Tausalzl{\"o}sung beeinflusst. Zusammenfassend wurde festgestellt, dass die Cryogenic Suction Theorie eine gute Beschreibung des Frost-Tausalz-Angriffes darstellt, aber um weitere Aspekte erg{\"a}nzt werden muss. Die Ber{\"u}cksichtigung der intensiven S{\"a}ttigung von Beton durch den Prozess der Mikroeislinsenpumpe stellt hier die wichtigste Erweiterung dar. Basierend auf dieser {\"U}berlegung wurde eine kombinierte Schadenstheorie aufgestellt. Wichtige Annahmen dieser Theorie konnten experimentell best{\"a}tigt werden. Im Ergebnis wurde so die Grundlage f{\"u}r ein tiefergehendes Verst{\"a}ndnis des Frost-Tausalz-Angriffes geschaffen. Zudem wurde ein neuer Ansatz identifiziert, um die (potentielle) Verringerung des Frost-Tausalz-Widerstandes klinkerreduzierter Betone zu erkl{\"a}ren.},
  subject      = {Beton},
  language  = {de}
}
@phdthesis{Nowak,
  author    = {Nowak, Saskia},
  title     = {Alterung von Calciumsulfatphasen : Physiko-chemisch bedingte Feuchteaufnahmen und Einfluss auf die Reaktivit{\"a}t},
  isbn      = {978-3-00-041328-5},
  doi       = {10.25643/bauhaus-universitaet.1873},
  url       = {http://nbn-resolving.de/urn:nbn:de:gbv:wim2-20130320-18731},
  school      = {Bauhaus-Universit{\"a}t Weimar},
  pages     = {155},
  abstract  = {Die Arbeit zeigt die wesentlichen Gr{\"u}nde auf, warum betahalbhydratreiche Niederbranntgipsbinder (industriell als Stuckgips bezeichnet) oft sehr unterschiedliche Eigenschaften aufweisen. Der Anteil an Halbhydrat, welches aus dem stark hygroskopischen Anhydrit III (A III) durch die Reaktion mit Luftfeuchtigkeit entsteht, stellt einen erheblichen, bislang vollkommen unbeachteten Einfluss dar. Dieses Halbhydrat aus A III zeigt andere Oberfl{\"a}cheneigenschaften und ein Reaktionsverhalten, das von frisch gebranntem Betahalbhydrat abweicht. Es zeigt sich, wie weitreichend der Einfluss physiko-chemischer Oberfl{\"a}chenprozesse wie Adsorption und Kondensation ist. Hierdurch wird nicht nur die Oberfl{\"a}chenenergie der Partikel abgebaut, sondern auch eine Verminderung der Hydratationsw{\"a}rme verursacht. Somit wirken sich physikalische Vorg{\"a}nge thermodynamisch aus. Einwirkende und resultierende Parameter einer Alterung wirken wie folgt {\"a}ußerst komplex zusammen: Die dominierenden Bindemitteleigenschaften Abbindeverhalten und Wasseranspruch ver{\"a}ndern sich durch eine Alterung sowohl aufgrund der Phasenumwandlungen als auch infolge der Ver{\"a}nderungen der Kristallite. Ebenso einflussreich ist die Ver{\"a}nderung der Oberfl{\"a}chencharakteristik. Die Auswirkung der Alterung auf die Reaktivit{\"a}t geht deutlich {\"u}ber den Abbau von Anhydrit III, die Dezimierung von abbindef{\"a}higem Material und die beschleunigende Wirkung von Alterungsdihydrat hinaus. Das Wachstum der Kristallite von Halbhydrat und die Verringerung der inneren Energie sowie die energetisch g{\"u}nstige spontane Beladung der Kristallgitterkan{\"a}le kleinster Anhydrit III-Kristallite mit dampff{\"o}rmigem Wasser m{\"u}ssen als maßgebliche Ursachen f{\"u}r die Abnahme der Reaktivit{\"a}t infolge der Alterung herausgestellt werden. Die Abnahme der spezifischen Oberfl{\"a}che und der Oberfl{\"a}chenenergie wirken sich außerdem auf den L{\"o}sungs- und den Hydratationsprozess aus. Der auf der Oberfl{\"a}che von Anhydrit III kristallisierte Anhydrit II wirkt sich auch nach der Umwandlung von A III in Halbhydrat l{\"o}sungshemmend aus. Infolge der alterungsbedingten Dihydratbildung, die bei anhaltender Feuchteeinwirkung einsetzt, wird diese Wirkung aufgehoben bzw. vermindert. Obgleich Dihydrat f{\"u}r seinen Beschleunigungseffekt bekannt ist, entfaltet Alterungsdihydrat infolge seiner besonderen Ausbildung innerhalb der wenige Molek{\"u}llagen umfassenden Kondenswasserschicht nur eine geringe keimbildende Wirkung. Eine wesentliche Erkenntnis betrifft den Bindungscharakter des {\"U}berst{\"o}chiometrischen Wassers. Diesbez{\"u}glich ist eine rein physikalische Bindung nachweisbar. Das in der Arbeit als st{\"a}rker adsorptiv gebunden bezeichnete Wasser kommt neben der Freien Feuchte ausschließlich bei Anwesenheit von Halbhydrat vor. Dieser Zusammenhang wird erstmalig hergestellt und mit Hilfe der kristallchemisch bedingten h{\"o}heren Oberfl{\"a}chenenergie von Halbhydrat erkl{\"a}rt.},
  subject      = {Alterung},
  language  = {de}
}